METHOD FOR MANUFACTURING OF GROUND ORGANIC MONOLITH PARTICLES AND THE GROUND ORGANIC MONOLITH PARTICLES THEREBY
The present invention relates to organic monolith powder and a preparation method thereof. More specifically, the method includes the steps of: preparing a mixed solution by mixing a functional monomer, a crosslinking monomer, and a solvent and removing the oxygen in the mixed solution (step 1); mixing a pore inducer having the molecular weight of 20 to 1,000 thousands and a polymerization initiator in the mixed solution to initiate a polymerization reaction (step 2); and separating the organic monolith in the mixed solution having the polymerization reaction in the step 2. According to the present invention, the organic monolith powder preparation method uses the pore inducer having the molecular weight of 20 to 1,000 thousands to form the mezzo-sized pores and total pore volume of the mezzo-size. The present invention can increase the material transfer rate by forming the macro pores fitted near the monolit surface instead of the inside of the macro pores, obtains the most densely filled structure, increases the charging efficiency by using the monolit shape to increase the flow rate and power of the charging liquid, thereby obtaining the high separation efficiency similar to that of C18-bonded 5 μm silica when the chromatography is used in the stationary phase.
본 발명은 유기 모노리트 분말의 제조방법 및 이에 따라 제조되는 유기 모노리트 분말에 관한 것으로, 구체적으로는 기능성 모노머 및 가교 모노머와 용매를 혼합하여 혼합용액을 제조하고, 혼합용액 내의 산소를 제거하는 단계(단계 1); 상기 혼합용액에 2만 내지 100만의 분자량을 갖는 기공유도물질 및 중합개시제를 혼합한 후, 중합반응을 진행하는 단계(단계 2); 및 상기 단계 2에서 중합반응이 수행된 혼합용액에서 유기 모노리트를 분리하는 단계(단계 3);를 포함하는 유기 모노리트 분말의 제조방법에 관한 것이다. 본 발명에 따른 유기 모노리트 분말의 제조방법은 2만 내지 100만의 분자량을 갖는 기공유도물질을 사용함으로써, 메조크기의 기공은 거의 없으며 매크로크기의 총 기공 부피가 큰 유기 모노리트 분말을 제조할 수 있다. 이때, 매크로 기공이 내부에는 존재하지 않으면서 모노리트 표면 부근에 박혀있는 형태로 존재하므로 물질 전달속도가 빠르고, 모노리트 형태로 인하여 충전 용매의 흐름이 빠르고 힘이 있어서 충전효율이 좋아지고 최대한 조밀한 충전 구조를 얻을 수 있으므로, 크로마토그래피 정지상으로 사용할 때, C18부착 5 ㎛ 실리카 분말의 분리효율과 유사한 우수한 분리효율을 얻을 수 있다.
METHOD FOR MANUFACTURING OF GROUND ORGANIC MONOLITH PARTICLES AND THE GROUND ORGANIC MONOLITH PARTICLES THEREBY
The present invention relates to organic monolith powder and a preparation method thereof. More specifically, the method includes the steps of: preparing a mixed solution by mixing a functional monomer, a crosslinking monomer, and a solvent and removing the oxygen in the mixed solution (step 1); mixing a pore inducer having the molecular weight of 20 to 1,000 thousands and a polymerization initiator in the mixed solution to initiate a polymerization reaction (step 2); and separating the organic monolith in the mixed solution having the polymerization reaction in the step 2. According to the present invention, the organic monolith powder preparation method uses the pore inducer having the molecular weight of 20 to 1,000 thousands to form the mezzo-sized pores and total pore volume of the mezzo-size. The present invention can increase the material transfer rate by forming the macro pores fitted near the monolit surface instead of the inside of the macro pores, obtains the most densely filled structure, increases the charging efficiency by using the monolit shape to increase the flow rate and power of the charging liquid, thereby obtaining the high separation efficiency similar to that of C18-bonded 5 μm silica when the chromatography is used in the stationary phase.
본 발명은 유기 모노리트 분말의 제조방법 및 이에 따라 제조되는 유기 모노리트 분말에 관한 것으로, 구체적으로는 기능성 모노머 및 가교 모노머와 용매를 혼합하여 혼합용액을 제조하고, 혼합용액 내의 산소를 제거하는 단계(단계 1); 상기 혼합용액에 2만 내지 100만의 분자량을 갖는 기공유도물질 및 중합개시제를 혼합한 후, 중합반응을 진행하는 단계(단계 2); 및 상기 단계 2에서 중합반응이 수행된 혼합용액에서 유기 모노리트를 분리하는 단계(단계 3);를 포함하는 유기 모노리트 분말의 제조방법에 관한 것이다. 본 발명에 따른 유기 모노리트 분말의 제조방법은 2만 내지 100만의 분자량을 갖는 기공유도물질을 사용함으로써, 메조크기의 기공은 거의 없으며 매크로크기의 총 기공 부피가 큰 유기 모노리트 분말을 제조할 수 있다. 이때, 매크로 기공이 내부에는 존재하지 않으면서 모노리트 표면 부근에 박혀있는 형태로 존재하므로 물질 전달속도가 빠르고, 모노리트 형태로 인하여 충전 용매의 흐름이 빠르고 힘이 있어서 충전효율이 좋아지고 최대한 조밀한 충전 구조를 얻을 수 있으므로, 크로마토그래피 정지상으로 사용할 때, C18부착 5 ㎛ 실리카 분말의 분리효율과 유사한 우수한 분리효율을 얻을 수 있다.
METHOD FOR MANUFACTURING OF GROUND ORGANIC MONOLITH PARTICLES AND THE GROUND ORGANIC MONOLITH PARTICLES THEREBY
유기 모노리트 분말의 제조방법 및 이에 따라 제조되는 유기 모노리트 분말
CHEONG WON JO (Autor:in)
29.07.2015
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
Europäisches Patentamt | 2016
METHOD FOR PREPARING ORGANIC MONOLITH POWDER AND ORGANIC MONOLITH POWDER PREPARED THEREBY
| Europäisches Patentamt | 2015
Preparation method of ceramic monolith structure and ceramic monolith structure thereby
Europäisches Patentamt | 2016
PREPARATION METHOD OF CERAMIC MONOLITH STRUCTURE AND CERAMIC MONOLITH STRUCTURE THEREBY
| Europäisches Patentamt | 2016