Composition of high strength concrete having superior cut-off resistance
The present invention relates to an ultra-high performance concrete (UHPC) composition having excellent cut-off resistance, using Al_2O_3 or SiC having high hardness as a fine aggregate, so as to enhance cut-off resistance performance while maintaining advantage of UHPC, thereby being applicable to various fields such as various kinds of safety and security equipment, facilities or structures. According to the present invention, the UHPC composition comprises: cement; 10 to 30 parts by weight of fumed silica with respect to 100 parts by weight of cement; 100 to 200 parts by weight of fine aggregate with respect to 100 parts by weight of cement; 10 to 40 parts by weight of filling materials with respect to 100 parts by weight of cement; 2 to 6 parts by weight of a high performance water reducing agent with respect to 100 parts by weight of cement; and water. The fine aggregate is any one of Al_2O_3 and SiC, and a water-cement ratio is 0.2 to 0.25, inclusively.
본 발명은 경도가 높은 산화알루미늄 또는 탄화규소를 잔골재로 사용하여 UHPC의 장점을 그대로 유지하면서 절단 저항 성능을 향상시킴으로써, 각종 안전·보안 관련 장비나 이러한 설비 또는 구조물 등을 비롯하여 다양한 분야에 활용할 수 있는 절단 저항이 우수한 초고성능 콘크리트 조성물에 대한 것이다. 본 발명의 절단 저항이 우수한 초고성능 콘크리트 조성물은 시멘트, 시멘트 100 중량부 대비 실리카퓸 10 내지 30 중량부, 잔골재 100 내지 200 중량부, 충전재 10 내지 40 중량부, 고성능 감수제 2 내지 6 중량부 및 물을 포함하여 구성되되, 상기 잔골재는 산화알루미늄(AlO) 또는 탄화규소(SiC) 중 어느 하나이고, 물-시멘트비는 0.2 이상 0.25 이하인 것을 특징으로 한다.
Composition of high strength concrete having superior cut-off resistance
The present invention relates to an ultra-high performance concrete (UHPC) composition having excellent cut-off resistance, using Al_2O_3 or SiC having high hardness as a fine aggregate, so as to enhance cut-off resistance performance while maintaining advantage of UHPC, thereby being applicable to various fields such as various kinds of safety and security equipment, facilities or structures. According to the present invention, the UHPC composition comprises: cement; 10 to 30 parts by weight of fumed silica with respect to 100 parts by weight of cement; 100 to 200 parts by weight of fine aggregate with respect to 100 parts by weight of cement; 10 to 40 parts by weight of filling materials with respect to 100 parts by weight of cement; 2 to 6 parts by weight of a high performance water reducing agent with respect to 100 parts by weight of cement; and water. The fine aggregate is any one of Al_2O_3 and SiC, and a water-cement ratio is 0.2 to 0.25, inclusively.
본 발명은 경도가 높은 산화알루미늄 또는 탄화규소를 잔골재로 사용하여 UHPC의 장점을 그대로 유지하면서 절단 저항 성능을 향상시킴으로써, 각종 안전·보안 관련 장비나 이러한 설비 또는 구조물 등을 비롯하여 다양한 분야에 활용할 수 있는 절단 저항이 우수한 초고성능 콘크리트 조성물에 대한 것이다. 본 발명의 절단 저항이 우수한 초고성능 콘크리트 조성물은 시멘트, 시멘트 100 중량부 대비 실리카퓸 10 내지 30 중량부, 잔골재 100 내지 200 중량부, 충전재 10 내지 40 중량부, 고성능 감수제 2 내지 6 중량부 및 물을 포함하여 구성되되, 상기 잔골재는 산화알루미늄(AlO) 또는 탄화규소(SiC) 중 어느 하나이고, 물-시멘트비는 0.2 이상 0.25 이하인 것을 특징으로 한다.
Composition of high strength concrete having superior cut-off resistance
절단 저항이 우수한 초고성능 콘크리트 조성물
HONG SUNG GUL (Autor:in) / KANG SUNG HOON (Autor:in)
13.03.2017
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
Concrete Additive Composition having High Early Strength
Europäisches Patentamt | 2015
| Europäisches Patentamt | 2019
| Europäisches Patentamt | 2015
High performance concrete composition having improved early-strength chracteristics
| Europäisches Patentamt | 2019
PLACING METHOD OF HIGH STRENGTH CONCRETE HAVING FREEZING DAMAGE RESISTANCE
| Europäisches Patentamt | 2017