Modified asphalt based sealant composition and manufacturing thereof
The present invention relates to a modified asphalt sealant composition which is used as crack repairing materials, expansion joints, porthole repairing materials, various filling materials, waterproofing materials, and binders for the construction and repair of pavement, buildings, bridges, and civil structures, and a method for manufacturing the same. The composition comprises 0.01-0.1 parts by weight of graphene oxide (GO), 1-30 parts by weight of a softener, 5-40 parts by weight of thermoplastic elastomer (TPE), 5-30 parts by weight of crumb rubber, 1-30 parts by weight of a petroleum resin based on 100 parts by weight of an asphalt binder modified with a styrene-butadiene-styrene block copolymer. The modified asphalt sealant composition according to the present invention uses nano-material graphene oxide (GO) to modify the asphalt binder to significantly enhance the mechanical performance and durability to ensure durability by applying the composition to pavement and civil structures, thereby contributing to life extension.
본 발명은 포장도로, 건축물, 교량 및 토목 구조물의 신설 및 보수에 균열 보수재, 신축이음재, 포트홀 보수재, 각종 채움재, 방수재 및 바인더 등으로 사용되는 개질 아스팔트계 실란트 조성물 및 이의 제조방법에 관한 것으로 스티렌-부타디엔-스티렌 블록 공중합체로 개질된 아스팔트 바인더 100 중량부에 산화 그래핀(Graphene oxide, GO) 0.01 내지 0.1 중량부, 연화제 1 내지 30 중량부, 열가소성 탄성체(TPE) 5 내지 40 중량부, 고무분말(Crumb Rubber) 5 내지 30 중량부, 석유수지 1 내지 30 중량부를 포함하는 것을 특징으로 한다. 본 발명에 따른 개질 아스팔트계 실란트 조성물은 아스팔트 바인더를 개질 시키기 위해 나노물질인 산화 그래핀(Graphene oxide, GO)을 적용함으로써 기계적 성능과 내구성을 크게 향상시켜 포장도로 및 토목 구조물에 적용함으로써 내구성을 확보하여 수명연장에 기여 할 수 있다.
Modified asphalt based sealant composition and manufacturing thereof
The present invention relates to a modified asphalt sealant composition which is used as crack repairing materials, expansion joints, porthole repairing materials, various filling materials, waterproofing materials, and binders for the construction and repair of pavement, buildings, bridges, and civil structures, and a method for manufacturing the same. The composition comprises 0.01-0.1 parts by weight of graphene oxide (GO), 1-30 parts by weight of a softener, 5-40 parts by weight of thermoplastic elastomer (TPE), 5-30 parts by weight of crumb rubber, 1-30 parts by weight of a petroleum resin based on 100 parts by weight of an asphalt binder modified with a styrene-butadiene-styrene block copolymer. The modified asphalt sealant composition according to the present invention uses nano-material graphene oxide (GO) to modify the asphalt binder to significantly enhance the mechanical performance and durability to ensure durability by applying the composition to pavement and civil structures, thereby contributing to life extension.
본 발명은 포장도로, 건축물, 교량 및 토목 구조물의 신설 및 보수에 균열 보수재, 신축이음재, 포트홀 보수재, 각종 채움재, 방수재 및 바인더 등으로 사용되는 개질 아스팔트계 실란트 조성물 및 이의 제조방법에 관한 것으로 스티렌-부타디엔-스티렌 블록 공중합체로 개질된 아스팔트 바인더 100 중량부에 산화 그래핀(Graphene oxide, GO) 0.01 내지 0.1 중량부, 연화제 1 내지 30 중량부, 열가소성 탄성체(TPE) 5 내지 40 중량부, 고무분말(Crumb Rubber) 5 내지 30 중량부, 석유수지 1 내지 30 중량부를 포함하는 것을 특징으로 한다. 본 발명에 따른 개질 아스팔트계 실란트 조성물은 아스팔트 바인더를 개질 시키기 위해 나노물질인 산화 그래핀(Graphene oxide, GO)을 적용함으로써 기계적 성능과 내구성을 크게 향상시켜 포장도로 및 토목 구조물에 적용함으로써 내구성을 확보하여 수명연장에 기여 할 수 있다.
Modified asphalt based sealant composition and manufacturing thereof
개질 아스팔트계 실란트 조성물 및 이의 제조방법
MOON EUI SEONG (Autor:in) / MOON YOUNG GYU (Autor:in) / KIM DU BYUNG (Autor:in)
01.08.2019
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
Performance optimization of composite modified asphalt sealant based on rheological behavior
| Online Contents | 2013
Performance optimization of composite modified asphalt sealant based on rheological behavior
| British Library Online Contents | 2013