Eco-friendly hybrid waterproofing and rust resisting method
The present invention relates to a waterproofing and anti-corrosion method of a concrete structure, which reinforces waterproofness and durability of various kinds of concrete structures of a water purification plant, a sewage treatment plant, water/sewage pipe, and the like to protect a surface and prevent corrosion of an internal rebar. In particular, according to the present invention, the waterproofing and anti-corrosion method of a concrete structure comprises: a pretreatment step of washing a concrete base surface with high pressure water and smoothening the surface; a coating formation step of coating a rubber resin-based waterproofing/anti-corrosion agent on the pretreated base surface to form a coating; and a finishing step of washing the surface of the formed coating with high pressure water. The rubber resin-based waterproofing/anti-corrosion agent comprises: 50 to 80 weight percent of butyl rubber; 1 to 5 weight percent of organic amine; 5 to 10 weight percent of acrylic latex; 0.1 to 20 weight percent of a carbon reinforcement agent; 0.1 to 5 weight percent of a plasticizer; 10 to 20 weight percent of additives; and 5 to 10 weight percent of a curing promoter. Accordingly, since the rubber resin-based waterproofing/anti-corrosion agent is used, bonding property with a material to be coated is excellent, and properties, such as waterproofing and anti-chemical properties, are excellent, thereby providing performance to protect a surface of a concrete structure. Moreover, since a top coating agent including nano metal powder or nano metal oxide password is applied, properties, such as weatherability, thermal characteristics, wear resistance, impact resistance, crack resistance, and the like, are largely improved, thereby providing advantages of preventing corrosion of an internal rebar and maintaining a structure protection effect for a long period.
본 발명은 정수장이나 하수처리장, 상하수도관 등의 각종 콘크리트 구조물의 내수성과 내구성을 강화하여 표면을 보호하고 내부 철근의 부식을 방지할 수 있는 콘크리트 구조물 방수 방식 공법에 관한 것으로서, 구체적으로는 콘크리트 바탕면을 고압 세척하고 평활처리하는 전처리 단계; 상기 전처리된 바탕면에 고무 수지계 방수방식제를 도포하여 도막을 형성하는 도막 형성 단계; 상기 형성된 도막의 표면을 고압 세척하는 마감 단계;를 포함하여 구성되며, 상기 고무 수지계 방수방식제는 부틸고무 50~80 중량%, 유기아민 1~5중량%, 아크릴라텍스 5~10 중량%, 카본 보강제 0.1~20 중량%, 가소제 0.1~5 중량%, 첨가제 10~20 중량%, 및 경화촉진제 5~10 중량%을 포함하여 구성되는 것을 특징으로 하는 콘크리트 구조물의 방수 방식 공법을 제공한다. 본 발명에 따르면, 고무 수지계 방수 방식제를 사용함으로써 피도재와의 부착성이 우수하고 내수성 및 내약품성 등의 물성이 우수하여 콘크리트 구조물 표면을 보호하는 성능이 우수하며, 또한 나노 금속 분말 또는 나노 금속 산화물 분말이 포함된 탑 코팅제를 적용함으로써 내후성, 열적 특성, 내마모성, 내충격성, 내균열성 등의 물성이 대폭 향상될 수 있으므로 내부 철근의 부식을 방지할 수 있고 구조물의 보호 효과를 장기간 유지할 수 있는 장점이 있다.
Eco-friendly hybrid waterproofing and rust resisting method
The present invention relates to a waterproofing and anti-corrosion method of a concrete structure, which reinforces waterproofness and durability of various kinds of concrete structures of a water purification plant, a sewage treatment plant, water/sewage pipe, and the like to protect a surface and prevent corrosion of an internal rebar. In particular, according to the present invention, the waterproofing and anti-corrosion method of a concrete structure comprises: a pretreatment step of washing a concrete base surface with high pressure water and smoothening the surface; a coating formation step of coating a rubber resin-based waterproofing/anti-corrosion agent on the pretreated base surface to form a coating; and a finishing step of washing the surface of the formed coating with high pressure water. The rubber resin-based waterproofing/anti-corrosion agent comprises: 50 to 80 weight percent of butyl rubber; 1 to 5 weight percent of organic amine; 5 to 10 weight percent of acrylic latex; 0.1 to 20 weight percent of a carbon reinforcement agent; 0.1 to 5 weight percent of a plasticizer; 10 to 20 weight percent of additives; and 5 to 10 weight percent of a curing promoter. Accordingly, since the rubber resin-based waterproofing/anti-corrosion agent is used, bonding property with a material to be coated is excellent, and properties, such as waterproofing and anti-chemical properties, are excellent, thereby providing performance to protect a surface of a concrete structure. Moreover, since a top coating agent including nano metal powder or nano metal oxide password is applied, properties, such as weatherability, thermal characteristics, wear resistance, impact resistance, crack resistance, and the like, are largely improved, thereby providing advantages of preventing corrosion of an internal rebar and maintaining a structure protection effect for a long period.
본 발명은 정수장이나 하수처리장, 상하수도관 등의 각종 콘크리트 구조물의 내수성과 내구성을 강화하여 표면을 보호하고 내부 철근의 부식을 방지할 수 있는 콘크리트 구조물 방수 방식 공법에 관한 것으로서, 구체적으로는 콘크리트 바탕면을 고압 세척하고 평활처리하는 전처리 단계; 상기 전처리된 바탕면에 고무 수지계 방수방식제를 도포하여 도막을 형성하는 도막 형성 단계; 상기 형성된 도막의 표면을 고압 세척하는 마감 단계;를 포함하여 구성되며, 상기 고무 수지계 방수방식제는 부틸고무 50~80 중량%, 유기아민 1~5중량%, 아크릴라텍스 5~10 중량%, 카본 보강제 0.1~20 중량%, 가소제 0.1~5 중량%, 첨가제 10~20 중량%, 및 경화촉진제 5~10 중량%을 포함하여 구성되는 것을 특징으로 하는 콘크리트 구조물의 방수 방식 공법을 제공한다. 본 발명에 따르면, 고무 수지계 방수 방식제를 사용함으로써 피도재와의 부착성이 우수하고 내수성 및 내약품성 등의 물성이 우수하여 콘크리트 구조물 표면을 보호하는 성능이 우수하며, 또한 나노 금속 분말 또는 나노 금속 산화물 분말이 포함된 탑 코팅제를 적용함으로써 내후성, 열적 특성, 내마모성, 내충격성, 내균열성 등의 물성이 대폭 향상될 수 있으므로 내부 철근의 부식을 방지할 수 있고 구조물의 보호 효과를 장기간 유지할 수 있는 장점이 있다.
Eco-friendly hybrid waterproofing and rust resisting method
친환경 하이브리드 방수 방식 공법
CHOI WON YONG (Autor:in) / LEE HAK GEUN (Autor:in)
15.10.2018
Patent
Elektronische Ressource
Koreanisch
HYBRID ENVIRONMENT-FRIENDLY ROOFTOP WATERPROOFING METHOD
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2019
Eco-friendly waterproofing fluid and waterproofing method using it
| Europäisches Patentamt | 2024
Waterproofing method using eco-friendly water-soluble floor waterproofing agent
| Europäisches Patentamt | 2021