SINTERED BODY FROM ALPHA-ALUMINA FOR PRODUCING SAPPHIRE SINGLE CRYSTAL
FIELD: metallurgy.SUBSTANCE: invention relates to a technique for producing a sintered body from α-alumina as a raw material for further production of sapphire single crystals. Method comprises following steps: mixing 100 parts by weight α-alumina with 1-20 parts by weight α-alumina precursor to obtain a mixture, molding a compact from mixture and firing said compact to obtain a sintered body of α-alumina, wherein α-alumina has a specific surface area equal to 1-20 m/g, a moisture content less than 0.5 %, purity of 99.99 wt.% or more and content of each of Si, Na, Ca, Fe, Cu and Mg, equal to 10 ppm or less, α-alumina precursor has a specific surface area of 50 m/g or more, moisture content of 0.5 % or more, purity of 99.99 wt.% or more and content of each of Si, Na, Ca, Fe, Cu and Mg, equal to 10 ppm or less, at a pressing pressure of 20-400 MPa, firing is conducted at a temperature of 1,200-1,700 °C for 0.5-24 hours and rate of temperature rise of 30-500 °C/h. Invention enables to obtain a body having a relative density of 60 % or more, a closed porosity of 10 % or less, purity of 99.99 wt.% or more, content of each of Si, Na, Ca, Fe, Cu and Mg equal to 10 ppm or less, and volume of 1 cmor more.EFFECT: bodies with said characteristics have high mechanical strength and allow easy production of a high quality sapphire single crystal with less coloring and cracking and high volumetric efficiency.6 cl, 1 dwg, 4 tbl, 3 ex
Изобретение относится к технологии производства спеченной заготовки из α-оксида алюминия в качестве исходного сырья для дальнейшего получения из нее монокристаллов сапфира. Способ включает следующие стадии: смешивание 100 вес.ч. α-оксида алюминия с 1-20 вес.ч. предшественника α-оксида алюминия для получения смеси, формование прессовки из полученной смеси и обжиг прессовки для получения спеченной заготовки из α-оксида алюминия, при этом α-оксид алюминия имеет площадь удельной поверхности, равную 1-20 м/г, содержание влаги - менее 0,5%, чистоту - 99,99% вес. или более и содержание каждого из Si, Na, Ca, Fe, Cu и Mg, равное 10 ч./млн или менее, предшественник α-оксида алюминия имеет площадь удельной поверхности, равную 50 м/г или более, содержание влаги - 0,5% или более, чистоту - 99,99% вес. или более и содержание каждого из Si, Na, Ca, Fe, Cu и Mg, равное 10 ч./млн или менее, при давлении прессования 20-400 МПа, обжиг ведут при температуре 1200-1700°C в течение времени 0,5-24 часа и скорости повышения температуры 30-500°C/ч. Изобретение позволяет получать заготовки с относительной плотностью 60% или более, закрытой пористостью - 10% или менее, чистотой - 99,99% вес. или более, содержанием каждого из Si, Na, Ca, Fe, Cu и Mg 10 ч./млн или менее, объем - 1 смили более. Заготовки с такими характеристиками имеют высокую механическую прочность и обеспечивают легкое получение высококачественного монокристалла сапфира с меньшей степенью окрашивания и растрескивания и с высокой объемной производительностью. 2 н. и 4 з.п. ф-лы, 1 ил., 4 табл., 3 пр.
SINTERED BODY FROM ALPHA-ALUMINA FOR PRODUCING SAPPHIRE SINGLE CRYSTAL
FIELD: metallurgy.SUBSTANCE: invention relates to a technique for producing a sintered body from α-alumina as a raw material for further production of sapphire single crystals. Method comprises following steps: mixing 100 parts by weight α-alumina with 1-20 parts by weight α-alumina precursor to obtain a mixture, molding a compact from mixture and firing said compact to obtain a sintered body of α-alumina, wherein α-alumina has a specific surface area equal to 1-20 m/g, a moisture content less than 0.5 %, purity of 99.99 wt.% or more and content of each of Si, Na, Ca, Fe, Cu and Mg, equal to 10 ppm or less, α-alumina precursor has a specific surface area of 50 m/g or more, moisture content of 0.5 % or more, purity of 99.99 wt.% or more and content of each of Si, Na, Ca, Fe, Cu and Mg, equal to 10 ppm or less, at a pressing pressure of 20-400 MPa, firing is conducted at a temperature of 1,200-1,700 °C for 0.5-24 hours and rate of temperature rise of 30-500 °C/h. Invention enables to obtain a body having a relative density of 60 % or more, a closed porosity of 10 % or less, purity of 99.99 wt.% or more, content of each of Si, Na, Ca, Fe, Cu and Mg equal to 10 ppm or less, and volume of 1 cmor more.EFFECT: bodies with said characteristics have high mechanical strength and allow easy production of a high quality sapphire single crystal with less coloring and cracking and high volumetric efficiency.6 cl, 1 dwg, 4 tbl, 3 ex
Изобретение относится к технологии производства спеченной заготовки из α-оксида алюминия в качестве исходного сырья для дальнейшего получения из нее монокристаллов сапфира. Способ включает следующие стадии: смешивание 100 вес.ч. α-оксида алюминия с 1-20 вес.ч. предшественника α-оксида алюминия для получения смеси, формование прессовки из полученной смеси и обжиг прессовки для получения спеченной заготовки из α-оксида алюминия, при этом α-оксид алюминия имеет площадь удельной поверхности, равную 1-20 м/г, содержание влаги - менее 0,5%, чистоту - 99,99% вес. или более и содержание каждого из Si, Na, Ca, Fe, Cu и Mg, равное 10 ч./млн или менее, предшественник α-оксида алюминия имеет площадь удельной поверхности, равную 50 м/г или более, содержание влаги - 0,5% или более, чистоту - 99,99% вес. или более и содержание каждого из Si, Na, Ca, Fe, Cu и Mg, равное 10 ч./млн или менее, при давлении прессования 20-400 МПа, обжиг ведут при температуре 1200-1700°C в течение времени 0,5-24 часа и скорости повышения температуры 30-500°C/ч. Изобретение позволяет получать заготовки с относительной плотностью 60% или более, закрытой пористостью - 10% или менее, чистотой - 99,99% вес. или более, содержанием каждого из Si, Na, Ca, Fe, Cu и Mg 10 ч./млн или менее, объем - 1 смили более. Заготовки с такими характеристиками имеют высокую механическую прочность и обеспечивают легкое получение высококачественного монокристалла сапфира с меньшей степенью окрашивания и растрескивания и с высокой объемной производительностью. 2 н. и 4 з.п. ф-лы, 1 ил., 4 табл., 3 пр.
SINTERED BODY FROM ALPHA-ALUMINA FOR PRODUCING SAPPHIRE SINGLE CRYSTAL
СПЕЧЕННАЯ ЗАГОТОВКА ИЗ АЛЬФА-ОКСИДА АЛЮМИНИЯ ДЛЯ ПОЛУЧЕНИЯ МОНОКРИСТАЛЛА САПФИРА
OZAKI KHIROTAKA (Autor:in) / FUDZIVARA SINDZI (Autor:in)
10.04.2016
Patent
Elektronische Ressource
Russisch
IPC:
C30B
SINGLE-CRYSTAL GROWTH
,
Züchten von Einkristallen
/
C01F
COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
,
Verbindungen der Metalle Beryllium, Magnesium, Aluminium, Calcium, Strontium, Barium, Radium, Thorium oder der Seltenen Erden
/
C04B
Kalk
,
LIME
α-ALUMINA SINTERED BODY FOR PRODUCTION OF SAPPHIRE SINGLE CRYSTAL
| Europäisches Patentamt | 2015
METHOD FOR PRODUCING ALUMINA SINTERED BODY AND ALUMINA SINTERED BODY
| Europäisches Patentamt | 2021
METHOD FOR PRODUCING ALUMINA SINTERED BODY AND ALUMINA SINTERED BODY
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2023