SELF COMPACTING CONCRETE USING VISCOSITY MODIFIER FOR COMMON CONCRETE
The present invention relates to self-compacting concrete for moderate strength using a mixture for viscosity control. The present invention is to provide self-compacting concrete for moderate strength which implements flow performance and compacting performance in a low powder area without material separation. The total powder content of a binder containing low-density and bulky fly ash and a blast furnace slag admixture in cement is lowered to 350 kg/m^3 or less, and a coarse aggregate is used to secure the viscosity in concrete. In particular, by containing a mixture for adjusting the viscosity in the concrete mixture, a three-dimensional structure in a liquid phase by interaction with blending water and a fine powder surface is formed to increase the volume per unit volume in the concrete mixture. Accordingly, since the fluidity and viscosity are maintained at the compressive strength of 21-24 MPa when concrete is mixed, the concrete can be applied to various parts including general buildings or general construction sites.
본 발명은 점성조절용 혼합물을 이용한 보통강도용 자기 충전 콘크리트에 관한 것이다. 본 발명은 저분체 영역에서 재료분리 없이 유동성능 및 채움 성능을 구현한 보통강도용 자기 충전 콘크리트를 제공하기 위하여, 시멘트에 밀도가 낮고 부피가 큰 플라이애시 및 고로슬래그 미분말의 혼화재료를 포함한 결합재의 총 분체량을 350kg/㎥ 이하로 낮추고, 굵은골재 사용량을 조절하여 콘크리트 내 점성을 확보하고, 특히, 콘크리트 배합 내 점성조절용 혼합물을 함유하여, 배합수와 및 미세 분체 표면과의 상호 작용에 의해 액상에서 3차원 구조를 형성함으로써 콘크리트 배합 내 단위용적당 부피를 높여, 콘크리트 배합 시 압축강도 21 내지 24㎫에서 유동성과 점성이 유지되므로, 일반건축물 또는 일반 건설현장을 비롯한 다양한 부위에 적용이 가능할 것이다.
SELF COMPACTING CONCRETE USING VISCOSITY MODIFIER FOR COMMON CONCRETE
The present invention relates to self-compacting concrete for moderate strength using a mixture for viscosity control. The present invention is to provide self-compacting concrete for moderate strength which implements flow performance and compacting performance in a low powder area without material separation. The total powder content of a binder containing low-density and bulky fly ash and a blast furnace slag admixture in cement is lowered to 350 kg/m^3 or less, and a coarse aggregate is used to secure the viscosity in concrete. In particular, by containing a mixture for adjusting the viscosity in the concrete mixture, a three-dimensional structure in a liquid phase by interaction with blending water and a fine powder surface is formed to increase the volume per unit volume in the concrete mixture. Accordingly, since the fluidity and viscosity are maintained at the compressive strength of 21-24 MPa when concrete is mixed, the concrete can be applied to various parts including general buildings or general construction sites.
본 발명은 점성조절용 혼합물을 이용한 보통강도용 자기 충전 콘크리트에 관한 것이다. 본 발명은 저분체 영역에서 재료분리 없이 유동성능 및 채움 성능을 구현한 보통강도용 자기 충전 콘크리트를 제공하기 위하여, 시멘트에 밀도가 낮고 부피가 큰 플라이애시 및 고로슬래그 미분말의 혼화재료를 포함한 결합재의 총 분체량을 350kg/㎥ 이하로 낮추고, 굵은골재 사용량을 조절하여 콘크리트 내 점성을 확보하고, 특히, 콘크리트 배합 내 점성조절용 혼합물을 함유하여, 배합수와 및 미세 분체 표면과의 상호 작용에 의해 액상에서 3차원 구조를 형성함으로써 콘크리트 배합 내 단위용적당 부피를 높여, 콘크리트 배합 시 압축강도 21 내지 24㎫에서 유동성과 점성이 유지되므로, 일반건축물 또는 일반 건설현장을 비롯한 다양한 부위에 적용이 가능할 것이다.
SELF COMPACTING CONCRETE USING VISCOSITY MODIFIER FOR COMMON CONCRETE
점성조절용 혼합물을 이용한 보통강도용 자기충전 콘크리트
JEONG YONG (Autor:in) / YOON SEOB (Autor:in) / LEE HAN YONG (Autor:in) / MOON BYEONG YONG (Autor:in) / KIM JUNG BIN (Autor:in) / YUN IL SANG (Autor:in)
16.08.2019
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
SELF-COMPACTING CONCRETE - Self-compacting concrete
| Online Contents | 2000
SELF-COMPACTING CONCRETE - Self-compacting concrete at Millennium Point
| Online Contents | 2000
SELF-COMPACTING CONCRETE : Self-compacting concrete containing granite powder
| Online Contents | 2013
Degree of segregation of self-compacting concrete using viscosity agent
| British Library Conference Proceedings | 2006