SIS PSMA Middle Temperature Modified-Resin Stone Mastic Asphalt Concrete Compositions Using Stylene Isoprene Stylene and Constructing Methods Using Thereof
The present invention provides a middle temperature polymer-modified stone mastic asphalt (PSMA) concrete composition using styrene-isoprene-styrene (SIS), and a construction method thereof. According to the present invention, the middle temperature PMSA concrete composition comprises with respect to 100 parts by weight of asphalt: 1 to 25 parts by weight of SIS; 1 to 25 parts by weight of hydrogenated petroleum resin; 500 to 2,000 parts by weight of aggregates; 10 to 90 parts by weight of fine powder aggregates; 0.5 to 10 parts by weight of a modifier; 0.5 to 25 parts by weight of ethylene-propylene copolymer; 0.1 to 2 parts by weight of cellulose fiber; and 0.1 to 2 parts by weight of a middle temperature additive. Accordingly, the middle temperature PMSA concrete composition using SIS provides effects of providing high durability, easily performing a deposition process at low cost without easily generating plastic deformation, aging, and/or defoliation, being deposited and/or paved at a middle temperature lower than that of a conventional asphalt concrete composition, and reducing plastic deformation quickly generated in summer.
본 발명은 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 25중량부; 수소가 첨가된 석유수지 1 내지 25중량부; 골재 500 내지 2,000중량부; 미분말 골재 10 내지 90중량부; 개질제 0.5 내지 10중량부; 에틸렌-프로필렌 공중합체 0.5 내지 25중량부; 셀룰로오스 섬유 0.1 내지 2중량부; 및 중온화 첨가제 0.1 내지 2중량부를 포함하는 고분자 개질 쇄석 매스틱 아스팔트 콘크리트 조성물 및 이를 이용한 시공방법을 제공한다. 본 발명에 따른 SIS를 이용한 중온 고분자 개질 쇄석 매스틱 아스팔트 콘크리트 조성물, 특정적으로 SIS를 이용한 중온 고분자 개질 쇄석 매스틱 아스팔트 콘크리트 조성물은 내구성이 좋고, 소성변형, 노화 및/또는 박리가 쉽게 발생하지 않으면서도, 저비용으로 타설공정을 용이하게 수행할 수 있을 뿐만 아니라, 일반 아스팔트 콘크리트 조성물 보다 낮은 온도인 중온에서 타설 및/또는 포설이 가능하고, 여름철 등에 급속하게 발생하는 소성변형을 감소시킬 수 있도록 하는 등의 효과가 있다.
SIS PSMA Middle Temperature Modified-Resin Stone Mastic Asphalt Concrete Compositions Using Stylene Isoprene Stylene and Constructing Methods Using Thereof
The present invention provides a middle temperature polymer-modified stone mastic asphalt (PSMA) concrete composition using styrene-isoprene-styrene (SIS), and a construction method thereof. According to the present invention, the middle temperature PMSA concrete composition comprises with respect to 100 parts by weight of asphalt: 1 to 25 parts by weight of SIS; 1 to 25 parts by weight of hydrogenated petroleum resin; 500 to 2,000 parts by weight of aggregates; 10 to 90 parts by weight of fine powder aggregates; 0.5 to 10 parts by weight of a modifier; 0.5 to 25 parts by weight of ethylene-propylene copolymer; 0.1 to 2 parts by weight of cellulose fiber; and 0.1 to 2 parts by weight of a middle temperature additive. Accordingly, the middle temperature PMSA concrete composition using SIS provides effects of providing high durability, easily performing a deposition process at low cost without easily generating plastic deformation, aging, and/or defoliation, being deposited and/or paved at a middle temperature lower than that of a conventional asphalt concrete composition, and reducing plastic deformation quickly generated in summer.
본 발명은 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 25중량부; 수소가 첨가된 석유수지 1 내지 25중량부; 골재 500 내지 2,000중량부; 미분말 골재 10 내지 90중량부; 개질제 0.5 내지 10중량부; 에틸렌-프로필렌 공중합체 0.5 내지 25중량부; 셀룰로오스 섬유 0.1 내지 2중량부; 및 중온화 첨가제 0.1 내지 2중량부를 포함하는 고분자 개질 쇄석 매스틱 아스팔트 콘크리트 조성물 및 이를 이용한 시공방법을 제공한다. 본 발명에 따른 SIS를 이용한 중온 고분자 개질 쇄석 매스틱 아스팔트 콘크리트 조성물, 특정적으로 SIS를 이용한 중온 고분자 개질 쇄석 매스틱 아스팔트 콘크리트 조성물은 내구성이 좋고, 소성변형, 노화 및/또는 박리가 쉽게 발생하지 않으면서도, 저비용으로 타설공정을 용이하게 수행할 수 있을 뿐만 아니라, 일반 아스팔트 콘크리트 조성물 보다 낮은 온도인 중온에서 타설 및/또는 포설이 가능하고, 여름철 등에 급속하게 발생하는 소성변형을 감소시킬 수 있도록 하는 등의 효과가 있다.
SIS PSMA Middle Temperature Modified-Resin Stone Mastic Asphalt Concrete Compositions Using Stylene Isoprene Stylene and Constructing Methods Using Thereof
SIS를 이용한 중온 고분자 개질 쇄석 매스틱 아스팔트 콘크리트(PSMA) 조성물 및 이의 시공방법
KIM IN JUNG (Autor:in)
13.02.2020
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2019
| Europäisches Patentamt | 2019
| Europäisches Patentamt | 2019