Ultra rapid harding concrete composition having the frost resistance and a repairing method of concrete structure using the same
The present invention relates to a rapid hardening concrete composition having excellent frost resistance, and a concrete structure repairing method using the same. According to the present invention, the rapid hardening concrete composition comprises: 10 to 60 wt% of fine aggregate; 10 to 40 wt% of coarse aggregate; 0.1 to 10 wt% of water; 5 to 25 wt% of a concrete binder including 30 to 70 parts by weight of Portland cement, 10 to 30 parts by weight of calcium sulfoaluminate, 1 to 10 parts by weight of calcium hydroxide, 0.1 to 5 parts by weight of zinc sulfate, 0.1 to 5 parts by weight of lithium carbonate, 5 to 10 parts by weight of cellulose fiber, and 5 to 20 parts by weight of ethylene vinyl acetate; and 1 to 20 wt% of a functional additive including 30 to 60 parts by weight of styrene butadiene styrene latex, 3 to 25 parts by weight of the polyfunctional compound of chemical formula 1, 20 to 50 parts by weight of polyether-modified siloxane, and 5 to 30 parts by weight of an ethylene-ethyl acrylate-maleic anhydride copolymer. Accordingly, since bubbles can be stably maintained until hardening even in a high-temperature environment, and microbubbles can be continuously maintained without coarsening of the bubbles so as to provide excellent frost resistance, and thus a repair effect can be maintained for a long time.
본 발명은 잔골재 10 내지 60 중량%, 굵은 골재 10 내지 40 중량%, 물 0.1 내지 10 중량%, 포틀랜드 시멘트 30 내지 70 중량부, 칼슘설포알루미네이트 10 내지 30 중량부, 수산화칼슘 1 내지 10 중량부, 황산아연 0.1 내지 5 중량부, 리튬카보네이트 0.1 내지 5 중량부, 셀룰로오스 섬유 5 내지 10 중량부 및 에틸렌비닐아세테이트 5 내지 20 중량부를 함유하는 콘크리트용 결합재 5 내지 25 중량%, 및 스티렌부타디엔스티렌 라텍스 30 내지 60 중량부, 하기 화학식 1의 다관능 화합물 3 내지 25 중량부, 폴리에테르 변성 실록산 20 내지 50 중량부, 에틸렌-에틸아크릴레이트-무수 말레산 공중합체 5 내지 30 중량부를 함유하는 기능성 첨가제 1 내지 20 중량%를 포함하여 이루어지는 것으로, 고온의 환경에서도 경화 시까지 안정적으로 기포가 유지되고, 기포의 조대화 없이 미세 기포가 지속적으로 유지되어 동해 저항성이 우수하므로 보수 효과가 장기간 유지될 수 있는 동해저항성이 우수한 속경형 시멘트 콘크리트 조성물 및 콘크리트 구조물 유지보수방법에 관한 것이다.
Ultra rapid harding concrete composition having the frost resistance and a repairing method of concrete structure using the same
The present invention relates to a rapid hardening concrete composition having excellent frost resistance, and a concrete structure repairing method using the same. According to the present invention, the rapid hardening concrete composition comprises: 10 to 60 wt% of fine aggregate; 10 to 40 wt% of coarse aggregate; 0.1 to 10 wt% of water; 5 to 25 wt% of a concrete binder including 30 to 70 parts by weight of Portland cement, 10 to 30 parts by weight of calcium sulfoaluminate, 1 to 10 parts by weight of calcium hydroxide, 0.1 to 5 parts by weight of zinc sulfate, 0.1 to 5 parts by weight of lithium carbonate, 5 to 10 parts by weight of cellulose fiber, and 5 to 20 parts by weight of ethylene vinyl acetate; and 1 to 20 wt% of a functional additive including 30 to 60 parts by weight of styrene butadiene styrene latex, 3 to 25 parts by weight of the polyfunctional compound of chemical formula 1, 20 to 50 parts by weight of polyether-modified siloxane, and 5 to 30 parts by weight of an ethylene-ethyl acrylate-maleic anhydride copolymer. Accordingly, since bubbles can be stably maintained until hardening even in a high-temperature environment, and microbubbles can be continuously maintained without coarsening of the bubbles so as to provide excellent frost resistance, and thus a repair effect can be maintained for a long time.
본 발명은 잔골재 10 내지 60 중량%, 굵은 골재 10 내지 40 중량%, 물 0.1 내지 10 중량%, 포틀랜드 시멘트 30 내지 70 중량부, 칼슘설포알루미네이트 10 내지 30 중량부, 수산화칼슘 1 내지 10 중량부, 황산아연 0.1 내지 5 중량부, 리튬카보네이트 0.1 내지 5 중량부, 셀룰로오스 섬유 5 내지 10 중량부 및 에틸렌비닐아세테이트 5 내지 20 중량부를 함유하는 콘크리트용 결합재 5 내지 25 중량%, 및 스티렌부타디엔스티렌 라텍스 30 내지 60 중량부, 하기 화학식 1의 다관능 화합물 3 내지 25 중량부, 폴리에테르 변성 실록산 20 내지 50 중량부, 에틸렌-에틸아크릴레이트-무수 말레산 공중합체 5 내지 30 중량부를 함유하는 기능성 첨가제 1 내지 20 중량%를 포함하여 이루어지는 것으로, 고온의 환경에서도 경화 시까지 안정적으로 기포가 유지되고, 기포의 조대화 없이 미세 기포가 지속적으로 유지되어 동해 저항성이 우수하므로 보수 효과가 장기간 유지될 수 있는 동해저항성이 우수한 속경형 시멘트 콘크리트 조성물 및 콘크리트 구조물 유지보수방법에 관한 것이다.
Ultra rapid harding concrete composition having the frost resistance and a repairing method of concrete structure using the same
동해저항성이 우수한 속경형 시멘트 콘크리트 조성물 및 콘크리트 구조물 유지보수방법
YOO SE KYUN (Autor:in)
22.03.2021
Patent
Elektronische Ressource
Koreanisch
ECO-FRIENDLY AND ULTRA-RAPID-HARDING CONSTRUCTION METHOD FOR REPAIRING CONCRETE STRUCTURE