CA-CS Hydraulic binder composition using dry type slowly cooled calcium aluminate-calcium silicate based ladle furnace slag: Fid-Bau Portal

CA-CS Hydraulic binder composition using dry type slowly cooled calcium aluminate-calcium silicate based ladle furnace slag

KIM JIN MAN / CHOI SUN MI / HYUN JI SOO

Abstract

The present invention relates to a hydraulic binder using dry type slowly-cooled calcium aluminate(CA)-calcium silicate(CS) based steelmaking slag of a secondary refining process and, more specifically, to a hydraulic binder using dry type slowly-cooled CA-CS based steelmaking slag, in which gypsum is mixed with the CA-CS based steelmaking slag slowly cooled in the air and including Al_2O_3 content to realize hydration characteristics. According to the present invention, the hydraulic binder using the dry type slowly-cooled CA-CS based steelmaking slag mixes gypsum with the CA-CS based steelmaking slag slowly cooled in the air and including Al_2O_3 content and thus, provides the hydration characteristics for hydraulic properties and ettringite generation characteristics for realizing strength, thereby providing excellent effects of being used as a cement-based material and promoting utilization of steelmaking by-products.

본 발명은 2차 정련과정에서의 건식 서냉 CA-CS계 철강슬래그를 이용한 수경성 결합재에 관한 것으로, 보다 상세하게는 공기중에서 서냉되고 AlO함량이 존재하는 CA-CS계 철강슬래그에 석고를 혼합하여 수화특성을 가지도록 한 건식 서냉 CA-CS계 철강슬래그를 이용한 수경성 결합재에 관한 것이다. 본 발명의 건식 서냉 CA-CS계 철강슬래그를 이용한 수경성 결합재는 공기중에서 서냉되고 AlO함량이 존재하는 CA-CS계 철강슬래그에 석고를 혼합하여 수경성을 위한 수화반응 특성과 강도발현을 위한 에트링가이트 생성특성을 나타내므로 시멘트계 재료로 활용될 수 있으며, 철강 부산물의 활용도 제고에도 기여할 수 있는 우수한 효과가 있다.

Zugriff

Download

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren