LOW-THERMAL-EXPANSION CERAMIC WARE
The present invention relates to a low thermo-expandable and heat-resistant pottery. Heat shock resistance of clay can be maximized by minimizing thermal expansion coefficient of the heat-resistant pottery clay, selectively adding, into the clay, natural petalite or synthetic eucryptite as an Li_2O-Al_2O_3-SiO_2-based (LAS) material and controlling thermal expansion properties by content ratio of a mixture and a heat treatment temperature. The produced clay heat-resistant shock sensitivity without few or no thermal expansion. Beta-eucryptite (β-eucryptite) powder used as a low thermos-expandable ingredient is artificially synthesized by adding lithium carbonate (Li_2CO) and aluminum hydroxide (Al(OH)_3) into silica (SiO_2).
본 발명은 내열자기 소지의 열팽창계수를 최소화하여 소지의 열충격 저항성을 최대화시키기 위하여, 점토에 LAS계 재료로서 천연 petalite 또는 합성 eucryptite를 선택적으로 첨가하고 혼합물의 조성 비율과 열처리 온도를 변화시켜 열팽창 특성을 제어한다. 제조된 소지는 열팽창이 거의 없는 내열충격성을 보였다. 저열팽창 재료로 사용된 β-eucryptite 분말은 규석 (SiO)에 탄산리튬 (LiCO) 및 수산화알루미늄 (Al(OH))을 첨가하여 인공적으로 합성되었다.
LOW-THERMAL-EXPANSION CERAMIC WARE
The present invention relates to a low thermo-expandable and heat-resistant pottery. Heat shock resistance of clay can be maximized by minimizing thermal expansion coefficient of the heat-resistant pottery clay, selectively adding, into the clay, natural petalite or synthetic eucryptite as an Li_2O-Al_2O_3-SiO_2-based (LAS) material and controlling thermal expansion properties by content ratio of a mixture and a heat treatment temperature. The produced clay heat-resistant shock sensitivity without few or no thermal expansion. Beta-eucryptite (β-eucryptite) powder used as a low thermos-expandable ingredient is artificially synthesized by adding lithium carbonate (Li_2CO) and aluminum hydroxide (Al(OH)_3) into silica (SiO_2).
본 발명은 내열자기 소지의 열팽창계수를 최소화하여 소지의 열충격 저항성을 최대화시키기 위하여, 점토에 LAS계 재료로서 천연 petalite 또는 합성 eucryptite를 선택적으로 첨가하고 혼합물의 조성 비율과 열처리 온도를 변화시켜 열팽창 특성을 제어한다. 제조된 소지는 열팽창이 거의 없는 내열충격성을 보였다. 저열팽창 재료로 사용된 β-eucryptite 분말은 규석 (SiO)에 탄산리튬 (LiCO) 및 수산화알루미늄 (Al(OH))을 첨가하여 인공적으로 합성되었다.
LOW-THERMAL-EXPANSION CERAMIC WARE
저열팽창성 내열자기
KIM NAM IL (Autor:in) / LEE SANG JIN (Autor:in) / GONG HEON (Autor:in)
20.11.2015
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
"Moisture expansion" of ceramic white ware
| Engineering Index Backfile | 1932
Ceramic ware manufacturing methode using injection molding and Ceramic ware thereof
Europäisches Patentamt | 2016
CERAMIC WARE MANUFACTURING METHODE USING INJECTION MOLDING AND CERAMIC WARE THEREOF
| Europäisches Patentamt | 2015