METHOD OF PRODUCING PARAMAGNETIC GARNET TYPE TRANSPARENT CERAMIC
To provide a method of producing paramagnetic garnet type transparent ceramic, i.e., a sintered body of a paramagnetic garnet type oxide containing Tb and Y, which ceramic is highly transparent, is of extremely high and stable production reproducibility, and is truly practically usable.SOLUTION: The method of producing paramagnetic garnet type transparent ceramic constituted of a sintered body of a composite oxide of a prescribed composition including Tb, Y, Sc and Al, by wet-blending terbium oxide powder, yttrium oxide powder, scandium oxide powder and aluminum oxide powder as starting materials, and silicon dioxide as a sintering aid to prepare slurry, molding the slurry and sintering the molding, is characterized in that the mean particle diameters of terbium oxide powder and yttrium oxide powder are each 3 μm or more, and the mean particle diameters of scandium oxide powder and aluminum oxide powder are each smaller than 1 μm, the particle size distributions of the terbium oxide powder, yttrium oxide powder, scandium oxide powder and aluminum oxide powder in the slurry each have a single peak, the median diameter (D50 value) in each of the particle diameter distributions is 400 nm or more, and the value of cumulative volume-based 95% mean particle diameter from the smallest value side in the particle size distribution (D95 value), is 2 μm or less.SELECTED DRAWING: Figure 2
【課題】Ｔｂ及びＹを含有する常磁性ガーネット型酸化物の焼結体であって、透明性が極めて高く、その製造再現性が極めて高く安定している、真に実用的な常磁性ガーネット型透明セラミックスの製造方法を提供する。【解決手段】Ｔｂ、Ｙ、Ｓｃ及びＡｌを含有する所定組成の複合酸化物の焼結体からなる常磁性ガーネット型透明セラミックスの製造方法において、出発原料の酸化テルビウム粉末、酸化イットリウム粉末それぞれの平均粒子径が３μｍ以上であり、上記出発原料の酸化スカンジウム粉末、酸化アルミニウム粉末それぞれの平均粒子径が１μｍ未満であって、上記スラリーにおける酸化テルビウム粉末、酸化イットリウム粉末、酸化スカンジウム粉末及び酸化アルミニウム粉末の粒度分布が単一ピークを有し、該粒度分布のメジアン径（Ｄ５０値）が４００ｎｍ以上であり、かつ該粒度分布の最小値側からの累積９５体積％の値（Ｄ９５値）が２μｍ以下である。【選択図】図２
METHOD OF PRODUCING PARAMAGNETIC GARNET TYPE TRANSPARENT CERAMIC
To provide a method of producing paramagnetic garnet type transparent ceramic, i.e., a sintered body of a paramagnetic garnet type oxide containing Tb and Y, which ceramic is highly transparent, is of extremely high and stable production reproducibility, and is truly practically usable.SOLUTION: The method of producing paramagnetic garnet type transparent ceramic constituted of a sintered body of a composite oxide of a prescribed composition including Tb, Y, Sc and Al, by wet-blending terbium oxide powder, yttrium oxide powder, scandium oxide powder and aluminum oxide powder as starting materials, and silicon dioxide as a sintering aid to prepare slurry, molding the slurry and sintering the molding, is characterized in that the mean particle diameters of terbium oxide powder and yttrium oxide powder are each 3 μm or more, and the mean particle diameters of scandium oxide powder and aluminum oxide powder are each smaller than 1 μm, the particle size distributions of the terbium oxide powder, yttrium oxide powder, scandium oxide powder and aluminum oxide powder in the slurry each have a single peak, the median diameter (D50 value) in each of the particle diameter distributions is 400 nm or more, and the value of cumulative volume-based 95% mean particle diameter from the smallest value side in the particle size distribution (D95 value), is 2 μm or less.SELECTED DRAWING: Figure 2
【課題】Ｔｂ及びＹを含有する常磁性ガーネット型酸化物の焼結体であって、透明性が極めて高く、その製造再現性が極めて高く安定している、真に実用的な常磁性ガーネット型透明セラミックスの製造方法を提供する。【解決手段】Ｔｂ、Ｙ、Ｓｃ及びＡｌを含有する所定組成の複合酸化物の焼結体からなる常磁性ガーネット型透明セラミックスの製造方法において、出発原料の酸化テルビウム粉末、酸化イットリウム粉末それぞれの平均粒子径が３μｍ以上であり、上記出発原料の酸化スカンジウム粉末、酸化アルミニウム粉末それぞれの平均粒子径が１μｍ未満であって、上記スラリーにおける酸化テルビウム粉末、酸化イットリウム粉末、酸化スカンジウム粉末及び酸化アルミニウム粉末の粒度分布が単一ピークを有し、該粒度分布のメジアン径（Ｄ５０値）が４００ｎｍ以上であり、かつ該粒度分布の最小値側からの累積９５体積％の値（Ｄ９５値）が２μｍ以下である。【選択図】図２
METHOD OF PRODUCING PARAMAGNETIC GARNET TYPE TRANSPARENT CERAMIC
常磁性ガーネット型透明セラミックスの製造方法
IKARI MASANORI (Autor:in) / TANAKA KEITA (Autor:in) / MATSUMOTO TAKUSHI (Autor:in)
08.08.2023
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
METHOD FOR PRODUCING PARAMAGNETIC GARNET-TYPE TRANSPARENT CERAMIC
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2025
| Europäisches Patentamt | 2022