Thermal Shock Resistant Composition for Bottom Gas Bubbling Refractory
A thermal shock resistant composition for a bottom gas bubbling refractory is provided. According to the present invention, the thermal shock resistant composition for a bottom gas bubbling refractory comprises a main material composed of 75-90 wt% of electrofused magnesia clinker and 10-25 wt% of flaky graphite. With respect to 100 parts by weight of the main material, the composition comprises: 0.5-5.0 parts by weight of coal-based pitch; 0.5-5.0 parts by weight of a Si-based organic or inorganic hybrid powder binder containing polycarbosilane; 0.5-5.0 parts by weight of frit having a melting temperature of 750~950°C; and 1.0-5.0 parts by weight of aluminum powder.
전로 저취 내화물용 내열충격성 조성물이 제공된다. 본 발명은, 중량%로 전융 마그네시아 클린커 75~90%와 인상 흑연 10~25%를 포함하여 조성되는 주원료와, 상기 주원료 100중량부에 대하여 석탄계 피치 0.5~5.0 중량부; 폴리카르보실란이 포함된 Si계 유,무기 하이브리드 분말 바인더 0.5~5.0 중량부; 750~950℃의 용융온도를 가지는 Frit 0.5~5.0 중량부; 및 알루미늄 분말 1.0~5.0 중량부를 첨가하여 이루어진 전로 저취 노즐 내화물용 조성물에 관한 것이다.
Thermal Shock Resistant Composition for Bottom Gas Bubbling Refractory
A thermal shock resistant composition for a bottom gas bubbling refractory is provided. According to the present invention, the thermal shock resistant composition for a bottom gas bubbling refractory comprises a main material composed of 75-90 wt% of electrofused magnesia clinker and 10-25 wt% of flaky graphite. With respect to 100 parts by weight of the main material, the composition comprises: 0.5-5.0 parts by weight of coal-based pitch; 0.5-5.0 parts by weight of a Si-based organic or inorganic hybrid powder binder containing polycarbosilane; 0.5-5.0 parts by weight of frit having a melting temperature of 750~950°C; and 1.0-5.0 parts by weight of aluminum powder.
전로 저취 내화물용 내열충격성 조성물이 제공된다. 본 발명은, 중량%로 전융 마그네시아 클린커 75~90%와 인상 흑연 10~25%를 포함하여 조성되는 주원료와, 상기 주원료 100중량부에 대하여 석탄계 피치 0.5~5.0 중량부; 폴리카르보실란이 포함된 Si계 유,무기 하이브리드 분말 바인더 0.5~5.0 중량부; 750~950℃의 용융온도를 가지는 Frit 0.5~5.0 중량부; 및 알루미늄 분말 1.0~5.0 중량부를 첨가하여 이루어진 전로 저취 노즐 내화물용 조성물에 관한 것이다.
Thermal Shock Resistant Composition for Bottom Gas Bubbling Refractory
전로 저취 내화물용 내열충격성 조성물
HEO JOON (Autor:in) / PARK JAE KYUNG (Autor:in) / BAE IN KYUNG (Autor:in) / KIM BONG JIK (Autor:in)
02.05.2019
Patent
Elektronische Ressource
Koreanisch
Thermal Shock Resistant Composition for Bottom Gas Bubbling Refractory
Europäisches Patentamt | 2019
Europäisches Patentamt | 2020
| Europäisches Patentamt | 2020
Light refractory aggregate resistant to thermal shock
| Europäisches Patentamt | 2016