LATEX MODIFIED UTRA HIGH EARLY STRENGTH CEMENT CONCRETE COMPOSITION WITH LIQUID SULFUR HAVING EXCELLENT CRACK RESISTANCE AND REPAIRING METHOD FOR ROAD PAVEMENT THEREWITH
The present invention is a latex-modified ultra-high-early-strength cement concrete composition containing liquid sulfur which comprises an ultra-high-early-strength binder, fine aggregate, coarse aggregate, mixing water, and a latex modifier containing liquid sulfur. The ultra-high-early-strength binder comprises early-strength Portland cement, calcium sulfoaluminate, anhydrite, sodium sulfate, lithium metaphosphate, seaweed fiber, and zinc oxide. The latex modifier containing liquid sulfur comprises vinyl chloride-vinyl acetate copolymer, acrylonitrile-butadiene-styrene copolymer, styrene-butadiene-styrene (SBS) copolymer, liquid sulfur, N-isopropyl acrylamide and cyanoacrylate ester. The liquid sulfur is prepared by mixing sulfur generated in a refining process of crude oil with dicyclopentadiene acrylate monomer represented by chemical formula 1, isosorbide, sodium hydroxide, calcium hydroxide, and water and making reaction thereof. In chemical formula 1, R1 is H or a linear or branched C1 to C4 alkyl group, and n is an integer from 0 to 5.
본 발명은 균열저감효과가 뛰어난 액상유황 함유 라텍스 개질 초조강형 시멘트 콘크리트 조성물로서, 초조강형 결합재 10 내지 40 중량%, 잔골재 10 내지 50 중량%, 굵은골재 5 내지 40 중량%, 배합수 0.1 내지 10 중량% 및 액상유황 함유 라텍스 개질제 0.1 내지 10 중량%를 포함하고; 상기 초조강형 결합재는 조강 포틀랜드 시멘트 100 중량부에 대하여, 칼슘설포알루미네이트 20 내지 40 중량부, 무수석고 10 내지 30 중량부, 황산나트륨 1 내지 10 중량부, 메타인산리튬 1 내지 10 중량부, 해조류 섬유 0.1 내지 5 중량부 및 산화아연 0.1 내지 5 중량부를 포함하는 것이고; 상기 액상유황 함유 라텍스 개질제는 염화비닐-초산비닐 공중합체 100 중량부에 대하여, 아크릴로니트릴-부타디엔-스티렌 공중합체 40 내지 60 중량부, 스티렌-부타디엔-스티렌(SBS) 공중합체 1 내지 10 중량부, 액상유황 1 내지 10 중량부, N-이소프로필아크릴아마이드 0.1 내지 5 중량부 및 시아노아크릴 에스테르 0.1 내지 5 중량부를 포함하는 것이고; 상기 액상유황은 원유의 정유 공정에서 발생된 유황 100 중량부에, 하기 화학식 1로 표시되는 아크릴화 디시클로펜타디엔 모노머 1 내지 10 중량부, 아이소소바이드 0.5 내지 3 중량부, 수산화나트륨 45 내지 65 중량부, 수산화칼슘 30 내지 50 중량부 및 물 150 내지 250 중량부를 혼합하고, 150 내지 220℃ 및 2 내지 3기압에서 반응시켜 제조되는 것을 사용함으로써; 원유정제시 발생되는 유황을 활용하여 균열저감효과가 매우 개선될 뿐만 아니라, 내화학성, 동결융해 및 염해에 대한 내성이 매우 개선되어 구조물의 내구수명을 연장할 수 있는 균열저감효과가 뛰어난 액상유황 함유 라텍스 개질 초조강형 시멘트 콘크리트 조성물 및 이를 이용한 도로포장 보수 시공방법에 관한 것이다. [화학식 1] JPEG112021500348591-pat00007.jpg2184 상기 식에서, R1은 H 또는 선형 또는 분지된 C1 내지 C4의 알킬기이고, n은 0 내지 5의 정수이다.
LATEX MODIFIED UTRA HIGH EARLY STRENGTH CEMENT CONCRETE COMPOSITION WITH LIQUID SULFUR HAVING EXCELLENT CRACK RESISTANCE AND REPAIRING METHOD FOR ROAD PAVEMENT THEREWITH
The present invention is a latex-modified ultra-high-early-strength cement concrete composition containing liquid sulfur which comprises an ultra-high-early-strength binder, fine aggregate, coarse aggregate, mixing water, and a latex modifier containing liquid sulfur. The ultra-high-early-strength binder comprises early-strength Portland cement, calcium sulfoaluminate, anhydrite, sodium sulfate, lithium metaphosphate, seaweed fiber, and zinc oxide. The latex modifier containing liquid sulfur comprises vinyl chloride-vinyl acetate copolymer, acrylonitrile-butadiene-styrene copolymer, styrene-butadiene-styrene (SBS) copolymer, liquid sulfur, N-isopropyl acrylamide and cyanoacrylate ester. The liquid sulfur is prepared by mixing sulfur generated in a refining process of crude oil with dicyclopentadiene acrylate monomer represented by chemical formula 1, isosorbide, sodium hydroxide, calcium hydroxide, and water and making reaction thereof. In chemical formula 1, R1 is H or a linear or branched C1 to C4 alkyl group, and n is an integer from 0 to 5.
본 발명은 균열저감효과가 뛰어난 액상유황 함유 라텍스 개질 초조강형 시멘트 콘크리트 조성물로서, 초조강형 결합재 10 내지 40 중량%, 잔골재 10 내지 50 중량%, 굵은골재 5 내지 40 중량%, 배합수 0.1 내지 10 중량% 및 액상유황 함유 라텍스 개질제 0.1 내지 10 중량%를 포함하고; 상기 초조강형 결합재는 조강 포틀랜드 시멘트 100 중량부에 대하여, 칼슘설포알루미네이트 20 내지 40 중량부, 무수석고 10 내지 30 중량부, 황산나트륨 1 내지 10 중량부, 메타인산리튬 1 내지 10 중량부, 해조류 섬유 0.1 내지 5 중량부 및 산화아연 0.1 내지 5 중량부를 포함하는 것이고; 상기 액상유황 함유 라텍스 개질제는 염화비닐-초산비닐 공중합체 100 중량부에 대하여, 아크릴로니트릴-부타디엔-스티렌 공중합체 40 내지 60 중량부, 스티렌-부타디엔-스티렌(SBS) 공중합체 1 내지 10 중량부, 액상유황 1 내지 10 중량부, N-이소프로필아크릴아마이드 0.1 내지 5 중량부 및 시아노아크릴 에스테르 0.1 내지 5 중량부를 포함하는 것이고; 상기 액상유황은 원유의 정유 공정에서 발생된 유황 100 중량부에, 하기 화학식 1로 표시되는 아크릴화 디시클로펜타디엔 모노머 1 내지 10 중량부, 아이소소바이드 0.5 내지 3 중량부, 수산화나트륨 45 내지 65 중량부, 수산화칼슘 30 내지 50 중량부 및 물 150 내지 250 중량부를 혼합하고, 150 내지 220℃ 및 2 내지 3기압에서 반응시켜 제조되는 것을 사용함으로써; 원유정제시 발생되는 유황을 활용하여 균열저감효과가 매우 개선될 뿐만 아니라, 내화학성, 동결융해 및 염해에 대한 내성이 매우 개선되어 구조물의 내구수명을 연장할 수 있는 균열저감효과가 뛰어난 액상유황 함유 라텍스 개질 초조강형 시멘트 콘크리트 조성물 및 이를 이용한 도로포장 보수 시공방법에 관한 것이다. [화학식 1] JPEG112021500348591-pat00007.jpg2184 상기 식에서, R1은 H 또는 선형 또는 분지된 C1 내지 C4의 알킬기이고, n은 0 내지 5의 정수이다.
LATEX MODIFIED UTRA HIGH EARLY STRENGTH CEMENT CONCRETE COMPOSITION WITH LIQUID SULFUR HAVING EXCELLENT CRACK RESISTANCE AND REPAIRING METHOD FOR ROAD PAVEMENT THEREWITH
균열저감효과가 뛰어난 액상유황 함유 라텍스 개질 초조강형 시멘트 콘크리트 조성물 및 이를 이용한 도로포장 보수 시공방법
SONG JI YEON (Autor:in)
23.07.2021
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2018
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2021