JOINT FILLER COMPOSITION AND MANUFACTURONG METHOD THEREOF
A highly ductile composition for filling an expansion joint of the present invention comprises: 20 to 30 wt% of cement; 30 to 40 wt% of fly ash; 15 to 25 wt% of silica sand; 0.5 to 3.5 wt% of beads; 0.1 to 0.5 wt% of a thickener; 1 to 2 wt% of a water reducing agent; 8 to 15 wt% of water; and 0.01 to 0.03 wt% of polyvinyl alcohol fibers. At this time, it is preferable that the beads have a density of 1.2 to 1.9 g/cm^3, are polystyrene beads, and have a particle diameter of 1.5 to 2 mm. According to one embodiment of the present invention, a manufacturing method of the highly ductile composition for filling an expansion joint comprises: a powder stirring step of mixing cement, fly ash, silica sand, and a thickener; a first stirring step of mixing water and a water reducing agent after the powder stirring step; a second stirring step of mixing polyvinyl alcohol fibers after the first stirring step; and a third stirring step of mixing beads after the second stirring step. The beads of the present invention are formed with a sharp edge as shown in FIG. 1 and are mixed inside the composition. Due to the characteristics of the material and shape, the beads are weakly bonded to a binder (cement, ash) of the highly ductile composition for filling an expansion joint. Accordingly, the highly ductile composition does not crack by being filled in an expansion joint.
본 발명의 신축이음부 충전용 고연성 조성물은 시멘트 20~30 중량%; 플라이애시 30~40 중량%; 규사 15~25 중량%; 비드(Beads) 0.5~3.5 중량%; 증점제 0.1~0.5 중량%; 감수제 1~2 중량%; 물 8~15 중량%; 폴리비닐알콜 섬유 0.01~0.03 중량%;를 포함한다. 이때 비드(Beads)의 밀도는 1.2~1.9g/㎤인 것으로서, 폴리스티렌(Polystyrene) 비드(Beads)이고, 입경이 1.5 ~ 2mm인 것이 바람직하다. 본 발명의 일 실시 예에 따른 신축이음부 충전용 고연성 조성물 제조방법은 시멘트, 플라이애시, 규사, 증점제를 혼합하여 믹싱하는 분체교반단계; 분체교반단계 이후에 물과 감수제를 혼합하여 믹싱하는 제1교반단계; 제1교반단계 이후에 폴리비닐알콜 섬유를 혼합하여 믹싱하는 제2교반단계; 제2교반단계 이후에 비드(Beads)를 혼합하여 믹싱하는 제3교반단계;를 포함한다. 본 발명의 비드(Beads)는 도 1과 같이 모서리부가 날카롭게 형성되어, 조성물 내부에 혼합되는데, 재질 및 형상의 특성으로 인해 신축이음부 충전용 고연성 조성물의 바인더(시멘트, 애시)와 약하게 결합되는 특징이 있다.
JOINT FILLER COMPOSITION AND MANUFACTURONG METHOD THEREOF
A highly ductile composition for filling an expansion joint of the present invention comprises: 20 to 30 wt% of cement; 30 to 40 wt% of fly ash; 15 to 25 wt% of silica sand; 0.5 to 3.5 wt% of beads; 0.1 to 0.5 wt% of a thickener; 1 to 2 wt% of a water reducing agent; 8 to 15 wt% of water; and 0.01 to 0.03 wt% of polyvinyl alcohol fibers. At this time, it is preferable that the beads have a density of 1.2 to 1.9 g/cm^3, are polystyrene beads, and have a particle diameter of 1.5 to 2 mm. According to one embodiment of the present invention, a manufacturing method of the highly ductile composition for filling an expansion joint comprises: a powder stirring step of mixing cement, fly ash, silica sand, and a thickener; a first stirring step of mixing water and a water reducing agent after the powder stirring step; a second stirring step of mixing polyvinyl alcohol fibers after the first stirring step; and a third stirring step of mixing beads after the second stirring step. The beads of the present invention are formed with a sharp edge as shown in FIG. 1 and are mixed inside the composition. Due to the characteristics of the material and shape, the beads are weakly bonded to a binder (cement, ash) of the highly ductile composition for filling an expansion joint. Accordingly, the highly ductile composition does not crack by being filled in an expansion joint.
본 발명의 신축이음부 충전용 고연성 조성물은 시멘트 20~30 중량%; 플라이애시 30~40 중량%; 규사 15~25 중량%; 비드(Beads) 0.5~3.5 중량%; 증점제 0.1~0.5 중량%; 감수제 1~2 중량%; 물 8~15 중량%; 폴리비닐알콜 섬유 0.01~0.03 중량%;를 포함한다. 이때 비드(Beads)의 밀도는 1.2~1.9g/㎤인 것으로서, 폴리스티렌(Polystyrene) 비드(Beads)이고, 입경이 1.5 ~ 2mm인 것이 바람직하다. 본 발명의 일 실시 예에 따른 신축이음부 충전용 고연성 조성물 제조방법은 시멘트, 플라이애시, 규사, 증점제를 혼합하여 믹싱하는 분체교반단계; 분체교반단계 이후에 물과 감수제를 혼합하여 믹싱하는 제1교반단계; 제1교반단계 이후에 폴리비닐알콜 섬유를 혼합하여 믹싱하는 제2교반단계; 제2교반단계 이후에 비드(Beads)를 혼합하여 믹싱하는 제3교반단계;를 포함한다. 본 발명의 비드(Beads)는 도 1과 같이 모서리부가 날카롭게 형성되어, 조성물 내부에 혼합되는데, 재질 및 형상의 특성으로 인해 신축이음부 충전용 고연성 조성물의 바인더(시멘트, 애시)와 약하게 결합되는 특징이 있다.
JOINT FILLER COMPOSITION AND MANUFACTURONG METHOD THEREOF
신축이음부 충전용 고연성 조성물 및 그 제조방법
KIL YONG SU (Autor:in) / KIM MAN HO (Autor:in) / IM BYEONG HO (Autor:in)
08.12.2020
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
THERMALLY EXPANDABLE PUTTY COMPOSITION AND JOINT FILLER
| Europäisches Patentamt | 2021
JOINT FILLER, METHOD FOR PRODUCING JOINT FILLER, AND JOINED BODY
| Europäisches Patentamt | 2018