PILE GROUTING MATERIALS USING FERRONICKEL SLAG
The present invention relates to a pile grouting material including 100-300 wt part of blast furnace slag fine aggregates, and 100-300 wt part of gypsum containing at least 50 wt% of calcium oxide, and at least 15 wt% of sulfate oxide based on 100 wt part of ferronickel slag fine aggregates. According to the present invention, CaO and SiO_2 ingredients obtained by vitrificating ferronickel slag fine aggregates and granulated blast furnace slag are activated by alkali and sulphate stimulus of the gypsum including at least 50 wt% of calcium oxide, and at least 15 wt% of sulfate oxide at hydrogen ion concentration (pH) of 12 or more, so that strength equal to or greater than that of type I ordinary cement used as the pile grouting material can be obtained. In addition, according to the pile grouting material, end bearing capacity and skin friction of a bored pile can be more improved as compared with those of existing injected cement liquid by preventing injected liquid from leaking by underground water filled in a gap between a bored ground and an original ground and existing between bores and the bored pile through a volume expansion reaction in which at least 30 wt% of MgO ingredients contained in ferronickel slag fine aggregates meet water (H_2O) to change into Mg(OH)_2 to be expanded.
본 발명은 페로니켈 슬래그 미분말 100중량부에 대하여 고로슬래그 미분말 100~300중량부와 칼슘 옥사이드(Calcium oxide) 함량이 50중량% 이상이고 설페이트 옥사이드(Sulfate oxide) 함량이 15중량% 이상인 석고 100~300중량부를 포함하는 것을 특징으로 하는 말뚝 주입재에 관한 것이다. 본 발명에 따르면, 페로니켈 슬래그 미분말과 고로슬래그 미분말의 유리화된 CaO, SiO성분들이 수소이온농도(pH) 12 이상이며 칼슘 옥사이드(Calcium oxide) 함량이 50중량% 이상이고 설페이트 옥사이드(Sulfate oxide) 함량이 15중량% 이상인 석고의 알칼리 및 황산염 자극에 의해 활성화되어 1종 보통시멘트를 말뚝 주입재로 사용하는 것과 동등 이상의 강도를 발현할 수 있다. 또한, 본 발명에 따른 말뚝 주입재는 페로니켈 슬래그 미분말에 30중량% 이상 함유된 MgO 성분이 배합수(HO)와 만나 Mg(OH)로 전이되면서 팽창하는 체적 팽창작용을 이용하여 천공지반과 원지반의 간극을 채워주며 천공구멍과 매입말뚝 사이에 존재할 수 있는 지하수에 의한 주입액의 유실을 방지하여 매입 말뚝의 선단지지력 및 주면마찰력을 기존 시멘트 주입액에 비하여 크게 향상시킬 수 있는 효과가 있다.
PILE GROUTING MATERIALS USING FERRONICKEL SLAG
The present invention relates to a pile grouting material including 100-300 wt part of blast furnace slag fine aggregates, and 100-300 wt part of gypsum containing at least 50 wt% of calcium oxide, and at least 15 wt% of sulfate oxide based on 100 wt part of ferronickel slag fine aggregates. According to the present invention, CaO and SiO_2 ingredients obtained by vitrificating ferronickel slag fine aggregates and granulated blast furnace slag are activated by alkali and sulphate stimulus of the gypsum including at least 50 wt% of calcium oxide, and at least 15 wt% of sulfate oxide at hydrogen ion concentration (pH) of 12 or more, so that strength equal to or greater than that of type I ordinary cement used as the pile grouting material can be obtained. In addition, according to the pile grouting material, end bearing capacity and skin friction of a bored pile can be more improved as compared with those of existing injected cement liquid by preventing injected liquid from leaking by underground water filled in a gap between a bored ground and an original ground and existing between bores and the bored pile through a volume expansion reaction in which at least 30 wt% of MgO ingredients contained in ferronickel slag fine aggregates meet water (H_2O) to change into Mg(OH)_2 to be expanded.
본 발명은 페로니켈 슬래그 미분말 100중량부에 대하여 고로슬래그 미분말 100~300중량부와 칼슘 옥사이드(Calcium oxide) 함량이 50중량% 이상이고 설페이트 옥사이드(Sulfate oxide) 함량이 15중량% 이상인 석고 100~300중량부를 포함하는 것을 특징으로 하는 말뚝 주입재에 관한 것이다. 본 발명에 따르면, 페로니켈 슬래그 미분말과 고로슬래그 미분말의 유리화된 CaO, SiO성분들이 수소이온농도(pH) 12 이상이며 칼슘 옥사이드(Calcium oxide) 함량이 50중량% 이상이고 설페이트 옥사이드(Sulfate oxide) 함량이 15중량% 이상인 석고의 알칼리 및 황산염 자극에 의해 활성화되어 1종 보통시멘트를 말뚝 주입재로 사용하는 것과 동등 이상의 강도를 발현할 수 있다. 또한, 본 발명에 따른 말뚝 주입재는 페로니켈 슬래그 미분말에 30중량% 이상 함유된 MgO 성분이 배합수(HO)와 만나 Mg(OH)로 전이되면서 팽창하는 체적 팽창작용을 이용하여 천공지반과 원지반의 간극을 채워주며 천공구멍과 매입말뚝 사이에 존재할 수 있는 지하수에 의한 주입액의 유실을 방지하여 매입 말뚝의 선단지지력 및 주면마찰력을 기존 시멘트 주입액에 비하여 크게 향상시킬 수 있는 효과가 있다.
PILE GROUTING MATERIALS USING FERRONICKEL SLAG
페로니켈 슬래그를 활용한 말뚝 주입재