CONCRETE EXFOLIATION MATERIAL AND CONCRETE EXFOLIATION METHOD
To provide a concrete exfoliation preventing material which has excellent followability to displacement caused by a crack or the like on a concrete structure and can prevent exfoliation of concrete pieces, and a concrete exfoliation preventing method which can be easily executed.SOLUTION: A concrete exfoliation prevention material comprises an intermediate layer and a surface layer provided on a concrete structure, wherein the intermediate layer has an average adhesive strength of 1-5 N/mm in a 180 degree exfoliation test (K6854-2 specified in JIS) at a temperature of 23°C and relative humidity of 50%, and the surface layer has an elongation of 100-700% at a temperature of 23°C and a humidity of 50%; in a punching test at a relative temperature of 23°C and a relative humidity of 50%, the concrete exfoliation prevention material has a punching load per 10 cm of 0.3 kN or more, an elongation performance of 10 mm or more, and a crack-following property of 2 mm or more at a temperature of 23°C and relative humidity of 50%.SELECTED DRAWING: None
【課題】コンクリート構造物上に生じる亀裂などによる変位に対して追従性が良好で、コンクリート片の剥落を防止できるコンクリート剥落防止材及び、施工が容易なコンクリート剥落防止方法を提供する。【解決手段】コンクリート構造物上に設けられる中間層と表面層とを備えたコンクリート剥落防止材であって、中間層は、温度２３℃、相対湿度５０％における１８０゜剥離試験（JIS規格に規定されるK6854-2）での平均接着強度が１〜５Ｎ／ｍｍであり、表面層は、温度２３℃、湿度５０％における伸び率が１００〜７００％であり、コンクリート剥落防止材は、相対温度２３℃、湿度５０％における押し抜き試験において、直径１０ｃｍ当たりの押し抜き荷重が０．３ｋＮ以上であり、伸び性能が１０ｍｍ以上であり、かつ、ひび割れ追従性が温度２３℃、相対湿度５０％で２ｍｍ以上となるコンクリート剥落防止材。【選択図】なし
CONCRETE EXFOLIATION MATERIAL AND CONCRETE EXFOLIATION METHOD
To provide a concrete exfoliation preventing material which has excellent followability to displacement caused by a crack or the like on a concrete structure and can prevent exfoliation of concrete pieces, and a concrete exfoliation preventing method which can be easily executed.SOLUTION: A concrete exfoliation prevention material comprises an intermediate layer and a surface layer provided on a concrete structure, wherein the intermediate layer has an average adhesive strength of 1-5 N/mm in a 180 degree exfoliation test (K6854-2 specified in JIS) at a temperature of 23°C and relative humidity of 50%, and the surface layer has an elongation of 100-700% at a temperature of 23°C and a humidity of 50%; in a punching test at a relative temperature of 23°C and a relative humidity of 50%, the concrete exfoliation prevention material has a punching load per 10 cm of 0.3 kN or more, an elongation performance of 10 mm or more, and a crack-following property of 2 mm or more at a temperature of 23°C and relative humidity of 50%.SELECTED DRAWING: None
【課題】コンクリート構造物上に生じる亀裂などによる変位に対して追従性が良好で、コンクリート片の剥落を防止できるコンクリート剥落防止材及び、施工が容易なコンクリート剥落防止方法を提供する。【解決手段】コンクリート構造物上に設けられる中間層と表面層とを備えたコンクリート剥落防止材であって、中間層は、温度２３℃、相対湿度５０％における１８０゜剥離試験（JIS規格に規定されるK6854-2）での平均接着強度が１〜５Ｎ／ｍｍであり、表面層は、温度２３℃、湿度５０％における伸び率が１００〜７００％であり、コンクリート剥落防止材は、相対温度２３℃、湿度５０％における押し抜き試験において、直径１０ｃｍ当たりの押し抜き荷重が０．３ｋＮ以上であり、伸び性能が１０ｍｍ以上であり、かつ、ひび割れ追従性が温度２３℃、相対湿度５０％で２ｍｍ以上となるコンクリート剥落防止材。【選択図】なし
CONCRETE EXFOLIATION MATERIAL AND CONCRETE EXFOLIATION METHOD
コンクリート剥落防止材及びコンクリート剥落防止方法
ISOBE RYUTARO (Autor:in) / HANZAWA KOSUKE (Autor:in) / FURUTA YUKA (Autor:in) / MIYATA YUTAKA (Autor:in) / NAKAYAMA HIDENORI (Autor:in) / NEGISHI MASAMI (Autor:in) / SHITAMAE YOSHINOBU (Autor:in) / OKITA YASUNOBU (Autor:in)
09.09.2021
Patent
Elektronische Ressource
Japanisch
EXFOLIATION PREVENTION MATERIAL AND EXFOLIATION PREVENTION STRUCTURE OF CONCRETE STRUCTURE