HIGH FUNCTIONAL MORTAR COMPOSITION FOR REPAIRING-REINFORCING CONCRETE STRUCTURE HAVING EXCELLENT UNDERWATER-CURING PROPERTY AND HIGH DURABILITY AND METHOD FOR REPAIRING-REINFORCING CONCRETE STRUCTURE USING THE SAME
The present invention relates to a high-functional mortar composition for repair and reinforcement of a concrete structure having excellent underwater hardening performance and high durability, and to a method for repair and reinforcement of a concrete structure using the same. The composition comprises 5 to 75 wt% of a performance improving material, 5 to 90 wt% of fine aggregate, and 1 to 35 wt% of water. The performance improving material comprises: 20 to 70 wt% of normal Portland cement; 5 to 40 wt% of blast furnace slag; 5 to 35 wt% of calcium sulfoaluminate; 1 to 15 wt% of cenosphere; 1 to 15 wt% of gelite; 1 to 15 wt% of diatomaceous earth; 0.1 to 10 wt% of charcoal powder; 0.1 to 10 wt% of magnesium silicate fluoride; 0.01 to 5 wt% of Sargassum fulvellum powder; 0.01 to 5 wt% of an ethylene-vinyl acetate copolymer; 0.01 to 5 wt% of a methyl methacrylate-butyl acrylate copolymer; 0.01 to 5 wt% of polyacrylamide; 0.01 to 5 wt% of a styrene-acrylic ester copolymer; and 0.01 to 5 wt% of starch-hydroxymethyl cellulose. The Sargassum fulvellum powder is obtained by mixing, at a weight ratio of 1 : 1 to 3, dry powder of Sargassum fulvellum powdered after being dried, and fiber powder of Sargassum fulvellum powdered after removing agar from Sargassum fulvellum and making the same into fibers. The high-functional mortar composition can express very high strength even in water or in poor wet conditions, and provide very good durability.
본 발명은 우수한 수중경화성능 및 고내구성을 갖는 콘크리트 구조물의 보수보강용 고기능성 모르타르 조성물에 관한 것으로서, 성능개선재 5 내지 75 중량%, 잔골재 5 내지 90 중량% 및 물 1 내지 35 중량%를 포함하고; 상기 성능개선재는 보통 포틀랜드 시멘트 20 내지 70 중량%, 고로슬래그 5 내지 40 중량%, 칼슘설포알루미네이트 5 내지 35 중량%, 세노스페어 1 내지 15 중량%, 겔라이트 1 내지 15 중량%, 규조토 1 내지 15 중량%, 숯분말 0.1 내지 10 중량%, 규불화마그네슘 0.1 내지 10 중량%, 모자반 분말 0.01 내지 5 중량%, 에틸렌-초산 비닐 공중합체 0.01 내지 5 중량%, 메틸메타크릴레이트-부틸아크릴레이트 공중합체 0.01 내지 5 중량%, 폴리아크릴아마이드 0.01 내지 5 중량%, 스티렌-아크릴 에스테르 공중합체 0.01 내지 5 중량% 및 스타치-히드록시메틸셀룰로오스 0.01 내지 5 중량%를 포함하는 것이고; 상기 모자반 분말은 모자반을 건조한 후 분말화한 모자반의 건조분말: 및 모자반의 한천을 제거하여 섬유화시킨 후 분말화한 모자반의 섬유분말을 1: 1 내지 3 중량비율로 혼합한 것을 사용하여; 수중이나 열악한 습윤상태에서도 매우 높은 강도를 발현할 수 있고, 매우 우수한 내구성을 제공할 수 있는 우수한 수중경화성능 및 고내구성을 갖는 콘크리트 구조물의 보수보강용 고기능성 모르타르 조성물 및 이를 이용한 콘크리트 구조물의 보수보강 시공방법에 관한 것이다.
HIGH FUNCTIONAL MORTAR COMPOSITION FOR REPAIRING-REINFORCING CONCRETE STRUCTURE HAVING EXCELLENT UNDERWATER-CURING PROPERTY AND HIGH DURABILITY AND METHOD FOR REPAIRING-REINFORCING CONCRETE STRUCTURE USING THE SAME
The present invention relates to a high-functional mortar composition for repair and reinforcement of a concrete structure having excellent underwater hardening performance and high durability, and to a method for repair and reinforcement of a concrete structure using the same. The composition comprises 5 to 75 wt% of a performance improving material, 5 to 90 wt% of fine aggregate, and 1 to 35 wt% of water. The performance improving material comprises: 20 to 70 wt% of normal Portland cement; 5 to 40 wt% of blast furnace slag; 5 to 35 wt% of calcium sulfoaluminate; 1 to 15 wt% of cenosphere; 1 to 15 wt% of gelite; 1 to 15 wt% of diatomaceous earth; 0.1 to 10 wt% of charcoal powder; 0.1 to 10 wt% of magnesium silicate fluoride; 0.01 to 5 wt% of Sargassum fulvellum powder; 0.01 to 5 wt% of an ethylene-vinyl acetate copolymer; 0.01 to 5 wt% of a methyl methacrylate-butyl acrylate copolymer; 0.01 to 5 wt% of polyacrylamide; 0.01 to 5 wt% of a styrene-acrylic ester copolymer; and 0.01 to 5 wt% of starch-hydroxymethyl cellulose. The Sargassum fulvellum powder is obtained by mixing, at a weight ratio of 1 : 1 to 3, dry powder of Sargassum fulvellum powdered after being dried, and fiber powder of Sargassum fulvellum powdered after removing agar from Sargassum fulvellum and making the same into fibers. The high-functional mortar composition can express very high strength even in water or in poor wet conditions, and provide very good durability.
본 발명은 우수한 수중경화성능 및 고내구성을 갖는 콘크리트 구조물의 보수보강용 고기능성 모르타르 조성물에 관한 것으로서, 성능개선재 5 내지 75 중량%, 잔골재 5 내지 90 중량% 및 물 1 내지 35 중량%를 포함하고; 상기 성능개선재는 보통 포틀랜드 시멘트 20 내지 70 중량%, 고로슬래그 5 내지 40 중량%, 칼슘설포알루미네이트 5 내지 35 중량%, 세노스페어 1 내지 15 중량%, 겔라이트 1 내지 15 중량%, 규조토 1 내지 15 중량%, 숯분말 0.1 내지 10 중량%, 규불화마그네슘 0.1 내지 10 중량%, 모자반 분말 0.01 내지 5 중량%, 에틸렌-초산 비닐 공중합체 0.01 내지 5 중량%, 메틸메타크릴레이트-부틸아크릴레이트 공중합체 0.01 내지 5 중량%, 폴리아크릴아마이드 0.01 내지 5 중량%, 스티렌-아크릴 에스테르 공중합체 0.01 내지 5 중량% 및 스타치-히드록시메틸셀룰로오스 0.01 내지 5 중량%를 포함하는 것이고; 상기 모자반 분말은 모자반을 건조한 후 분말화한 모자반의 건조분말: 및 모자반의 한천을 제거하여 섬유화시킨 후 분말화한 모자반의 섬유분말을 1: 1 내지 3 중량비율로 혼합한 것을 사용하여; 수중이나 열악한 습윤상태에서도 매우 높은 강도를 발현할 수 있고, 매우 우수한 내구성을 제공할 수 있는 우수한 수중경화성능 및 고내구성을 갖는 콘크리트 구조물의 보수보강용 고기능성 모르타르 조성물 및 이를 이용한 콘크리트 구조물의 보수보강 시공방법에 관한 것이다.
HIGH FUNCTIONAL MORTAR COMPOSITION FOR REPAIRING-REINFORCING CONCRETE STRUCTURE HAVING EXCELLENT UNDERWATER-CURING PROPERTY AND HIGH DURABILITY AND METHOD FOR REPAIRING-REINFORCING CONCRETE STRUCTURE USING THE SAME
우수한 수중경화성능 및 고내구성을 갖는 콘크리트 구조물의 보수보강용 고기능성 모르타르 조성물 및 이를 이용한 콘크리트 구조물의 보수보강 시공방법
KIM YOUNG WOON (Autor:in)
27.05.2021
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2019
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2018