The present invention relates to a functional mortar composition with excellent fire-resistant and earthquake-resistant performance using ceramic composite fiber and a fire-resistant and earthquake-resistant repair method using the same and, more specifically, to a mortar composition for the fire-resistant and earthquake-resistant reinforcement of a concrete structure and a fire-resistant and earthquake-resistant repair method using the same. The mortar composition includes: 1-10 parts by weight of a polymer, 0.1-8 parts by weight of a silica fume, and 0.5-5.0 parts by weight of ceramic composite fiber; 1-8 parts by weight of a strength enhancer; 30-50 parts by weight of an aggregate; 0.5-2.0 parts by weight of an anti-shrinkage agent; 3-7 parts by weight of polyvinyl alcohol (PVA) powder resin; 0.1-1.0 part by weight of a defoamer; 5-10 parts by weight of an expanding agent; 1-5 parts by weight of a powder type silicone water repellent; 5-15 parts by weight of a seismic performance enhancer; and 1-15 parts by weight of a limestone powder component with respect to 100 parts by weight of cement. According to the present invention, in constructing a concrete structure requiring a seismic reinforcement work has effects of: having excellent physical characteristics including bond strength, compressive strength, and flexural strength and having excellent durability by maintaining an excellent water repellency effect and a low water absorption rate; having excellent seismic reinforcement construction ability for a concrete structure by reducing unit weight of mortar and improving initial and long-term adhesion performance; being environmentally friendly since an organic solvent is not used; reinforcing the seismic performance of a structure by evenly absorbing earthquake vibration and various stresses by finely packing the fine cracks of mortar; and preventing problem occurrences caused by high temperature in a case of fire after maintenance by having excellent fire-resistance and heat-resistance.

본 발명은 세라믹 복합 섬유를 이용한 내화 및 내진 성능이 우수한 기능성 모르타르 조성물 및 이를 이용한 내화 내진 보수 공법에 관한 것으로서, 더욱 상세하게는 시멘트 100 중량부에 대하여 폴리머 1~10 중량부, 실리카 흄 0.1~8 중량부, 세라믹 복합 섬유 0.5~5.0 중량부; 강도증진제 1~8 중량부; 골재 30~50 중량부; 수축방지제 0.5~2.0 중량부; 폴리비닐알콜(PVA) 분말 수지 3~7 중량부; 소포제 0.1~1.0 중량부 ; 팽창제 5~10 중량부; 분말형 실리콘 발수제 1~5 중량부; 내진 성능 강화제 5~15 중량부; 및 석회석 분말 성분 1~15 중량부를 포함하는 콘크리트 구조물 내화 및 내진 보강용 모르타르 조성물 및 이를 이용한 내화 내진 보수 공법을 제공한다. 본 발명에 따르면, 내진 보강 공사가 필요한 콘크리트 구조물을 시공함에 있어, 발수효과가 우수하고 흡수율을 낮게 유지할 수 있으므로 내구성이 우수하고, 부착강도, 압축강도, 휨강도 등의 물리적 특성이 우수하며, 모르타르의 단위 중량을 줄이고 초기 및 장기 부착성능을 향상시켜 콘크리트 구조물에 대한 내진 보강 시공성이 매우 우수한 동시에 유기 용제를 사용하지 않으므로 친환경적이며, 모르타르의 미세 틈새를 치밀하게 메울 수 있으므로 지진 진동 및 각종 응력을 균일하게 흡수하여 구조물의 내진 성능을 강화할 수 있는 동시에, 내열성 및 내화성이 우수하여 보수 후 화재 발생시에 폭열로 인한 문제 발생을 방지할 수 있는 효과가 있다.