Slip-resistant non-slip composition using cement mixture and slip-resistant construction method using it
The present invention relates to a slip-resistant non-slip composition using a cement mixture and a slip-resistant construction method using the slip-resistant non-slip composition, in which construction is performed rapidly and conveniently, and adhesion, durability, and stability are excellent. According to the present invention, the slip-resistant non-slip composition using the cement mixture includes: 70 to 95 wt% of a secondary composition; and 5 to 30 wt% of a water-soluble mixed acryl resin composition, wherein the secondary composition includes 35 to 55 wt% of a primary composition and 45 to 65 wt% of silica sand, and the primary composition includes 55 to 64 wt% of calcium oxide, 10 to 25 wt% of silica, 5 to 16 wt% of aluminum oxide, 5 to 17 wt% of sulfur trioxide, 2 to 7 wt% of iron oxide, 0.5 to 3 wt% of magnesium oxide, 0.5 to 2 wt% of titanium dioxide, 0.1 to 3 wt% of tartaric acid, 0.1 to 2 wt% of polyvinyl alcohol, and 3 to 14 wt% of slag.
본 발명은 시멘트 혼합물을 원료로 사용하여 시공이 빠르고 편리하며 부착력, 내구성 및 안정성이 우수한 미끄럼 방지용 논슬립 조성물과 이를 이용한 미끄럼 방지 시공방법에 관한 것이다. 본 발명에서는, 2차 조성물 70~95중량% 및 수용성 혼합 아크릴수지 조성물 5~30중량%를 포함하며, 상기 2차 조성물은 1차 조성물 35~55중량% 및 규사 45~65중량%를 포함하고, 상기 1차 조성물은 산화칼슘(CaO) 55~64중량%, 실리카(SiO) 10~25중량%, 산화알루미늄(AlO) 5~16중량%, 삼산화황(SO) 5~17중량%, 산화철(FeO) 2~7중량%, 산화마그네슘(MgO) 0.5~3중량%, 이산화티타늄(TiO) 0.5~2중량%, 타타르산(CHO) 0.1~3중량%, 폴리비닐알콜 0.1~2중량% 및 슬래그 3~14중량%를 포함하는, 시멘트 혼합물을 이용한 미끄럼 방지용 논슬립 조성물이 제공된다. 본 발명의 시멘트 혼합물을 이용한 미끄럼 방지용 논슬립 조성물은 미끄럼 방지용으로 누구나 쉽고 빠르게 시공할 수 있고, 얇게는 0.5㎜까지 시공이 가능하며, 미끄럼 방지 효과가 좋고, 얇은 두께에도 부착력이 강하고 갈라짐이 없으며 내구성 및 안정성이 우수하다. 또한, 미끄럼 방지 기능과 더불어 코팅재로서 로고, 글자 등을 새기는데도 활용할 수 있고, 인테리어 제품 등 다양한 용도로도 활용이 가능하다.
Slip-resistant non-slip composition using cement mixture and slip-resistant construction method using it
The present invention relates to a slip-resistant non-slip composition using a cement mixture and a slip-resistant construction method using the slip-resistant non-slip composition, in which construction is performed rapidly and conveniently, and adhesion, durability, and stability are excellent. According to the present invention, the slip-resistant non-slip composition using the cement mixture includes: 70 to 95 wt% of a secondary composition; and 5 to 30 wt% of a water-soluble mixed acryl resin composition, wherein the secondary composition includes 35 to 55 wt% of a primary composition and 45 to 65 wt% of silica sand, and the primary composition includes 55 to 64 wt% of calcium oxide, 10 to 25 wt% of silica, 5 to 16 wt% of aluminum oxide, 5 to 17 wt% of sulfur trioxide, 2 to 7 wt% of iron oxide, 0.5 to 3 wt% of magnesium oxide, 0.5 to 2 wt% of titanium dioxide, 0.1 to 3 wt% of tartaric acid, 0.1 to 2 wt% of polyvinyl alcohol, and 3 to 14 wt% of slag.
본 발명은 시멘트 혼합물을 원료로 사용하여 시공이 빠르고 편리하며 부착력, 내구성 및 안정성이 우수한 미끄럼 방지용 논슬립 조성물과 이를 이용한 미끄럼 방지 시공방법에 관한 것이다. 본 발명에서는, 2차 조성물 70~95중량% 및 수용성 혼합 아크릴수지 조성물 5~30중량%를 포함하며, 상기 2차 조성물은 1차 조성물 35~55중량% 및 규사 45~65중량%를 포함하고, 상기 1차 조성물은 산화칼슘(CaO) 55~64중량%, 실리카(SiO) 10~25중량%, 산화알루미늄(AlO) 5~16중량%, 삼산화황(SO) 5~17중량%, 산화철(FeO) 2~7중량%, 산화마그네슘(MgO) 0.5~3중량%, 이산화티타늄(TiO) 0.5~2중량%, 타타르산(CHO) 0.1~3중량%, 폴리비닐알콜 0.1~2중량% 및 슬래그 3~14중량%를 포함하는, 시멘트 혼합물을 이용한 미끄럼 방지용 논슬립 조성물이 제공된다. 본 발명의 시멘트 혼합물을 이용한 미끄럼 방지용 논슬립 조성물은 미끄럼 방지용으로 누구나 쉽고 빠르게 시공할 수 있고, 얇게는 0.5㎜까지 시공이 가능하며, 미끄럼 방지 효과가 좋고, 얇은 두께에도 부착력이 강하고 갈라짐이 없으며 내구성 및 안정성이 우수하다. 또한, 미끄럼 방지 기능과 더불어 코팅재로서 로고, 글자 등을 새기는데도 활용할 수 있고, 인테리어 제품 등 다양한 용도로도 활용이 가능하다.
Slip-resistant non-slip composition using cement mixture and slip-resistant construction method using it
시멘트 혼합물을 이용한 미끄럼 방지용 논슬립 조성물 및 이를 이용한 미끄럼 방지 시공방법