SIS SEBS Middle Temperature Asphalt Concrete Compositions Having Styrene Isoprene Styrene Styrene Ethylene Butylene Styrene and Aggregate-powder of Improved Grain Size and Constructing Methods Using Thereof
The present invention relates to a medium-temperature asphalt concrete composition and a construction method using the composition, wherein the medium-temperature asphalt concrete composition contains, based on 100 parts by weight of asphalt: 1 to 25 parts by weight of styrene isoprene styrene; 1 to 25 parts by weight of a styrene ethylene butylene styrene copolymer; 1 to 25 parts by weight of a petroleum resin; 500 to 2,000 parts by weight of aggregate; 30 to 150 parts by weight of aggregate powder; 0.1 to 2 parts by weight of cellulose fiber; 0.1 to 2 parts by weight of wax; and 0.1 to 2 parts by weight of antioxidant. The medium-temperature asphalt concrete composition according to the present invention, the medium-temperature asphalt concrete composition having SIS, SEBS, and aggregate powder of improved grain size to be specific, is highly durable, and plastic deformation, aging, and/or peeling is unlikely to occur. In addition, a pouring process can be carried out with ease and at a low cost and pouring and/or laying can be performed at a medium temperature lower than the temperature of a plain asphalt concrete composition.
본 발명은 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 25중량부; 스티렌에틸렌부틸렌스티렌 공중합체 1 내지 25중량부; 석유수지 1 내지 25중량부; 골재 500 내지 2,000중량부; 미분말 골재 30 내지 150중량부; 셀룰로오스 섬유 0.1 내지 2중량부; 왁스 0.1 내지 2중량부; 및 산화방지제 0.1 내지 2중량부를 포함하는 중온아스팔트 콘크리트 조성물 및 이를 이용한 시공방법을 제공한다. 본 발명에 따른 중온아스팔트 콘크리트 조성물, 특정적으로 SIS, SEBS 및 개선된 골재 입도의 미분말 골재를 포함하는 중온아스팔트 콘크리트 조성물은 내구성이 좋고, 소성변형, 노화 및/또는 박리가 쉽게 발생하지 않으면서도, 저비용으로 타설공정을 용이하게 수행할 수 있을 뿐만 아니라, 일반 아스팔트 콘크리트 조성물 보다 낮은 온도인 중온에서 타설 및/또는 포설이 가능하도록 하는 등의 효과가 있다.
SIS SEBS Middle Temperature Asphalt Concrete Compositions Having Styrene Isoprene Styrene Styrene Ethylene Butylene Styrene and Aggregate-powder of Improved Grain Size and Constructing Methods Using Thereof
The present invention relates to a medium-temperature asphalt concrete composition and a construction method using the composition, wherein the medium-temperature asphalt concrete composition contains, based on 100 parts by weight of asphalt: 1 to 25 parts by weight of styrene isoprene styrene; 1 to 25 parts by weight of a styrene ethylene butylene styrene copolymer; 1 to 25 parts by weight of a petroleum resin; 500 to 2,000 parts by weight of aggregate; 30 to 150 parts by weight of aggregate powder; 0.1 to 2 parts by weight of cellulose fiber; 0.1 to 2 parts by weight of wax; and 0.1 to 2 parts by weight of antioxidant. The medium-temperature asphalt concrete composition according to the present invention, the medium-temperature asphalt concrete composition having SIS, SEBS, and aggregate powder of improved grain size to be specific, is highly durable, and plastic deformation, aging, and/or peeling is unlikely to occur. In addition, a pouring process can be carried out with ease and at a low cost and pouring and/or laying can be performed at a medium temperature lower than the temperature of a plain asphalt concrete composition.
본 발명은 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 25중량부; 스티렌에틸렌부틸렌스티렌 공중합체 1 내지 25중량부; 석유수지 1 내지 25중량부; 골재 500 내지 2,000중량부; 미분말 골재 30 내지 150중량부; 셀룰로오스 섬유 0.1 내지 2중량부; 왁스 0.1 내지 2중량부; 및 산화방지제 0.1 내지 2중량부를 포함하는 중온아스팔트 콘크리트 조성물 및 이를 이용한 시공방법을 제공한다. 본 발명에 따른 중온아스팔트 콘크리트 조성물, 특정적으로 SIS, SEBS 및 개선된 골재 입도의 미분말 골재를 포함하는 중온아스팔트 콘크리트 조성물은 내구성이 좋고, 소성변형, 노화 및/또는 박리가 쉽게 발생하지 않으면서도, 저비용으로 타설공정을 용이하게 수행할 수 있을 뿐만 아니라, 일반 아스팔트 콘크리트 조성물 보다 낮은 온도인 중온에서 타설 및/또는 포설이 가능하도록 하는 등의 효과가 있다.
SIS SEBS Middle Temperature Asphalt Concrete Compositions Having Styrene Isoprene Styrene Styrene Ethylene Butylene Styrene and Aggregate-powder of Improved Grain Size and Constructing Methods Using Thereof
SIS, SEBS 및 개선된 골재 입도의 미분말 골재를 포함하는 중온아스팔트 콘크리트 조성물 및 이의 시공방법