METHOD FOR PREPARING SUBMICRON BIPHASIC TRICALCIUM PHOSPHATE AND HYDROXYAPATITE CERAMICS
FIELD: medicine.SUBSTANCE: what is presented is a method for preparing submicron biphasic tricalcium phosphate and hydroxyapatite ceramics involving synthesis of single-phase powder of calcium salts and ammonium hydrophosphate, disaggregation, moulding and annealing. According to the invention, the calcium salt is presented by calcium acetate in the form of an aqueous solution of the concentration of 1M - 2M in Ca/P ratio applicable for initial salts and falling within the range of 1.5-1.6. The synthesis procedure involves single-step pouring of an aqueous solution of ammonium hydrophosphate to the aqueous solution of calcium acetate and mixing of the above solutions for 10-20 minutes, and separating the precipitate. The products are annealed at a temperature falling within the range of 1,050-1,150°C and kept at the above temperature for 0.5-1.5 hours. The produced ceramics contains ?-tricalcium phosphate and hydroxyapatite with a grain size of 400-600 nm.EFFECT: preparing the submicron biphasic ceramics having a uniform microsctructure.2 dwg, 1 tbl, 1 ex
Изобретение относится к области медицины и может быть использовано в травматологии и ортопедии, челюстно-лицевой хирургии и хирургической стоматологии для лечения дефектов костной ткани и в качестве материала-носителя лекарственных средств. Предложен способ получения субмикронной бифазной керамики на основе трикальцийфосфата и гидроксиапатита, включающий синтез однофазного порошка из растворов соли кальция и гидрофосфата аммония, дезагрегацию, формование и обжиг. Согласно изобретению в качестве соли кальция используют ацетат кальция в виде водного раствора с концентрацией 1М - 2М при соотношении Ca/P для исходных солей в интервале 1,5-1,6. Синтез проводят, одномоментно приливая водный раствор гидрофосфата аммония к водному раствору ацетата кальция с последующим перемешиванием указанных растворов в течение 10-20 минут, после чего отделяют осадок. Изделия обжигают в интервале 1050-1150°C с выдержкой при этой температуре в течение 0,5-1,5 часов. Полученная керамика содержит фазы β-трикальцийфосфата и гидроксиапатита, размер зерен составляет 400-600 нм. Технический результат изобретения - получение субмикронной бифазной керамики с однородной микроструктурой. 2 ил., 1 табл., 1 пр.
METHOD FOR PREPARING SUBMICRON BIPHASIC TRICALCIUM PHOSPHATE AND HYDROXYAPATITE CERAMICS
FIELD: medicine.SUBSTANCE: what is presented is a method for preparing submicron biphasic tricalcium phosphate and hydroxyapatite ceramics involving synthesis of single-phase powder of calcium salts and ammonium hydrophosphate, disaggregation, moulding and annealing. According to the invention, the calcium salt is presented by calcium acetate in the form of an aqueous solution of the concentration of 1M - 2M in Ca/P ratio applicable for initial salts and falling within the range of 1.5-1.6. The synthesis procedure involves single-step pouring of an aqueous solution of ammonium hydrophosphate to the aqueous solution of calcium acetate and mixing of the above solutions for 10-20 minutes, and separating the precipitate. The products are annealed at a temperature falling within the range of 1,050-1,150°C and kept at the above temperature for 0.5-1.5 hours. The produced ceramics contains ?-tricalcium phosphate and hydroxyapatite with a grain size of 400-600 nm.EFFECT: preparing the submicron biphasic ceramics having a uniform microsctructure.2 dwg, 1 tbl, 1 ex
Изобретение относится к области медицины и может быть использовано в травматологии и ортопедии, челюстно-лицевой хирургии и хирургической стоматологии для лечения дефектов костной ткани и в качестве материала-носителя лекарственных средств. Предложен способ получения субмикронной бифазной керамики на основе трикальцийфосфата и гидроксиапатита, включающий синтез однофазного порошка из растворов соли кальция и гидрофосфата аммония, дезагрегацию, формование и обжиг. Согласно изобретению в качестве соли кальция используют ацетат кальция в виде водного раствора с концентрацией 1М - 2М при соотношении Ca/P для исходных солей в интервале 1,5-1,6. Синтез проводят, одномоментно приливая водный раствор гидрофосфата аммония к водному раствору ацетата кальция с последующим перемешиванием указанных растворов в течение 10-20 минут, после чего отделяют осадок. Изделия обжигают в интервале 1050-1150°C с выдержкой при этой температуре в течение 0,5-1,5 часов. Полученная керамика содержит фазы β-трикальцийфосфата и гидроксиапатита, размер зерен составляет 400-600 нм. Технический результат изобретения - получение субмикронной бифазной керамики с однородной микроструктурой. 2 ил., 1 табл., 1 пр.
METHOD FOR PREPARING SUBMICRON BIPHASIC TRICALCIUM PHOSPHATE AND HYDROXYAPATITE CERAMICS
СПОСОБ ПОЛУЧЕНИЯ СУБМИКРОННОЙ БИФАЗНОЙ КЕРАМИКИ НА ОСНОВЕ ТРИКАЛЬЦИЙФОСФАТА И ГИДРОКСИАПАТИТА
SAFRONOVA TAT JANA VIKTOROVNA (Autor:in) / PUTLJAEV VALERIJ IVANOVICH (Autor:in) / EVDOKIMOV PAVEL VLADIMIROVICH (Autor:in) / KAZAKOVA GILJANA KONSTANTINOVNA (Autor:in) / IVANOV VLADIMIR KONSTANTINOVICH (Autor:in)
10.07.2015
Patent
Elektronische Ressource
Russisch
Dissolution Behavior of Submicron Biphasic Tricalcium Phosphate Powders
| British Library Online Contents | 2006
| British Library Online Contents | 2017
Tricalcium phosphate ceramics compexed with hydroxyapatite
| Tema Archiv | 1987
| British Library Online Contents | 2005
| British Library Online Contents | 2005