QUICK-DRYING TYPE SELF-LEVELING MORTAR COMPOSITION
The present invention is adapted to shorten a bottom finishing period in a bottom mortar wet process. The present invention relates to a quick-drying type self-leveling mortar composition for reducing moisture contained in mortar at a high speed, the composition including 13 to 24 kg weight part of calcium aluminate cement, 2 to 11 kg weight part of general Portland cement, 3 to 12 kg weight part of gypsum, 0.1 to 2.0 kg weight part of slaked lime, 30 to 40 kg weight part of aggregate, 1 to 5 kg weight part of revival state powder ethylene vinyl acetate, 0.05 to 0.25 weight part of lithium carbonate, 0.2 to 1.0 kg weight part of calcium formate, 0.03 to 0.25 kg weight part of tin acid, 0.1 to 1.2 kg weight part of polycarboxylate, 0.1 to 0.7 kg weight part of polyglycol, 0.01 to 0.08 weight part of hydroxyethylenecellulose, and 2.52 to 50.41 kg weight part of lime stone.
본 발명은 바닥모르타르 습식공정에 있어 바닥마감 공정기간을 단축시키기 위한 목적으로, 타설후 모르타르내 함유된 수분을 빠른속도로 저감시키기 위한 속건형 셀프레벨링 모르타르 조성물에 관한것으로서, 칼슘알루미네이트시멘트 13~24kg중량부, 보통포틀랜드시멘트 2~11kg중량부, 석고 3~12kg중량부, 소석회 0.1~2.0kg중량부, 0.6mm이하 입도로 조절된 골재 30~40kg중량부, 재유화형 분말 에틸렌비닐아세테이트 1~5kg중량부, 리튬카보네이트 0.05~0.25kg중량부, 칼슘포메이트 0.2~1.0kg중량부, 주석산 0.03~0.25kg중량부, 폴리카복실레이트 0.1~1.2kg중량부, 폴리글리콜 0.1~0.7kg중량부, 히드록시에틸셀루로오스 0.01~0.08kg중량부에 석회석 분 2.52~50.41kg중량부로 조성되어 있음을 특징으로 하는 속건형 셀프레벨링 모르타르 조성물에 관한 것이다.
QUICK-DRYING TYPE SELF-LEVELING MORTAR COMPOSITION
The present invention is adapted to shorten a bottom finishing period in a bottom mortar wet process. The present invention relates to a quick-drying type self-leveling mortar composition for reducing moisture contained in mortar at a high speed, the composition including 13 to 24 kg weight part of calcium aluminate cement, 2 to 11 kg weight part of general Portland cement, 3 to 12 kg weight part of gypsum, 0.1 to 2.0 kg weight part of slaked lime, 30 to 40 kg weight part of aggregate, 1 to 5 kg weight part of revival state powder ethylene vinyl acetate, 0.05 to 0.25 weight part of lithium carbonate, 0.2 to 1.0 kg weight part of calcium formate, 0.03 to 0.25 kg weight part of tin acid, 0.1 to 1.2 kg weight part of polycarboxylate, 0.1 to 0.7 kg weight part of polyglycol, 0.01 to 0.08 weight part of hydroxyethylenecellulose, and 2.52 to 50.41 kg weight part of lime stone.
본 발명은 바닥모르타르 습식공정에 있어 바닥마감 공정기간을 단축시키기 위한 목적으로, 타설후 모르타르내 함유된 수분을 빠른속도로 저감시키기 위한 속건형 셀프레벨링 모르타르 조성물에 관한것으로서, 칼슘알루미네이트시멘트 13~24kg중량부, 보통포틀랜드시멘트 2~11kg중량부, 석고 3~12kg중량부, 소석회 0.1~2.0kg중량부, 0.6mm이하 입도로 조절된 골재 30~40kg중량부, 재유화형 분말 에틸렌비닐아세테이트 1~5kg중량부, 리튬카보네이트 0.05~0.25kg중량부, 칼슘포메이트 0.2~1.0kg중량부, 주석산 0.03~0.25kg중량부, 폴리카복실레이트 0.1~1.2kg중량부, 폴리글리콜 0.1~0.7kg중량부, 히드록시에틸셀루로오스 0.01~0.08kg중량부에 석회석 분 2.52~50.41kg중량부로 조성되어 있음을 특징으로 하는 속건형 셀프레벨링 모르타르 조성물에 관한 것이다.
QUICK-DRYING TYPE SELF-LEVELING MORTAR COMPOSITION
속건형 셀프레벨링 모르타르 조성물
JEON YONG HEE (Autor:in) / CHO SUNG HYUN (Autor:in) / SEO SHIN SEOK (Autor:in) / KANG DONG GYUN (Autor:in) / YOUN YONG SANG (Autor:in)
09.06.2016
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME