WATER PROOFING COMPOSITION AND WATERPROOF METHOD FOR PAVEMENT THEREOF
A waterproofing composition of the present invention comprises: 55 to 65 wt% of a modified asphalt; and 35 to 45 wt% of an epoxy resin, wherein the modified asphalt comprises 0.3 to 0.67 part by weight of asphalt, 0.02 to 0.2 part by weight of a plasticizer, 0.11 to 0.55 part by weight of resin, 10 to 26 parts by weight of fatty acid anhydride, and 0.05 to 0.66 part by weight of a hardening accelerator based on the weight of the modified asphalt. In a general asphalt road, a waterproofing layer is formed on a bottom layer on which the asphalt concrete is paved before installing an asphalt concrete, the tack coat and primer coat are applied to the top surface of the waterproofing layer, and the asphalt concrete is installed to form a pavement layer. However, a waterproofing layer for road pavement of the present invention having an acid anhydrous-based modified asphalt and epoxy resin mixed therein is coated with a waterproofing layer to form the waterproofing layer (20) and perform roles of the tack coat and the primer coat at the same time. Therefore, the waterproofing composition according to the present invention not only reduces a time of applying separate tack coat and primer coat but also can solve an attachment property problem between the waterproofing layer and a tack or primer coat layer and an adhesive property problem between the tack coat layer and the asphalt concrete layer at the same time which are problems of an existing asphalt road.
본 발명의 방수조성물은 개질아스팔트 55~65 중량%; 에폭시 레진 35~45 중량%;를 포함하되, 상기 개질아스팔트는 상기 개질아스파트 중량을 기준으로, 아스팔트 0.3~0.67 중량부, 가소제 0.02~0.2 중량부, 수지 0.11~0.55 중량부, 지방산 무수물 10~26 중량부, 경화촉진제 0.05~0.66 중량부,를 포함한다. 일반적인 아스팔트도로는 아스팔트 콘크리트 포설 전에 아스팔트콘크리트가 포설되는 저면층에 방수층을 형성하고, 방수층의 상면에 텍코트와 프라이머코트를 각각 도포한 후 아스팔트콘크리트를 포설하여 포장층을 형성한다. 그러나 산 무수계열의 개질아스팔트와 에폭시레진을 혼합한 본 발명의 도로포장용 방수층은 방수층으로 도포 되어, 방수층(20)을 형성함과 아울러, 텍코트와 프라이머코트의 역활을 동시에 수행한다. 따라서 별도의 텍코트와 프라이머코트를 도포하는 시간을 단축함은 물론, 기존 아스팔트도로의 문제점인 방수층과 텍코트(프라이머코트)층의 첩착성 문제와 텍코트층과 아스팔트콘크리트층과의 접찹성 문제를 동시에 해결할 수 있다.
WATER PROOFING COMPOSITION AND WATERPROOF METHOD FOR PAVEMENT THEREOF
A waterproofing composition of the present invention comprises: 55 to 65 wt% of a modified asphalt; and 35 to 45 wt% of an epoxy resin, wherein the modified asphalt comprises 0.3 to 0.67 part by weight of asphalt, 0.02 to 0.2 part by weight of a plasticizer, 0.11 to 0.55 part by weight of resin, 10 to 26 parts by weight of fatty acid anhydride, and 0.05 to 0.66 part by weight of a hardening accelerator based on the weight of the modified asphalt. In a general asphalt road, a waterproofing layer is formed on a bottom layer on which the asphalt concrete is paved before installing an asphalt concrete, the tack coat and primer coat are applied to the top surface of the waterproofing layer, and the asphalt concrete is installed to form a pavement layer. However, a waterproofing layer for road pavement of the present invention having an acid anhydrous-based modified asphalt and epoxy resin mixed therein is coated with a waterproofing layer to form the waterproofing layer (20) and perform roles of the tack coat and the primer coat at the same time. Therefore, the waterproofing composition according to the present invention not only reduces a time of applying separate tack coat and primer coat but also can solve an attachment property problem between the waterproofing layer and a tack or primer coat layer and an adhesive property problem between the tack coat layer and the asphalt concrete layer at the same time which are problems of an existing asphalt road.
본 발명의 방수조성물은 개질아스팔트 55~65 중량%; 에폭시 레진 35~45 중량%;를 포함하되, 상기 개질아스팔트는 상기 개질아스파트 중량을 기준으로, 아스팔트 0.3~0.67 중량부, 가소제 0.02~0.2 중량부, 수지 0.11~0.55 중량부, 지방산 무수물 10~26 중량부, 경화촉진제 0.05~0.66 중량부,를 포함한다. 일반적인 아스팔트도로는 아스팔트 콘크리트 포설 전에 아스팔트콘크리트가 포설되는 저면층에 방수층을 형성하고, 방수층의 상면에 텍코트와 프라이머코트를 각각 도포한 후 아스팔트콘크리트를 포설하여 포장층을 형성한다. 그러나 산 무수계열의 개질아스팔트와 에폭시레진을 혼합한 본 발명의 도로포장용 방수층은 방수층으로 도포 되어, 방수층(20)을 형성함과 아울러, 텍코트와 프라이머코트의 역활을 동시에 수행한다. 따라서 별도의 텍코트와 프라이머코트를 도포하는 시간을 단축함은 물론, 기존 아스팔트도로의 문제점인 방수층과 텍코트(프라이머코트)층의 첩착성 문제와 텍코트층과 아스팔트콘크리트층과의 접찹성 문제를 동시에 해결할 수 있다.
WATER PROOFING COMPOSITION AND WATERPROOF METHOD FOR PAVEMENT THEREOF
방수조성물 및 이를 이용한 도로포장용 방수공법
MOON HUI SEOK (Autor:in)
24.07.2019
Patent
Elektronische Ressource
Koreanisch
Polyvinyl chloride waterproof sheet and complex water proofing method thereof
| Europäisches Patentamt | 2020
Water-proofing composition for bridge surface and water-proofing method thereof
| Europäisches Patentamt | 2019
POWDERED WATER PROOFING AGENT FOR CONCRETE AND METHOD OF WATERPROOF
Europäisches Patentamt | 2016
POWDERED WATER PROOFING AGENT FOR CONCRETE AND METHOD OF WATERPROOF
| Europäisches Patentamt | 2016
WATER PROOFING SHEET AND WATER PROOFING USING THEREOF
| Europäisches Patentamt | 2015