METHOD OF PRODUCING ARTICLES FROM SINTERED COMPOSITES
FIELD: process engineering.SUBSTANCE: invention relates to silicon carbide-based structural materials used in oil production and processing industries (end seals, oil pumps, downhole pumps, bearings, etc). Proposed process comprises forming of the billet based on fine filler as the powder of cubic boron nitride or boron carbide and temporary binder. Formed billet is annealed at final temperature corresponding to that of complete removal of volatile products from temporary binder, and siliconizing. This compound uses the mix of said powders with carbon of silicon-active variety with particle size of not over 20 mcm (ash or colloidal graphite) as aforesaid fine filler. Siliconizing after annealing is performed by vapour-liquid-phase process at capillary condensation of silicon vapours at billet heating to 1300-1500°C. Cubic boron nitride or boron carbide and carbon in the mix are taken in the amount of 70-80 and 20-30 wt %.EFFECT: higher hardness and strength of composite.2 cl, 1 tbl
Изобретение относится к области конструкционных материалов на основе карбида кремния, применяемых в оборудовании для нефтедобывающей и нефтеперерабатывающей промышленности (торцевые уплотнения нефтяных насосов и погружных агрегатов, подшипники скольжения и т.п.) и в ряде других отраслей промышленности. Технический результат изобретения - повышение прочности и твердости композиционного материала без усложнения технологии изготовления из него изделий. Способ включает формование заготовки на основе композиции из мелкодисперсного наполнителя в виде порошка кубического нитрида бора или карбида бора и временного связующего, обжиг сформованной заготовки при конечной температуре, соответствующей температуре полного удаления летучих продуктов из временного связующего, и силицирование. В композиции для формования заготовки в качестве мелкодисперсного наполнителя используют смесь вышеуказанных порошков с углеродом активной к кремнию разновидности с размером частиц не более 20 мкм (сажи или коллоидного графита), а силицирование после проведения обжига заготовки осуществляют парожидкофазным методом путем капиллярной конденсации паров кремния при нагреве заготовок до температуры 1300-1500С, а тиглей с кремнием - до температуры, превышающей температуру заготовок. Кубический нитрид бора или карбид бора и углерод в их смеси берут в количестве 70-80 и 20-30 масс.%. 1 з.п. ф-лы, 1 табл.
METHOD OF PRODUCING ARTICLES FROM SINTERED COMPOSITES
FIELD: process engineering.SUBSTANCE: invention relates to silicon carbide-based structural materials used in oil production and processing industries (end seals, oil pumps, downhole pumps, bearings, etc). Proposed process comprises forming of the billet based on fine filler as the powder of cubic boron nitride or boron carbide and temporary binder. Formed billet is annealed at final temperature corresponding to that of complete removal of volatile products from temporary binder, and siliconizing. This compound uses the mix of said powders with carbon of silicon-active variety with particle size of not over 20 mcm (ash or colloidal graphite) as aforesaid fine filler. Siliconizing after annealing is performed by vapour-liquid-phase process at capillary condensation of silicon vapours at billet heating to 1300-1500°C. Cubic boron nitride or boron carbide and carbon in the mix are taken in the amount of 70-80 and 20-30 wt %.EFFECT: higher hardness and strength of composite.2 cl, 1 tbl
Изобретение относится к области конструкционных материалов на основе карбида кремния, применяемых в оборудовании для нефтедобывающей и нефтеперерабатывающей промышленности (торцевые уплотнения нефтяных насосов и погружных агрегатов, подшипники скольжения и т.п.) и в ряде других отраслей промышленности. Технический результат изобретения - повышение прочности и твердости композиционного материала без усложнения технологии изготовления из него изделий. Способ включает формование заготовки на основе композиции из мелкодисперсного наполнителя в виде порошка кубического нитрида бора или карбида бора и временного связующего, обжиг сформованной заготовки при конечной температуре, соответствующей температуре полного удаления летучих продуктов из временного связующего, и силицирование. В композиции для формования заготовки в качестве мелкодисперсного наполнителя используют смесь вышеуказанных порошков с углеродом активной к кремнию разновидности с размером частиц не более 20 мкм (сажи или коллоидного графита), а силицирование после проведения обжига заготовки осуществляют парожидкофазным методом путем капиллярной конденсации паров кремния при нагреве заготовок до температуры 1300-1500С, а тиглей с кремнием - до температуры, превышающей температуру заготовок. Кубический нитрид бора или карбид бора и углерод в их смеси берут в количестве 70-80 и 20-30 масс.%. 1 з.п. ф-лы, 1 табл.
METHOD OF PRODUCING ARTICLES FROM SINTERED COMPOSITES
СПОСОБ ИЗГОТОВЛЕНИЯ ИЗДЕЛИЙ ИЗ РЕАКЦИОННОСПЕЧЕННОГО КОМПОЗИЦИОННОГО МАТЕРИАЛА
KISELEV PAVEL ARKAD EVICH (Autor:in)
27.06.2015
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2015
SINTERED ARTICLE AND SINTERED ARTICLE PRODUCING METHOD
| Europäisches Patentamt | 2018
Sintered body, method for producing sintered body, powder, and sintered body
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2022