HIGH STRENGTH QUICK-HARDENING CEMENT CONCRETE COMPOSITION MODIFIED BY CONCRETE ADMIXTURE AND REPAIRING METHOD FOR CONCRETE PAVEMENT USING THE SAME
The present invention is to provide a high-strength and ultra-rapid-hardening concrete composition modified with a concrete admixture and a concrete pavement repair method using the same. The high-strength and ultra-rapid-hardening concrete composition comprises 20 to 50 wt% of fine aggregate, 10 to 40 wt % of coarse aggregate, 10 to 40 wt % of a functional improvement binder, 0.5 to 20 wt % of a functional improvement admixture, and 0.1 to 5 wt % of water. The functional improvement binder includes 100 parts by weight of early-strength Portland cement, 20 to 40 parts by weight of calcium sulfoaluminate, 20 to 40 parts by weight of ferronickel slag, 1 to 20 parts by weight of potassium magnesium titanate, 1 to 20 parts by weight of blast furnace slag fine powder, 0.1 to 10 parts by weight of spicule, and 0.1 to 10 parts by weight of clinochlore. The functional improvement admixture includes 100 parts by weight of acrylic latex, 70 to 90 parts by weight of an acrylonitrile-butadiene-styrene copolymer, 10 to 30 parts by weight of a polyamide imide resin, 10 to 30 parts by weight of hydroxy fluorene (meth)acrylate, 10 to 30 parts by weight of styrene-maleimide copolymer, 0.1 to 10 parts by weight of thiophosphate ester, 0.1 to 10 parts by weight of luteolinidin glycoside, and 0.1 to 10 parts by weight of trehalose. Therefore, the present invention has a rapid hardening speed and thus can quickly restore a damaged part of a concrete road, and at the same time, can improve strength such as adhesion strength, bending strength, tensile strength, and compressive strength. In addition, the present invention can ensure durability such as waterproofness, corrosion resistance, abrasion resistance, and chemical resistance, and can provide durability such as salt permeation resistance, freeze-thaw resistance, and abrasion resistance.
본 발명은 잔골재 20 내지 50 중량%, 굵은 골재 10 내지 40 중량%, 기능개선 결합재 10 내지 40 중량%, 기능개선 혼화제 0.5 내지 20 중량% 및 물 0.1 내지 5 중량%를 포함하고; 상기 기능개선 결합재는 조강 포틀랜드 시멘트 100 중량부, 칼슘설포알루미네이트 20 내지 40 중량부, 페로니켈 슬래그 20 내지 40 중량부, 티탄산칼륨마그네슘 1 내지 20 중량부, 고로슬래그 미분말 1 내지 20 중량부, 스피큘 0.1 내지 10 중량부 및 클리노클로레 0.1 내지 10 중량부를 포함하는 것이고; 상기 기능개선 혼화제는 아크릴 라텍스 100 중량부, 아크릴로니트릴-부타디엔-스티렌 공중합체 70 내지 90 중량부, 폴리아미드이미드수지 10 내지 30 중량부, 하이드록시불소(메타)아크릴레이트 10 내지 30 중량부, 스티렌-말레이미드 공중합체 10 내지 30 중량부, 티오인산에스테르 0.1 내지 10 중량부, 루테올리니딘 글리코시드 0.1 내지 10 중량부, 및 트레할로오스 0.1 내지 10 중량부를 포함하는 것을 사용함으로써, 경화속도가 빨라 신속하게 콘크리트 도로의 파손부위를 복구할 수 있으며 동시에 부착강도, 휨강도, 인장강도 및 압축강도 등의 강도를 향상시킬 수 있고 방수성, 내식성, 내마모성, 내화학성 등의 내구성 확보가 가능하며 염분침투저항성, 동결융해저항성 및 마모저항성 등의 내구성을 제공할 수 있는 콘크리트 혼화제로 개질된 고강도 초속경 콘크리트 조성물 및 이를 이용한 콘크리트 포장 보수공법에 관한 것이다.
HIGH STRENGTH QUICK-HARDENING CEMENT CONCRETE COMPOSITION MODIFIED BY CONCRETE ADMIXTURE AND REPAIRING METHOD FOR CONCRETE PAVEMENT USING THE SAME
The present invention is to provide a high-strength and ultra-rapid-hardening concrete composition modified with a concrete admixture and a concrete pavement repair method using the same. The high-strength and ultra-rapid-hardening concrete composition comprises 20 to 50 wt% of fine aggregate, 10 to 40 wt % of coarse aggregate, 10 to 40 wt % of a functional improvement binder, 0.5 to 20 wt % of a functional improvement admixture, and 0.1 to 5 wt % of water. The functional improvement binder includes 100 parts by weight of early-strength Portland cement, 20 to 40 parts by weight of calcium sulfoaluminate, 20 to 40 parts by weight of ferronickel slag, 1 to 20 parts by weight of potassium magnesium titanate, 1 to 20 parts by weight of blast furnace slag fine powder, 0.1 to 10 parts by weight of spicule, and 0.1 to 10 parts by weight of clinochlore. The functional improvement admixture includes 100 parts by weight of acrylic latex, 70 to 90 parts by weight of an acrylonitrile-butadiene-styrene copolymer, 10 to 30 parts by weight of a polyamide imide resin, 10 to 30 parts by weight of hydroxy fluorene (meth)acrylate, 10 to 30 parts by weight of styrene-maleimide copolymer, 0.1 to 10 parts by weight of thiophosphate ester, 0.1 to 10 parts by weight of luteolinidin glycoside, and 0.1 to 10 parts by weight of trehalose. Therefore, the present invention has a rapid hardening speed and thus can quickly restore a damaged part of a concrete road, and at the same time, can improve strength such as adhesion strength, bending strength, tensile strength, and compressive strength. In addition, the present invention can ensure durability such as waterproofness, corrosion resistance, abrasion resistance, and chemical resistance, and can provide durability such as salt permeation resistance, freeze-thaw resistance, and abrasion resistance.
본 발명은 잔골재 20 내지 50 중량%, 굵은 골재 10 내지 40 중량%, 기능개선 결합재 10 내지 40 중량%, 기능개선 혼화제 0.5 내지 20 중량% 및 물 0.1 내지 5 중량%를 포함하고; 상기 기능개선 결합재는 조강 포틀랜드 시멘트 100 중량부, 칼슘설포알루미네이트 20 내지 40 중량부, 페로니켈 슬래그 20 내지 40 중량부, 티탄산칼륨마그네슘 1 내지 20 중량부, 고로슬래그 미분말 1 내지 20 중량부, 스피큘 0.1 내지 10 중량부 및 클리노클로레 0.1 내지 10 중량부를 포함하는 것이고; 상기 기능개선 혼화제는 아크릴 라텍스 100 중량부, 아크릴로니트릴-부타디엔-스티렌 공중합체 70 내지 90 중량부, 폴리아미드이미드수지 10 내지 30 중량부, 하이드록시불소(메타)아크릴레이트 10 내지 30 중량부, 스티렌-말레이미드 공중합체 10 내지 30 중량부, 티오인산에스테르 0.1 내지 10 중량부, 루테올리니딘 글리코시드 0.1 내지 10 중량부, 및 트레할로오스 0.1 내지 10 중량부를 포함하는 것을 사용함으로써, 경화속도가 빨라 신속하게 콘크리트 도로의 파손부위를 복구할 수 있으며 동시에 부착강도, 휨강도, 인장강도 및 압축강도 등의 강도를 향상시킬 수 있고 방수성, 내식성, 내마모성, 내화학성 등의 내구성 확보가 가능하며 염분침투저항성, 동결융해저항성 및 마모저항성 등의 내구성을 제공할 수 있는 콘크리트 혼화제로 개질된 고강도 초속경 콘크리트 조성물 및 이를 이용한 콘크리트 포장 보수공법에 관한 것이다.
HIGH STRENGTH QUICK-HARDENING CEMENT CONCRETE COMPOSITION MODIFIED BY CONCRETE ADMIXTURE AND REPAIRING METHOD FOR CONCRETE PAVEMENT USING THE SAME
콘크리트 혼화제로 개질된 고강도 초속경 콘크리트 조성물 및 이를 이용한 콘크리트 포장 보수공법
JUNG SEUNG HO (Autor:in)
28.10.2022
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
QUICK-HARDENING CEMENT CONCRETE COMPOSITION AND REPAIRING METHOD FOR ROAD PAVEMENT THEREWITH
| Europäisches Patentamt | 2018
| Europäisches Patentamt | 2022
Quick-hardening concrete composite and repairing method for concrete pavement using the same
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2024
Quick repairing method of old cement concrete pavement
| Europäisches Patentamt | 2015