Glaze for inkjet printing ceramic tile and manufacturing method of inkjet printing ceramic tile using the glaze
The present invention relates to glaze for an inkjet printing ceramic tile, containing: 0.5-1.5 moles of SiO_2 powder; 0.05-0.1 mole of ZrO_2 powder; 0.1-0.15 mole of Al_2O_3 powder; 0.5-0.9 mole of CaO powder; 0.05-0.2 mole of MgO powder; 0.05-0.2 mole of Na_2O powder; 0.1-0.3 mole of Zn_2SiO_4 powder; and 0-0.2 mole of B_2O_3 powder, wherein mole ratio between the SiO_2 powder and the Al_2O_3 powder is 5-10 and to a method for manufacturing an inkjet printing ceramic tile using the same. According to the present invention, a glaze layer can maintain an amorphous state, a crystal phase is not formed on the surface of the ceramic tile, decoloration does not occur with respect to ink with colors of blue, pink, yellow and black and stable colors can be formed even if a plasticizing process is performed after inkjet printing ink is covered.
본 발명은, SiO분말 0.5∼1.5몰, ZrO분말 0.05∼0.1몰, AlO분말 0.1∼0.15몰, CaO 분말 0.5∼0.9몰, MgO 분말 0.05∼0.2몰, NaO 분말 0.05∼0.2몰, ZnSiO분말 0.1∼0.3몰 및 BO분말 0∼0.2몰을 포함하며, 상기 SiO분말 / 상기 AlO분말의 몰비는 5∼10을 이루는 것을 특징으로 하는 잉크젯프린팅 도자타일용 유약 및 이를 이용한 잉크젯프린팅 도자타일의 제조방법에 관한 것이다. 본 발명에 의하면, 잉크젯프린팅 잉크 도포 후 소성을 진행하여도 유약층은 비정질 상태를 유지하고 도자타일 표면에서 결정상이 형성되지 않으며, 블루, 핑크, 옐로, 블랙 색상의 잉크에 대하여 컬러의 변색이 발생하지 않고 안정적으로 컬러가 발색될 수 있다.
Glaze for inkjet printing ceramic tile and manufacturing method of inkjet printing ceramic tile using the glaze
The present invention relates to glaze for an inkjet printing ceramic tile, containing: 0.5-1.5 moles of SiO_2 powder; 0.05-0.1 mole of ZrO_2 powder; 0.1-0.15 mole of Al_2O_3 powder; 0.5-0.9 mole of CaO powder; 0.05-0.2 mole of MgO powder; 0.05-0.2 mole of Na_2O powder; 0.1-0.3 mole of Zn_2SiO_4 powder; and 0-0.2 mole of B_2O_3 powder, wherein mole ratio between the SiO_2 powder and the Al_2O_3 powder is 5-10 and to a method for manufacturing an inkjet printing ceramic tile using the same. According to the present invention, a glaze layer can maintain an amorphous state, a crystal phase is not formed on the surface of the ceramic tile, decoloration does not occur with respect to ink with colors of blue, pink, yellow and black and stable colors can be formed even if a plasticizing process is performed after inkjet printing ink is covered.
본 발명은, SiO분말 0.5∼1.5몰, ZrO분말 0.05∼0.1몰, AlO분말 0.1∼0.15몰, CaO 분말 0.5∼0.9몰, MgO 분말 0.05∼0.2몰, NaO 분말 0.05∼0.2몰, ZnSiO분말 0.1∼0.3몰 및 BO분말 0∼0.2몰을 포함하며, 상기 SiO분말 / 상기 AlO분말의 몰비는 5∼10을 이루는 것을 특징으로 하는 잉크젯프린팅 도자타일용 유약 및 이를 이용한 잉크젯프린팅 도자타일의 제조방법에 관한 것이다. 본 발명에 의하면, 잉크젯프린팅 잉크 도포 후 소성을 진행하여도 유약층은 비정질 상태를 유지하고 도자타일 표면에서 결정상이 형성되지 않으며, 블루, 핑크, 옐로, 블랙 색상의 잉크에 대하여 컬러의 변색이 발생하지 않고 안정적으로 컬러가 발색될 수 있다.
Glaze for inkjet printing ceramic tile and manufacturing method of inkjet printing ceramic tile using the glaze
잉크젯프린팅 도자타일용 유약 및 이를 이용한 잉크젯프린팅 도자타일의 제조방법
KIM JIN HO (Autor:in) / HWANG KWANG TAEK (Autor:in) / MOON JOON SUB (Autor:in) / JEE YONG WOO (Autor:in)
09.08.2017
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2017
Transmutation glaze suitable for ceramic tile production and transmutation glaze ceramic tile
| Europäisches Patentamt | 2015
Glaze material of jade glaze, ceramic tile and preparation method of ceramic tile
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2024