ANTI-WASH HIGH STRENGTH MORTAR FOR CONCRETE REPAIR
The present invention provides underwater anti-washout high strength mortar for concrete repair. With respect to the total 100 wt% of the underwater anti-washout high strength mortar for concrete repair, contained are: 36-44 wt% of a binder including ferromolybdenum slag and cement; 50-60 wt% of silica including recycled ferromolybdenum aggregate and artificial silica and having 2.8-3.2 of fine aggregate fitness modulus (FM);0.5-5 wt% of re-emulsification type powder resin; 0.05-2 wt% of an antifoaming agent; 0.04-1 wt% of polypropylene fiber; and 0.1-10 wt% of additives including one or more selected from a group consisting of anhydrous gypsum, an expansion agent, a fluidizing agent and an inorganic thickener, wherein 10-40 wt% of the ferromolybdenum slag is contained with respect to the total 100 wt% of a binder. The present invention provides the anti-washout underwater high strength mortar for concrete repair, which has underwater anti-washout properties to show high strength after construction and has easy workability even at a low water ratio.
본 발명에 따른 수중 불분리형 고강도 콘크리트 보수용 모르타르는 수중 불분리형 고강도 콘크리트 보수용 모르타르 전체 100 중량%에 대하여, 페로몰리브덴 슬래그 및 시멘트를 함유하는 바인더 36 내지 44 중량%; 페로몰리브덴 재생골재 및 인조 규사를 함유하고, 잔골재 조립율(FM)이 2.8 내지 3.2인 규사 50 내지 60 중량%; 재유화형 분말수지 0.5 내지 5 중량%; 소포제 0.05 내지 2 중량%; 폴리프로필렌 파이버 0.04 내지 1 중량%; 및 무수석고, 팽창제, 유동화제 및 무기 증점제로 이루어진 군에서 선택되는 1 이상을 포함하는 첨가제 0.1 내지 10 중량%;를 포함하고, 상기 페로몰리브덴 슬래그는 상기 바인더 전체 100 중량%에 대하여 10 내지 40 중량%로 포함되는, 것을 특징으로 한다. 본 발명에 따른 수중 불분리형 고강도 콘크리트 보수용 모르타르는 수중 불분리성을 가지고, 시공 후 고강도를 나타내는 이점이 있으며, 낮은 물비율에서도 작업성이 용이한 이점이 있다.
ANTI-WASH HIGH STRENGTH MORTAR FOR CONCRETE REPAIR
The present invention provides underwater anti-washout high strength mortar for concrete repair. With respect to the total 100 wt% of the underwater anti-washout high strength mortar for concrete repair, contained are: 36-44 wt% of a binder including ferromolybdenum slag and cement; 50-60 wt% of silica including recycled ferromolybdenum aggregate and artificial silica and having 2.8-3.2 of fine aggregate fitness modulus (FM);0.5-5 wt% of re-emulsification type powder resin; 0.05-2 wt% of an antifoaming agent; 0.04-1 wt% of polypropylene fiber; and 0.1-10 wt% of additives including one or more selected from a group consisting of anhydrous gypsum, an expansion agent, a fluidizing agent and an inorganic thickener, wherein 10-40 wt% of the ferromolybdenum slag is contained with respect to the total 100 wt% of a binder. The present invention provides the anti-washout underwater high strength mortar for concrete repair, which has underwater anti-washout properties to show high strength after construction and has easy workability even at a low water ratio.
본 발명에 따른 수중 불분리형 고강도 콘크리트 보수용 모르타르는 수중 불분리형 고강도 콘크리트 보수용 모르타르 전체 100 중량%에 대하여, 페로몰리브덴 슬래그 및 시멘트를 함유하는 바인더 36 내지 44 중량%; 페로몰리브덴 재생골재 및 인조 규사를 함유하고, 잔골재 조립율(FM)이 2.8 내지 3.2인 규사 50 내지 60 중량%; 재유화형 분말수지 0.5 내지 5 중량%; 소포제 0.05 내지 2 중량%; 폴리프로필렌 파이버 0.04 내지 1 중량%; 및 무수석고, 팽창제, 유동화제 및 무기 증점제로 이루어진 군에서 선택되는 1 이상을 포함하는 첨가제 0.1 내지 10 중량%;를 포함하고, 상기 페로몰리브덴 슬래그는 상기 바인더 전체 100 중량%에 대하여 10 내지 40 중량%로 포함되는, 것을 특징으로 한다. 본 발명에 따른 수중 불분리형 고강도 콘크리트 보수용 모르타르는 수중 불분리성을 가지고, 시공 후 고강도를 나타내는 이점이 있으며, 낮은 물비율에서도 작업성이 용이한 이점이 있다.
ANTI-WASH HIGH STRENGTH MORTAR FOR CONCRETE REPAIR
수중 불분리형 고강도 콘크리트 보수용 모르타르
LEE SANG JAE (Autor:in)
10.12.2018
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
HIGH DURABILITY MORTAR COMPOSITION FOR CONCRETE REPAIR AND CONCRETE REPAIR METHOD USING THE MORTAR
| Europäisches Patentamt | 2015