ZIRCONIUM CARBIDE/ZIRCONIUM BORIDE/CARBON COMPOSITE AND METHOD FOR PRODUCING THE SAME
To provide a zirconium carbide/zirconium boride/carbon (ZrC/ZrB2/C) composite having large flexural hardness σb at high temperature, and to provide a method for producing the same.SOLUTION: A composite has: a volume ratio of ZrC/ZrB2/C of 25 to 65/58 to 27/17 to 8 vol.%; and flexural hardness σb in a range of 1,400 to 1,600°C of 400 MPa or more. The ZrC/ZrB2/C composite can be produced by: mixing ZrC powder with amorphous B powder, so that a theoretical volume ratio of ZrC/ZrB2 is 30/70 to 70/30 vol.%, to thereby obtain mixed powder; using the mixed powder to perform molding; and sintering the molded body having a desired shape after obtaining the molded body, wherein the sintering is preferably performed by pulse-energized pressure sintering.SELECTED DRAWING: None
【課題】高温において大きな曲げ強度σｂを有する炭化ジルコニウム／ホウ化ジルコニウム／炭素（ＺｒＣ／ＺｒＢ２／Ｃ）コンポジット及び、その製造方法の提供。【解決手段】このコンポジットにおけるＺｒＣ／ＺｒＢ２／Ｃの体積比率は２５〜６５／５８〜２７／１７〜８ｖｏｌ％であり、１４００〜１６００℃の範囲の曲げ強度σｂが４００ＭＰａ以上である。本発明のＺｒＣ／ＺｒＢ２／Ｃコンポジットは、ＺｒＣ粉体と非晶質Ｂ粉体を、ＺｒＣ／ＺｒＢ２の理論上の体積比率が３０／７０〜７０／３０ｖｏｌ％となるように混合を行って混合粉を得、この混合粉を用いて成形を行い、所望の形状を有した成形体を得た後に焼結を行うことによって製造でき、パルス通電加圧焼結にて焼結を行うことが好ましい。【選択図】なし
ZIRCONIUM CARBIDE/ZIRCONIUM BORIDE/CARBON COMPOSITE AND METHOD FOR PRODUCING THE SAME
To provide a zirconium carbide/zirconium boride/carbon (ZrC/ZrB2/C) composite having large flexural hardness σb at high temperature, and to provide a method for producing the same.SOLUTION: A composite has: a volume ratio of ZrC/ZrB2/C of 25 to 65/58 to 27/17 to 8 vol.%; and flexural hardness σb in a range of 1,400 to 1,600°C of 400 MPa or more. The ZrC/ZrB2/C composite can be produced by: mixing ZrC powder with amorphous B powder, so that a theoretical volume ratio of ZrC/ZrB2 is 30/70 to 70/30 vol.%, to thereby obtain mixed powder; using the mixed powder to perform molding; and sintering the molded body having a desired shape after obtaining the molded body, wherein the sintering is preferably performed by pulse-energized pressure sintering.SELECTED DRAWING: None
【課題】高温において大きな曲げ強度σｂを有する炭化ジルコニウム／ホウ化ジルコニウム／炭素（ＺｒＣ／ＺｒＢ２／Ｃ）コンポジット及び、その製造方法の提供。【解決手段】このコンポジットにおけるＺｒＣ／ＺｒＢ２／Ｃの体積比率は２５〜６５／５８〜２７／１７〜８ｖｏｌ％であり、１４００〜１６００℃の範囲の曲げ強度σｂが４００ＭＰａ以上である。本発明のＺｒＣ／ＺｒＢ２／Ｃコンポジットは、ＺｒＣ粉体と非晶質Ｂ粉体を、ＺｒＣ／ＺｒＢ２の理論上の体積比率が３０／７０〜７０／３０ｖｏｌ％となるように混合を行って混合粉を得、この混合粉を用いて成形を行い、所望の形状を有した成形体を得た後に焼結を行うことによって製造でき、パルス通電加圧焼結にて焼結を行うことが好ましい。【選択図】なし
ZIRCONIUM CARBIDE/ZIRCONIUM BORIDE/CARBON COMPOSITE AND METHOD FOR PRODUCING THE SAME
炭化ジルコニウム／ホウ化ジルコニウム／炭素コンポジット及びその製造方法
HIROTA TAKESHI (Autor:in) / KATO MASAKI (Autor:in) / MATSUMOTO KAI (Autor:in)
25.11.2021
Patent
Elektronische Ressource
Japanisch
ZIRCONIUM BORIDE/BORON CARBIDE COMPOSITE AND METHOD FOR MANUFACTURING SAME
| Europäisches Patentamt | 2020
Preparation method of densified zirconium boride-silicon carbide composite ceramic
| Europäisches Patentamt | 2021
Ternary boride-zirconium boride composite material and preparation method thereof
| Europäisches Patentamt | 2020