High grade asphalt concrete composition for thin overlay pavement and constructing method using the same
The present invention relates to a high-grade asphalt concrete composition for thin overlay pavement capable of forming high-temperature mixed asphalt by containing 3 to 8 wt% of an asphalt binder, 85 to 95 wt% of aggregate, 1 to 3 wt% of a filler, and 1.5 to 5 wt% of a high-temperature mixed modifier. The high-temperature mixed modifier contains an elastic polymer, a plastic polymer, oil, a filling agent, wax, and an additive for thin overlay pavement. The additive for thin overlay pavement contains 40 to 60 parts by weight of a fluorine resin, 30 to 50 parts by weight of isobornyl acrylate, 10 to 30 parts by weight of polyalkylene glycol, 5 to 25 parts by weight of triacetin, and 1 to 10 parts by weight of aluminum sulfate (Al_2(SO_4)) with respect to 100 parts by weight of a polylactic acid resin. With the high-grade asphalt concrete composition for thin overlay pavement and a construction method thereof, a high common PG performance grade of (PG 88-34, PG 94-34, PG 100-34) is met, excellent durability is achieved even with thin packaging, plastic deformation, aging and peeling are suppressed, infiltration water and potholes can be prevented, and salt damage and neutralization can be prevented.
본 발명은 아스팔트 바인더 3 내지 8 중량%, 골재 85 내지 95 중량%, 채움재 1 내지 3 중량% 및 고온 혼합식 개질재 1.5 내지 5 중량%를 포함하여 고온 혼합식 아스팔트를 형성할 수 있는 박층포장용 고등급 아스팔트 콘크리트 조성물에 관한 것으로, 상기 고온 혼합식 개질재는 탄성 중합체, 소성 중합체, 오일, 충전제, 왁스 및 박층포장용 첨가제를 포함하는 것이고, 상기 박층포장용 첨가제는 폴리유산 수지 100 중량부에 대하여, 불소수지 40 내지 60 중량부, 이소보닐 아크릴레이트 30 내지 50 중량부, 폴리알킬렌글리콜 10 내지 30 중량부, 트리아세틴 5 내지 25 중량부 및 황산알루미늄(Al(SO)) 1 내지 10 중량부를 포함하여; PG 등급성능이 고등급(PG 88-34, PG 94-34, PG 100-34)인 공용성 등급이고, 박층으로 포장되어도 내구성이 좋고, 소성변형, 노화 및 박리가 쉽게 발생하지 않으면서도, 침투수 및 포트홀을 방지할 수 있을 뿐만 아니라, 염해방지 및 중성화를 방지할 수 있는 박층포장용 고등급 아스팔트 콘크리트 조성물 및 이의 시공방법에 관한 것이다.
High grade asphalt concrete composition for thin overlay pavement and constructing method using the same
The present invention relates to a high-grade asphalt concrete composition for thin overlay pavement capable of forming high-temperature mixed asphalt by containing 3 to 8 wt% of an asphalt binder, 85 to 95 wt% of aggregate, 1 to 3 wt% of a filler, and 1.5 to 5 wt% of a high-temperature mixed modifier. The high-temperature mixed modifier contains an elastic polymer, a plastic polymer, oil, a filling agent, wax, and an additive for thin overlay pavement. The additive for thin overlay pavement contains 40 to 60 parts by weight of a fluorine resin, 30 to 50 parts by weight of isobornyl acrylate, 10 to 30 parts by weight of polyalkylene glycol, 5 to 25 parts by weight of triacetin, and 1 to 10 parts by weight of aluminum sulfate (Al_2(SO_4)) with respect to 100 parts by weight of a polylactic acid resin. With the high-grade asphalt concrete composition for thin overlay pavement and a construction method thereof, a high common PG performance grade of (PG 88-34, PG 94-34, PG 100-34) is met, excellent durability is achieved even with thin packaging, plastic deformation, aging and peeling are suppressed, infiltration water and potholes can be prevented, and salt damage and neutralization can be prevented.
본 발명은 아스팔트 바인더 3 내지 8 중량%, 골재 85 내지 95 중량%, 채움재 1 내지 3 중량% 및 고온 혼합식 개질재 1.5 내지 5 중량%를 포함하여 고온 혼합식 아스팔트를 형성할 수 있는 박층포장용 고등급 아스팔트 콘크리트 조성물에 관한 것으로, 상기 고온 혼합식 개질재는 탄성 중합체, 소성 중합체, 오일, 충전제, 왁스 및 박층포장용 첨가제를 포함하는 것이고, 상기 박층포장용 첨가제는 폴리유산 수지 100 중량부에 대하여, 불소수지 40 내지 60 중량부, 이소보닐 아크릴레이트 30 내지 50 중량부, 폴리알킬렌글리콜 10 내지 30 중량부, 트리아세틴 5 내지 25 중량부 및 황산알루미늄(Al(SO)) 1 내지 10 중량부를 포함하여; PG 등급성능이 고등급(PG 88-34, PG 94-34, PG 100-34)인 공용성 등급이고, 박층으로 포장되어도 내구성이 좋고, 소성변형, 노화 및 박리가 쉽게 발생하지 않으면서도, 침투수 및 포트홀을 방지할 수 있을 뿐만 아니라, 염해방지 및 중성화를 방지할 수 있는 박층포장용 고등급 아스팔트 콘크리트 조성물 및 이의 시공방법에 관한 것이다.
High grade asphalt concrete composition for thin overlay pavement and constructing method using the same
박층포장용 고등급 아스팔트 콘크리트 조성물 및 이의 시공방법
LIM HWAN MYUNG (Autor:in)
18.06.2020
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2023
Application Technology of Thin Asphalt Concrete Overlay on Old Pavement
| Trans Tech Publications | 2011
Construction method of pavement high-viscosity asphalt thin overlay
| Europäisches Patentamt | 2024