MORTAR COMPOSITION AND REPAIRING METHOD FOR CONCRETE STRUCTURE THEREOF
The present invention relates to a mortar composition and a repairing method for a concrete structure using the same. According to the present invention, the mortar composition comprises: 10-30 wt% of blast furnace slag; 5-15 wt% of fly ash; 0.5-1.5 wt% of a high-range water-reducing agent; 40-60 wt% of fine aggregate; and 10-20 wt% of an alkali activator. The alkali activator comprises: 3-6 wt% of sodium hydroxide; 1-5 wt% of sodium carbon; 20-40 wt% of liquid sodium silicate; and 50-75 wt% of water, based on the weight of the alkali activator. According to the present invention, the blast furnace slag and fly ash are mixed with a combining material substituting for cement in the mortar composition. The alkali activator is added to solve the problem of a slump loss and degradation and strength and durability, which may occur as the blast furnace slag and fly ash are mixed. According to the present invention, the alkali activator is a liquid additive including a whole amount included in the composition. The alkali activator provides an excellent combining force of the blast furnace slag and fly ash and easily develops the strength of the composition.
본 발명의 몰탈 조성물은 고로슬래그 10~30 중량%; 플라이애시 5~15 중량%; 유동화제 0.5 ~ 1.5 중량%; 잔골재 40 ~ 60 중량%; 알칼리 자극제 10 ~ 20 중량%;를 포함한다. 알칼리 자극제는 알칼리 자극제의 중량을 기준으로, 수산화나트륨 3~6 중량%; 탄산나트륨 1~5 중량%; 액상규산나트륨 20~40 중량%; 물 50~75 중량%;를 포함하는 것이 바람직하다. 이 경우, 본 발명의 몰탈 조성물은 시멘트를 대체하는 결합재로 고로슬래그와 플라이애시가 혼합된다. 알칼리 자극제는 고로슬래그와 플라이애시가 혼합되어 발생할 수 있는 강도 및 내구성 저하, 슬럼프 손실 등의 문제를 해결하기 위해 첨가되는 것이다. 본원발명의 알칼리 자극제는 조성물에 들어가는 전체 수량을 포함하는 액상형 첨가제로서, 고로슬래그 및 플라이애시와 결합력이 우수하고, 조성물의 강도발현을 용이하게 하는 특징이 있다.
MORTAR COMPOSITION AND REPAIRING METHOD FOR CONCRETE STRUCTURE THEREOF
The present invention relates to a mortar composition and a repairing method for a concrete structure using the same. According to the present invention, the mortar composition comprises: 10-30 wt% of blast furnace slag; 5-15 wt% of fly ash; 0.5-1.5 wt% of a high-range water-reducing agent; 40-60 wt% of fine aggregate; and 10-20 wt% of an alkali activator. The alkali activator comprises: 3-6 wt% of sodium hydroxide; 1-5 wt% of sodium carbon; 20-40 wt% of liquid sodium silicate; and 50-75 wt% of water, based on the weight of the alkali activator. According to the present invention, the blast furnace slag and fly ash are mixed with a combining material substituting for cement in the mortar composition. The alkali activator is added to solve the problem of a slump loss and degradation and strength and durability, which may occur as the blast furnace slag and fly ash are mixed. According to the present invention, the alkali activator is a liquid additive including a whole amount included in the composition. The alkali activator provides an excellent combining force of the blast furnace slag and fly ash and easily develops the strength of the composition.
본 발명의 몰탈 조성물은 고로슬래그 10~30 중량%; 플라이애시 5~15 중량%; 유동화제 0.5 ~ 1.5 중량%; 잔골재 40 ~ 60 중량%; 알칼리 자극제 10 ~ 20 중량%;를 포함한다. 알칼리 자극제는 알칼리 자극제의 중량을 기준으로, 수산화나트륨 3~6 중량%; 탄산나트륨 1~5 중량%; 액상규산나트륨 20~40 중량%; 물 50~75 중량%;를 포함하는 것이 바람직하다. 이 경우, 본 발명의 몰탈 조성물은 시멘트를 대체하는 결합재로 고로슬래그와 플라이애시가 혼합된다. 알칼리 자극제는 고로슬래그와 플라이애시가 혼합되어 발생할 수 있는 강도 및 내구성 저하, 슬럼프 손실 등의 문제를 해결하기 위해 첨가되는 것이다. 본원발명의 알칼리 자극제는 조성물에 들어가는 전체 수량을 포함하는 액상형 첨가제로서, 고로슬래그 및 플라이애시와 결합력이 우수하고, 조성물의 강도발현을 용이하게 하는 특징이 있다.
MORTAR COMPOSITION AND REPAIRING METHOD FOR CONCRETE STRUCTURE THEREOF
몰탈 조성물 및 이를 이용한 콘크리트 구조물 보수공법
LEE CHIN YONG (Autor:in) / CHOI EUN SEOK (Autor:in)
25.05.2018
Patent
Elektronische Ressource
Koreanisch
Europäisches Patentamt | 2020
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2017
Concrete structure repairing mortar and repairing method
| Europäisches Patentamt | 2018