COATING COMPOSITION FOR A TEXTILE GRID
The present invention relates to a coating composition for a textile grid, comprising a ratio of: 5-15 parts by weight of water; 65-75 parts by weight of an acryl emulsion resin; 0.1-5 parts by weight of acrylsol; 0.1-5 parts by weight of an acrylate-based thickener; 0.1-5 parts by weight of calcium carbonate (CaCO_3); 3-13 parts by weight of calcite powder; 0.1-5 parts by weight of talc powder; and 0.1-5 parts by weight of kaolin powder. The coating composition for a textile grid of the present invention has effects of excellent durability, heat resistance, and the strength of a textile grid product.
본 발명은 텍스타일 그리드용 코팅 조성물에 관한 것으로, 물 5 ~ 15중량부; 아크릴 에멀젼 수지(Acrylic emulsion resin) 65 ~ 75중량부; 아크릴졸(Acrylsol) 0.1 ~ 5중량부; 아크릴레이트계 점증제(Acrylic thickener) 0.1 ~ 5중량부; 탄산칼슘(CaCO) 분말 0.1 ~ 5중량부; 방해석(Calcite) 분말 3 ~ 13중량부; 탈크(Talc) 분말 0.1 ~ 5중량부; 카올린(Kaolin) 분말 0.1 ~ 5중량부의 비율로 이루어지는 것을 특징으로 한다. 상기 아크릴 에멀젼 수지(Acrylic emulsion resin)는 고형분 함량이 20 ~ 30중량%이고 점도는 1,000 ~ 2,500cps(25)인 것을 사용하며, 상기 아크릴레이트계 점증제(Acrylic thickener)는 소듐폴리아크릴레이트(Sodium polyacrylate)를 사용한다. 또한, 본 발명의 코팅 조성물은 추가적으로 소포제(defoamer), 분산제(dispersion agent), 계면활성제(surfactant) 흑색안료(pigment black) 중에서 선택되는 1종 이상의 첨가제를 각각 0.1 ~ 5중량부 포함할 수 있으며, 상기 흑색안료는 카본블랙(Carbon black)인 것을 특징으로 하고 있다. 본 발명의 텍스타일 그리드용 코팅 조성물은 물에 아크릴 에멀젼 수지, 아크릴졸, 아크릴레이트계 점증제 및 무기질 충전제이 혼합 및 분산되어 이루어지는 수성 조성물이므로 작업성이 양호하고 주변 대기 및 토양을 오염시키지 않기 때문에 환경에 친화적이며, 또한 소재의 밀도와 접착력이 양호하고 내가수분해성이 높기 때문에 텍스타일 그리드 제품의 강도, 내열성 및 내구성이 매우 우수하게 되는 효과가 있다.
COATING COMPOSITION FOR A TEXTILE GRID
The present invention relates to a coating composition for a textile grid, comprising a ratio of: 5-15 parts by weight of water; 65-75 parts by weight of an acryl emulsion resin; 0.1-5 parts by weight of acrylsol; 0.1-5 parts by weight of an acrylate-based thickener; 0.1-5 parts by weight of calcium carbonate (CaCO_3); 3-13 parts by weight of calcite powder; 0.1-5 parts by weight of talc powder; and 0.1-5 parts by weight of kaolin powder. The coating composition for a textile grid of the present invention has effects of excellent durability, heat resistance, and the strength of a textile grid product.
본 발명은 텍스타일 그리드용 코팅 조성물에 관한 것으로, 물 5 ~ 15중량부; 아크릴 에멀젼 수지(Acrylic emulsion resin) 65 ~ 75중량부; 아크릴졸(Acrylsol) 0.1 ~ 5중량부; 아크릴레이트계 점증제(Acrylic thickener) 0.1 ~ 5중량부; 탄산칼슘(CaCO) 분말 0.1 ~ 5중량부; 방해석(Calcite) 분말 3 ~ 13중량부; 탈크(Talc) 분말 0.1 ~ 5중량부; 카올린(Kaolin) 분말 0.1 ~ 5중량부의 비율로 이루어지는 것을 특징으로 한다. 상기 아크릴 에멀젼 수지(Acrylic emulsion resin)는 고형분 함량이 20 ~ 30중량%이고 점도는 1,000 ~ 2,500cps(25)인 것을 사용하며, 상기 아크릴레이트계 점증제(Acrylic thickener)는 소듐폴리아크릴레이트(Sodium polyacrylate)를 사용한다. 또한, 본 발명의 코팅 조성물은 추가적으로 소포제(defoamer), 분산제(dispersion agent), 계면활성제(surfactant) 흑색안료(pigment black) 중에서 선택되는 1종 이상의 첨가제를 각각 0.1 ~ 5중량부 포함할 수 있으며, 상기 흑색안료는 카본블랙(Carbon black)인 것을 특징으로 하고 있다. 본 발명의 텍스타일 그리드용 코팅 조성물은 물에 아크릴 에멀젼 수지, 아크릴졸, 아크릴레이트계 점증제 및 무기질 충전제이 혼합 및 분산되어 이루어지는 수성 조성물이므로 작업성이 양호하고 주변 대기 및 토양을 오염시키지 않기 때문에 환경에 친화적이며, 또한 소재의 밀도와 접착력이 양호하고 내가수분해성이 높기 때문에 텍스타일 그리드 제품의 강도, 내열성 및 내구성이 매우 우수하게 되는 효과가 있다.
COATING COMPOSITION FOR A TEXTILE GRID
텍스타일 그리드용 코팅 조성물
BAEK YUN JIN (Autor:in) / KIM HAE GYEONG (Autor:in)
01.06.2016
Patent
Elektronische Ressource
Koreanisch
British Library Online Contents | 2006
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2020