PRODUCTION METHOD OF LIGHT-WEIGHT CELLULAR CONCRETE USED WITH CARBONATION TREATED LIGHT-WEIGHT CELLULAR CONCRETE POWDER
To realize light-weight cellular concrete that can be taken as interior wall materials even if an ALC recycling amount is large while maintaining panel strength of the light-weight cellular concrete used as a wall material, also does not require a special measuring apparatus, facilitates process control, is hardly affected by fluctuation of a recycled raw material amount to compression strength even if recycled raw materials are used with 25 mass% or more in internal percentage solids without requiring a special firing facility, has a small contraction coefficient and can be stably held.SOLUTION: A production method of light-weight cellular concrete is characterized by coarsely grinding light-weight cellular concrete wastes to a diameter of 1.2 mm or less, and adding recycled raw materials for light-weight cellular concrete containing carbonation treated calcium carbonate with 20°C to 80°C from 2 mass% to 25 mass% of the whole mass of light-weight cellular concrete materials in internal percentage solids.SELECTED DRAWING: Figure 1
【課題】本発明は、壁材として使用している軽量気泡コンクリートのパネル強度を維持しながら、ＡＬＣリサイクル量がより多くても、内装壁材とでき、しかも、特別な測定装置が不要で工程管理が簡便であり、特別な焼成設備も必要とせずに、リサイクル原料を内割固形分で２５質量％以上使用しても、リサイクル原料量の圧縮強度への変動を受けにくく、収縮率も小さく安定して保持できる、軽量気泡コンクリートの実現を課題とする。【解決手段】軽量気泡コンクリート屑を１．２ｍｍ直径以下に粗粉砕し、２０℃～８０℃で炭酸化処理をした炭酸カルシウム含有する軽量気泡コンクリート用リサイクル原料を、内割固形分で軽量気泡コンクリート原料全体質量の２質量％から２５質量％添加することを特徴とする軽量気泡コンクリートの製造方法。【選択図】 図１
PRODUCTION METHOD OF LIGHT-WEIGHT CELLULAR CONCRETE USED WITH CARBONATION TREATED LIGHT-WEIGHT CELLULAR CONCRETE POWDER
To realize light-weight cellular concrete that can be taken as interior wall materials even if an ALC recycling amount is large while maintaining panel strength of the light-weight cellular concrete used as a wall material, also does not require a special measuring apparatus, facilitates process control, is hardly affected by fluctuation of a recycled raw material amount to compression strength even if recycled raw materials are used with 25 mass% or more in internal percentage solids without requiring a special firing facility, has a small contraction coefficient and can be stably held.SOLUTION: A production method of light-weight cellular concrete is characterized by coarsely grinding light-weight cellular concrete wastes to a diameter of 1.2 mm or less, and adding recycled raw materials for light-weight cellular concrete containing carbonation treated calcium carbonate with 20°C to 80°C from 2 mass% to 25 mass% of the whole mass of light-weight cellular concrete materials in internal percentage solids.SELECTED DRAWING: Figure 1
【課題】本発明は、壁材として使用している軽量気泡コンクリートのパネル強度を維持しながら、ＡＬＣリサイクル量がより多くても、内装壁材とでき、しかも、特別な測定装置が不要で工程管理が簡便であり、特別な焼成設備も必要とせずに、リサイクル原料を内割固形分で２５質量％以上使用しても、リサイクル原料量の圧縮強度への変動を受けにくく、収縮率も小さく安定して保持できる、軽量気泡コンクリートの実現を課題とする。【解決手段】軽量気泡コンクリート屑を１．２ｍｍ直径以下に粗粉砕し、２０℃～８０℃で炭酸化処理をした炭酸カルシウム含有する軽量気泡コンクリート用リサイクル原料を、内割固形分で軽量気泡コンクリート原料全体質量の２質量％から２５質量％添加することを特徴とする軽量気泡コンクリートの製造方法。【選択図】 図１
PRODUCTION METHOD OF LIGHT-WEIGHT CELLULAR CONCRETE USED WITH CARBONATION TREATED LIGHT-WEIGHT CELLULAR CONCRETE POWDER
炭酸化処理した軽量気泡コンクリート粉末を用いた軽量気泡コンクリートの製造方法
NAKAGAWA KIYOYUKI (Autor:in) / KATO KEISHIN (Autor:in) / YAMAGUCHI TAKAYA (Autor:in)
31.10.2024
Patent
Elektronische Ressource
Japanisch
MANUFACTURING METHOD OF LIGHT-WEIGHT CELLULAR CONCRETE
| Europäisches Patentamt | 2021
Potential Uses of Cellular Light-Weight Concrete
British Library Online Contents | 1996
| Taylor & Francis Verlag | 1985
MANUFACTURING METHOD OF LIGHT WEIGHT CELLULAR CONCRETE PANEL
| Europäisches Patentamt | 2016