The present invention relates to precast autoclave cured lightweight foamed concrete containing loess and a method for preparing the same. The method for preparing precast autoclave cured lightweight foamed concrete containing loess comprises the steps of: preparing a primary mixture by mixing Portland cement, fine silica powder, fine loess powder, and meta kaolin with water; preparing a secondary mixture by mixing slaked lime, gypsum and alumina cement with water; preparing a tertiary mixture by mixing the first mixture with the secondary mixture; adding bubbles generated by a foaming agent in a bubbler to the tertiary mixture; pouring the tertiary mixture into which the bubbles are added into a mold and primarily curing the mold at a temperature of 22 to 28℃ for three to five hours; demolding the primary cured product and secondarily curing the primary cured product at a temperature of 35 to 45℃ for six to eight hours; and tertiary curing the secondary cured product in an autoclave at a temperature of 170 to 190℃ for six to eight hours. The precast autoclave cured lightweight foamed concrete containing loess comprises: 30 to 45 wt% of the Portland cement; 30 to 45 wt% of the fine silica powder; 5 to 15 wt% of the fine loess powder; 2 to 5 wt% of meta kaolin; 2 to 5 wt% of the slaked lime; 2 to 6 wt% of the gypsum; 3 to 9 wt% of the alumina cement; and the foaming agent of 0.5 to 1.0 wt%. According to the present invention, the precast autoclave cured lightweight foamed concrete containing loess and the method for preparing the same have advantages of: shortening a construction period; reducing construction costs; making it easy to facilitate the quality management; enhancing durability; providing eco-friendly performance by the inclusion of loess, thereby protecting users against a harmful environment; and reducing manufacturing costs by the use of inexpensive fine loess powder.

본 발명은 포틀랜드 시멘트, 규사미분말, 황토미분말 및 메타 카올린을 물과 혼합하여 1차 혼합물을 제조하는 단계; 소석회, 석고 및 알루미나 시멘트를 물과 혼합하여 2차 혼합물을 제조하는 단계; 상기 1차 혼합물과 상기 2차 혼합물을 혼합하여 3차 혼합물을 제조하는 단계; 상기 3차 혼합물에 기포기에서 기포제에 의해 발생된 기포를 투입하는 단계; 상기 기포가 투입된 3차 혼합물을 몰드에 타설하여 22~28℃에서 3~5 시간 동안 1차 양생하는 단계; 상기 몰드를 탈형하고, 1차 양생물을 35~45℃에서 6~8 시간 동안 2차 양생하는 단계; 및 상기 2차 양생물을 오토클레이브에서 170~190℃에서 6~8 시간 동안 3차 양생하는 단계;를 포함하고, 상기 포틀랜드 시멘트가 30 ~ 45 wt%이고, 상기 규사미분말이 30 ~ 45 wt%이고, 상기 황토미분말이 5 ~ 15 wt%이고, 상기 메타 카올린이 2 ~ 5 wt%이고, 상기 소석회가 2 ~ 5 wt%이고, 상기 석고가 2 ~ 6 wt%이고, 상기 알루미나 시멘트가 3 ~ 9 wt%이고, 상기 기포제가 0.5 ~ 1.0 wt%인, 황토 함유 프리캐스트 오토클레이브 양생 경량 기포콘크리트 및 이의 제조방법에 관한 것이다. 본 발명에 따르면, 공기의 단축, 공사비의 절감, 품질 관리의 용이, 내구성 증대 등의 장점을 가질 수 있고, 황토 함유 등으로 인해 사용자를 유해한 환경으로부터 보호하도록 친환경성을 제공하고, 저렴한 황토미분말 등의 사용으로 인해 제조 단가를 절감하도록 한다.