SYNTHESIS OF LOW THERMAL EXPANSION CORDIERITE CERAMICS USING KAOLIN GROUP MINERALS AND CORDIERITE CERAMICS WITH LOW THERMAL EXPANSION THEREOF
The present invention relates to a method for preparing low-thermal expansion cordierite ceramics containing kaolin minerals to improve the difficult firing conditions of kaolin minerals and increase mechanical properties in MAS-based cordierite with low thermal expansion, and a low-thermal expansion cordierite-based ceramic composition containing kaolin minerals prepared thereby. The method for preparing low-thermal expansion cordierite ceramics containing kaolin minerals according to the present invention comprises: a first step of mixing halloysite kaolin, clay, kaolinite kaolin, talc, aluminum oxide (Al_2O_3) and magnesium oxide (MgO) to prepare a raw mixture; a second step of milling the raw material by using a ball mill and a pot mill; a third step of compressing the raw mixture subjected to milling to perform a press molding; a fourth step of drying the raw mixture subjected to press molding; and a fifth step of firing and sintering the raw material subjected to drying under an oxidative atmosphere. Accordingly, provided is the method for preparing low-thermal expansion cordierite ceramics that exhibit the characteristics of low thermal expansion coefficient, thermal shock resistance, low permittivity, and high electrical insulation.
본 발명은 열팽창이 낮은 MAS계 코디어라이트에 고령토 광물의 까다로운 소성 조건을 개선하고 기계적 특성을 증가시키기 위해 고령토 광물을 포함한 저열팽창 코디어라이트 세라믹 제조방법 및 이를 이용한 고령토 광물을 포함한 저열팽창 코디어라이트계 세라믹 조성물에 관한 것이다. 본 발명에 따른 고령토 광물을 포함한 저열팽창 코디어라이트 세라믹 제조 방법은, 할로이사이트 고령토(Halloysite Kaolin), 점토(Clay), 카올리나이트 고령토(Kaolinite Kaolin), 활석(talc), 산화알루미늄(Al2O3) 및 산화마그네슘(MgO)을 혼합하여 원료혼합물을 제조하는 제1단계; 상기 원료혼합물을 볼밀(Ball Mill)과 포트밀(Pot Mll)을 이용하여 밀링하는 제2단계; 상기 밀링 처리 된 원료혼합물에 압력을 가하여 프레스성형(Press Molding)하는 제3단계; 상기 프레스성형(Press Molding) 처리 된 원료혼합물을 건조하는 제4단계; 상기 건조 처리된 원료혼합물을 산화분위기에 소성시켜 소결하는 제5단계;를 포함하는 것을 특징으로 한다.
SYNTHESIS OF LOW THERMAL EXPANSION CORDIERITE CERAMICS USING KAOLIN GROUP MINERALS AND CORDIERITE CERAMICS WITH LOW THERMAL EXPANSION THEREOF
The present invention relates to a method for preparing low-thermal expansion cordierite ceramics containing kaolin minerals to improve the difficult firing conditions of kaolin minerals and increase mechanical properties in MAS-based cordierite with low thermal expansion, and a low-thermal expansion cordierite-based ceramic composition containing kaolin minerals prepared thereby. The method for preparing low-thermal expansion cordierite ceramics containing kaolin minerals according to the present invention comprises: a first step of mixing halloysite kaolin, clay, kaolinite kaolin, talc, aluminum oxide (Al_2O_3) and magnesium oxide (MgO) to prepare a raw mixture; a second step of milling the raw material by using a ball mill and a pot mill; a third step of compressing the raw mixture subjected to milling to perform a press molding; a fourth step of drying the raw mixture subjected to press molding; and a fifth step of firing and sintering the raw material subjected to drying under an oxidative atmosphere. Accordingly, provided is the method for preparing low-thermal expansion cordierite ceramics that exhibit the characteristics of low thermal expansion coefficient, thermal shock resistance, low permittivity, and high electrical insulation.
본 발명은 열팽창이 낮은 MAS계 코디어라이트에 고령토 광물의 까다로운 소성 조건을 개선하고 기계적 특성을 증가시키기 위해 고령토 광물을 포함한 저열팽창 코디어라이트 세라믹 제조방법 및 이를 이용한 고령토 광물을 포함한 저열팽창 코디어라이트계 세라믹 조성물에 관한 것이다. 본 발명에 따른 고령토 광물을 포함한 저열팽창 코디어라이트 세라믹 제조 방법은, 할로이사이트 고령토(Halloysite Kaolin), 점토(Clay), 카올리나이트 고령토(Kaolinite Kaolin), 활석(talc), 산화알루미늄(Al2O3) 및 산화마그네슘(MgO)을 혼합하여 원료혼합물을 제조하는 제1단계; 상기 원료혼합물을 볼밀(Ball Mill)과 포트밀(Pot Mll)을 이용하여 밀링하는 제2단계; 상기 밀링 처리 된 원료혼합물에 압력을 가하여 프레스성형(Press Molding)하는 제3단계; 상기 프레스성형(Press Molding) 처리 된 원료혼합물을 건조하는 제4단계; 상기 건조 처리된 원료혼합물을 산화분위기에 소성시켜 소결하는 제5단계;를 포함하는 것을 특징으로 한다.
SYNTHESIS OF LOW THERMAL EXPANSION CORDIERITE CERAMICS USING KAOLIN GROUP MINERALS AND CORDIERITE CERAMICS WITH LOW THERMAL EXPANSION THEREOF
고령토 광물을 활용한 저열팽창 코디어라이트 세라믹 제조방법 및 이를 이용한 고령토 광물을 포함한 저열팽창 코디어라이트계 세라믹 조성물
KIM SOON HO (Autor:in)
03.01.2023
Patent
Elektronische Ressource
Koreanisch
Europäisches Patentamt | 2024
Kaolin-based zeolite Y, a precursor for cordierite ceramics
| Elsevier | 2004
Kaolin-based zeolite Y, a precursor for cordierite ceramics
| Online Contents | 2005
Clays, clay minerals and cordierite ceramics - a review
| British Library Online Contents | 2015