The present invention relates to a surface layer-reinforcing rapid hardening cement concrete composition and a method of repairing and reinforcing pavement of a road using the same. The surface layer-reinforcing rapid hardening cement concrete composition comprises: 3-50 wt% of an initial strength expressing agent; 5-65 wt% of fine aggregate; 3-65 wt% of coarse aggregate; 0.01-30 wt% of a performance expressing agent; and 0.1-30 wt% of water. The performance expressing agent includes: 30-98 wt% of a styrene-methyl methacrylate-butyl acrylate copolymer; 1-25 wt% of an acrylic acid alkyl ester-acrylonitrile copolymer; 0.1-15 wt% of an ethylene-methylmethacrylate-vinyl acetate copolymer; 0.1-15 wt% of polyacrylic acid methyl; 0.1-15 wt% of a polyisobutyl methacrylate copolymer; 0.1-5 wt% of a polycarboxylic acid-based reducing agent; and 0.1-5 wt% of a silicon-based antifoaming agent. According to the present invention, the surface layer-reinforcing rapid hardening cement concrete composition is capable of increasing workability of concrete, improving strength of concrete, and specifically, strengthening a surface layer to improve scaling resistance, prevent generation of cracks, and greatly increase durability. In addition, the present invention is capable of producing dense concrete by promoting early hydration of cement and densification of tissues, thereby improving strength and durability, especially waterproof and rustproof performance of concrete. Furthermore, an expansion material and a shrinkage reducing agent are used to prevent surface cracking and expansion/destruction phenomena caused by drying shrinkage. Meanwhile, the present invention is able to satisfy all conditions required for pavement of a road, that is, wear resistance, watertightness, adhesion, durability, and crack resistance.

본 발명은 표층강화형 초속경 시멘트 콘크리트 조성물 및 이를 이용한 도로 포장 보수· 보강 공법에 관한 것으로, 초기강도 발현재 3∼50중량%, 잔골재 5∼65중량%, 굵은골재 3∼65중량%, 성능 발현제 0.01∼30 중량% 및 물 0.1∼30중량%를 포함하며, 상기 성능 발현제는 스티렌-메틸메타크릴레이트-부틸아크릴레이트 공중합체 30∼98중량%, 아크릴산알킬에스터-아크릴로니트릴 공중합체 1∼25중량%, 에틸렌-메틸메타크릴레이트-초산비닐 공중합체 0.1∼15중량%, 폴리아크릴산메틸 0.1∼15중량%, 폴리이소부틸메타크릴레이트 공중합체 0.1∼15중량%, 폴리칼본산계 감수제 0.1~5중량% 및 실리콘계 소포제 0.1~5중량%를 포함하는 것을 특징으로 하는 것이다. 본 발명에 따른 초속경 시멘트 콘크리트 조성물은 콘크리트의 작업성을 향상시킬 수 있고, 콘크리트의 강도를 개선하며, 특히 표층을 강화하여 스켈링저항성을 개선하고 균열을 방지하고 내구성을 크게 향상시킬 수 있다. 또한, 시멘트의 초기 수화 및 조직의 치밀화를 촉진하여 밀실한 콘크리트를 만들 수 있어 콘크리트의 강도 및 내구성, 특히 방수· 방청성을 개선할 수 있다. 또한, 팽창재와 수축저감제를 사용함으로써 건조수축에 의한 표면균열 및 팽창파괴현상을 방지하는 효과를 발휘할 수 있는 효과를 얻을 수 있다. 한편, 포장에 요구되는 제반 특성, 즉 내마모성, 수밀성, 부착성, 내구성 및 균열 저항성 등을 모두 만족할 수 있다.