RAPID HARDENING CONCRETE COMPOSITION FOR BRIDGE DECK OVERLAY CONCRETE PAVEMENT USING FERRO-NICKEL SLAG AND THE COSTRUCTION METHOD OF BRIDGE DECK OVERLAY CONCRETE PAVEMENT THEREOF
The present invention relates to a rapid-hardening concrete composition for bridge deck overlay pavement using classified ferro-nickel slag fine aggregate, and a method for constructing bridge deck overlay pavement using the same. The rapid-hardening concrete composition for bridge deck overlay pavement includes: 100 parts by weight of rapid-hardening cement; 200-250 parts by weight of ferro-nickel slag fine aggregate classified into a particle size of 1.2-2.5 mm; 5-20 parts by weight of a mixed thickener containing a cellulose-based thickener, acrylic thickener and a polyethylene oxide-based thickener at the same weight ratio; and 50-80 parts by weight of water. The rapid-hardening concrete composition provides improved cement bondability, water-proof property, cracking resistance and salt damage resistance by virtue of the effect of removing fine voids of the mixed thickener.
본 발명은 분급된 페로니켈 슬래그 잔골재를 사용한 초속경 콘크리트 교면포장 조성물 및 이를 이용한 교면포장 시공방법에 관한 것으로, 보다 상세하게는 초속경시멘트 100중량부와; 입자크기 1.2~2.5mm로 분급된 페로니켈슬래그 잔골재 200~250중량부와; 셀룰로오스계 증점제, 아크릴계 증점제 및 폴리에틸렌 옥사이드계 증점제가 각각 동일중량비로 혼합된 혼합증점제 5~20중량부와; 물 50~80중량부;를 포함하여 조성되어 혼합증점제에 의한 미세공극제거효과에 따른 시멘트 결합력 향상, 방수, 균열 저항성 및 염해저항성을 향상시키기 위한 분급된 페로니켈 슬래그 잔골재를 사용한 초속경 콘크리트 교면포장 조성물 및 이를 이용한 교면포장 시공방법에 관한 것이다.
RAPID HARDENING CONCRETE COMPOSITION FOR BRIDGE DECK OVERLAY CONCRETE PAVEMENT USING FERRO-NICKEL SLAG AND THE COSTRUCTION METHOD OF BRIDGE DECK OVERLAY CONCRETE PAVEMENT THEREOF
The present invention relates to a rapid-hardening concrete composition for bridge deck overlay pavement using classified ferro-nickel slag fine aggregate, and a method for constructing bridge deck overlay pavement using the same. The rapid-hardening concrete composition for bridge deck overlay pavement includes: 100 parts by weight of rapid-hardening cement; 200-250 parts by weight of ferro-nickel slag fine aggregate classified into a particle size of 1.2-2.5 mm; 5-20 parts by weight of a mixed thickener containing a cellulose-based thickener, acrylic thickener and a polyethylene oxide-based thickener at the same weight ratio; and 50-80 parts by weight of water. The rapid-hardening concrete composition provides improved cement bondability, water-proof property, cracking resistance and salt damage resistance by virtue of the effect of removing fine voids of the mixed thickener.
본 발명은 분급된 페로니켈 슬래그 잔골재를 사용한 초속경 콘크리트 교면포장 조성물 및 이를 이용한 교면포장 시공방법에 관한 것으로, 보다 상세하게는 초속경시멘트 100중량부와; 입자크기 1.2~2.5mm로 분급된 페로니켈슬래그 잔골재 200~250중량부와; 셀룰로오스계 증점제, 아크릴계 증점제 및 폴리에틸렌 옥사이드계 증점제가 각각 동일중량비로 혼합된 혼합증점제 5~20중량부와; 물 50~80중량부;를 포함하여 조성되어 혼합증점제에 의한 미세공극제거효과에 따른 시멘트 결합력 향상, 방수, 균열 저항성 및 염해저항성을 향상시키기 위한 분급된 페로니켈 슬래그 잔골재를 사용한 초속경 콘크리트 교면포장 조성물 및 이를 이용한 교면포장 시공방법에 관한 것이다.
RAPID HARDENING CONCRETE COMPOSITION FOR BRIDGE DECK OVERLAY CONCRETE PAVEMENT USING FERRO-NICKEL SLAG AND THE COSTRUCTION METHOD OF BRIDGE DECK OVERLAY CONCRETE PAVEMENT THEREOF
분급된 페로니켈 슬래그 잔골재를 사용한 초속경 콘크리트 교면포장 조성물 및 이를 이용한 교면포장 시공방법
KAWG EUN GU (Autor:in) / HAN SANG IL (Autor:in)
29.04.2020
Patent
Elektronische Ressource
Koreanisch