Cementitious composites and method for manufacturing the cementitious composites
A cement composite is disclosed. The cement composite is obtained by mixing a binder and a reinforcing fiber. The binder is blended with 50-100 parts by weight of fine blast furnace slag powder, 30-50 parts by weight of silica sand, and 2-6 parts by weight of a water reducing agent based on 100 parts by weight of Portland cement. The reinforcing fiber is blended at a volume ratio of 1 to 3% with respect to the cement composite.
시멘트 복합체가 개시된다. 시멘트 복합체는 결합재와 보강 섬유가 혼합되며, 상기 결합재는 포틀랜드 시멘트 100중량부에 대하여 고로슬래그미분말 50~100 중량부, 실리카샌드 30~50 중량부, 그리고 감수제 2 내지 6 중량부로 배합되고, 상기 보강 섬유는 상기 시멘트 복합체에 대해 1 내지 3% 체적비로 배합된다.
Cementitious composites and method for manufacturing the cementitious composites
A cement composite is disclosed. The cement composite is obtained by mixing a binder and a reinforcing fiber. The binder is blended with 50-100 parts by weight of fine blast furnace slag powder, 30-50 parts by weight of silica sand, and 2-6 parts by weight of a water reducing agent based on 100 parts by weight of Portland cement. The reinforcing fiber is blended at a volume ratio of 1 to 3% with respect to the cement composite.
시멘트 복합체가 개시된다. 시멘트 복합체는 결합재와 보강 섬유가 혼합되며, 상기 결합재는 포틀랜드 시멘트 100중량부에 대하여 고로슬래그미분말 50~100 중량부, 실리카샌드 30~50 중량부, 그리고 감수제 2 내지 6 중량부로 배합되고, 상기 보강 섬유는 상기 시멘트 복합체에 대해 1 내지 3% 체적비로 배합된다.
Cementitious composites and method for manufacturing the cementitious composites
시멘트 복합체 및 이의 제조 방법
DOO YEOL YOO (Autor:in) / MIN JAE KIM (Autor:in)
14.04.2022
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
Cementitious composites and method for manufacturing the cementitious composites
Europäisches Patentamt | 2023
Engineered cementitious composites
| British Library Conference Proceedings | 2005