Inhibiting Abnormal Grain Growth of Ultra Fine Polycrystalline Diamond
The present invention relates to a sintering method for inhibiting abnormal grain growth which occurs in a process of sintering polycrystalline diamond. The present invention provides a method for manufacturing a polycrystalline diamond sintering tool, including the steps of: providing first diamond powder having at least two grain peaks and having an average diameter (D50) of 0.5 to 1 mm; forming the first diamond powder by mixing the first diamond powder with coupling agent powder; and sintering the formed body on an ultra-hard substrate at a high temperature and a high pressure. According to the present invention, a method for manufacturing a PCD sintering body which inhibits abnormal grain growth of diamond grains can be provided by controlling the diameters of PCD grains without inputting an additional material.
본 발명은 다결정 다이아몬드의 소결 과정에서 발생하는 비정상 입성장을 억제하는 소결 방법에 관한 것이다. 본 발명은 최소한 2 개의 입도 피크를 갖고 평균입도(D50)가 0.5 ~ 1 ㎛인 제1 다이아몬드 분말을 제공하는 단계; 상기 제1 다이아몬드 분말을 결합제 분말과 혼합하여 성형하는 단계; 및 초경기판 상에서 상기 성형된 성형체를 고온고압 소결하는 단계를 포함하는 것을 특징으로 하는 다결정다이아몬드 소결 공구의 제조방법을 제공한다. 본 발명에 따르면, 추가적인 물질의 투입 없이 PCD 입자의 입도를 제어함으로써 다이아몬드 입자의 비정상 입자 성장을 억제하는 PCD 소결체의 제조 방법을 제공할 수 있게 된다.
Inhibiting Abnormal Grain Growth of Ultra Fine Polycrystalline Diamond
The present invention relates to a sintering method for inhibiting abnormal grain growth which occurs in a process of sintering polycrystalline diamond. The present invention provides a method for manufacturing a polycrystalline diamond sintering tool, including the steps of: providing first diamond powder having at least two grain peaks and having an average diameter (D50) of 0.5 to 1 mm; forming the first diamond powder by mixing the first diamond powder with coupling agent powder; and sintering the formed body on an ultra-hard substrate at a high temperature and a high pressure. According to the present invention, a method for manufacturing a PCD sintering body which inhibits abnormal grain growth of diamond grains can be provided by controlling the diameters of PCD grains without inputting an additional material.
본 발명은 다결정 다이아몬드의 소결 과정에서 발생하는 비정상 입성장을 억제하는 소결 방법에 관한 것이다. 본 발명은 최소한 2 개의 입도 피크를 갖고 평균입도(D50)가 0.5 ~ 1 ㎛인 제1 다이아몬드 분말을 제공하는 단계; 상기 제1 다이아몬드 분말을 결합제 분말과 혼합하여 성형하는 단계; 및 초경기판 상에서 상기 성형된 성형체를 고온고압 소결하는 단계를 포함하는 것을 특징으로 하는 다결정다이아몬드 소결 공구의 제조방법을 제공한다. 본 발명에 따르면, 추가적인 물질의 투입 없이 PCD 입자의 입도를 제어함으로써 다이아몬드 입자의 비정상 입자 성장을 억제하는 PCD 소결체의 제조 방법을 제공할 수 있게 된다.
Inhibiting Abnormal Grain Growth of Ultra Fine Polycrystalline Diamond
초미립 다결정 다이아몬드의 비정상 입자성장 제어 방법
SHIN YONG JUN (Autor:in)
26.05.2020
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
Homogeneous Abnormal Grain Growth in Polycrystalline Materials
| British Library Online Contents | 2012
Investigation of grain boundaries for abnormal grain growth in polycrystalline SrTiO~3
| British Library Online Contents | 2010
Fabrication of ultrafine polycrystalline diamond with nano-sized grain growth inhibitor
| Europäisches Patentamt | 2017
| British Library Online Contents | 1999
Abnormal Grain Growth in Metals
| British Library Online Contents | 2007