Self-healing Admixture Composition Manufacturing Method of the Admixture Mortar Composition Using the Admixture and Concrete Repair Method Using the Mortar
The present invention relates to a new crack-control self-healing mortar capable of crack reduction and crack healing and relates to a new self-healing admixture composition using mag carbon, a preferred method for manufacturing the same, mortar preferably using the same and a self-healing cross-section repair method using the same. The Crack control self-healing admixture composition of the present invention comprises: 30 - 84 wt% of mag carbon (MgO-C), 5.0 - 35wt% of a carbonate accelerator, 10 - 35 wt% of smectite clay mineral, and 1.0 - 5.0 wt% of an organic acid additive. The self-healing admixture of this composition is mixed and pulverized by MC reaction treatment of mag carbon, the carbonate accelerator, and smectite clay mineral at 100 - 200 rpm for 3 - 7 hrs of a holding time, wherein when the internal temperature of the MC reaction treatment equipment rises to 35℃ or higher during the MC reaction treatment, it can be preferable that an organic acid additive is added to continue the MC reaction treatment, thereby manufacturing the self-healing admixture. The self-healing admixture prepared in this way is mixed with 1 to 10 parts by weight of the self-healing mortar based on 100 parts by weight of a cement-based binder and then applied to a concrete cross-section repairing method when a portion in a concrete structure, where a degraded portion is removed is repaired.
본 발명은 균열저감과 균열치유가 가능한 새로운 균열제어 자기치유 모르타르에 관한 것으로, 마그카본을 이용한 새로운 조성의 자기치유 혼화재 조성물과 그 자기치유 혼화재의 바람직한 제조방법, 그리고 그 자기치유 혼화재를 바람직하게 이용한 모르타르와 자기치유 단면보수 공법에 관한 것이다. 본 발명에 따른 균열제어 자기치유 혼화재 조성물은, 마그카본(MgO-C) 30~84중량%, 탄산염 촉진제 5.0~35중량%, 스멕타이트 점토광물 10~35중량%, 유기산 첨가제 1.0~5.0중량%를 포함하여 조성되는 것을 특징으로 한다. 이러한 조성의 자기치유 혼화재는, 마그카본, 탄산염 촉진제, 스멕타이트 점토광물을 rpm 100~200, 유지시간 3~7hr 조건으로 MC반응 처리하여 혼합 분쇄하되 MC반응 처리 중에 MC반응처리장비 내부 온도가 35℃ 이상으로 상승하면 유기산 첨가제를 투입하여 MC반응 처리를 지속하는 방식으로 바람직하게 제조할 수 있다. 이렇게 제조한 자기치유 혼화재는 시멘트계 결합재 100중량부에 1~10중량부 치환 혼입하는 방법으로 자기치유 모르타르를 배합한 후, 콘크리트 구조물에서 열화부분이 제거된 부분에 시공하는 방식으로 콘크리트 단면보수공법에 적용할 수 있다.
Self-healing Admixture Composition Manufacturing Method of the Admixture Mortar Composition Using the Admixture and Concrete Repair Method Using the Mortar
The present invention relates to a new crack-control self-healing mortar capable of crack reduction and crack healing and relates to a new self-healing admixture composition using mag carbon, a preferred method for manufacturing the same, mortar preferably using the same and a self-healing cross-section repair method using the same. The Crack control self-healing admixture composition of the present invention comprises: 30 - 84 wt% of mag carbon (MgO-C), 5.0 - 35wt% of a carbonate accelerator, 10 - 35 wt% of smectite clay mineral, and 1.0 - 5.0 wt% of an organic acid additive. The self-healing admixture of this composition is mixed and pulverized by MC reaction treatment of mag carbon, the carbonate accelerator, and smectite clay mineral at 100 - 200 rpm for 3 - 7 hrs of a holding time, wherein when the internal temperature of the MC reaction treatment equipment rises to 35℃ or higher during the MC reaction treatment, it can be preferable that an organic acid additive is added to continue the MC reaction treatment, thereby manufacturing the self-healing admixture. The self-healing admixture prepared in this way is mixed with 1 to 10 parts by weight of the self-healing mortar based on 100 parts by weight of a cement-based binder and then applied to a concrete cross-section repairing method when a portion in a concrete structure, where a degraded portion is removed is repaired.
본 발명은 균열저감과 균열치유가 가능한 새로운 균열제어 자기치유 모르타르에 관한 것으로, 마그카본을 이용한 새로운 조성의 자기치유 혼화재 조성물과 그 자기치유 혼화재의 바람직한 제조방법, 그리고 그 자기치유 혼화재를 바람직하게 이용한 모르타르와 자기치유 단면보수 공법에 관한 것이다. 본 발명에 따른 균열제어 자기치유 혼화재 조성물은, 마그카본(MgO-C) 30~84중량%, 탄산염 촉진제 5.0~35중량%, 스멕타이트 점토광물 10~35중량%, 유기산 첨가제 1.0~5.0중량%를 포함하여 조성되는 것을 특징으로 한다. 이러한 조성의 자기치유 혼화재는, 마그카본, 탄산염 촉진제, 스멕타이트 점토광물을 rpm 100~200, 유지시간 3~7hr 조건으로 MC반응 처리하여 혼합 분쇄하되 MC반응 처리 중에 MC반응처리장비 내부 온도가 35℃ 이상으로 상승하면 유기산 첨가제를 투입하여 MC반응 처리를 지속하는 방식으로 바람직하게 제조할 수 있다. 이렇게 제조한 자기치유 혼화재는 시멘트계 결합재 100중량부에 1~10중량부 치환 혼입하는 방법으로 자기치유 모르타르를 배합한 후, 콘크리트 구조물에서 열화부분이 제거된 부분에 시공하는 방식으로 콘크리트 단면보수공법에 적용할 수 있다.
Self-healing Admixture Composition Manufacturing Method of the Admixture Mortar Composition Using the Admixture and Concrete Repair Method Using the Mortar
균열제어 자기치유 혼화재 조성물과 그 혼화재의 제조방법, 그리고 자기치유 모르타르 조성물과 이를 이용한 콘크리트 구조물의 단면보수공법
PARK DONG CHEOL (Autor:in) / LEE JUNG WOO (Autor:in) / KWON HYUK (Autor:in) / HWANG MOO YEON (Autor:in) / KIM TAE HYUNG (Autor:in)
16.08.2022
Patent
Elektronische Ressource
Koreanisch
Europäisches Patentamt | 2021
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2023