METHOD OF PRODUCING FERROELECTRIC CERAMIC MATERIAL BASED ON BISMUTH FERRITE
FIELD: manufacturing technology.SUBSTANCE: invention relates to production of ferroelectric ceramic materials based on bismuth ferrite and can be used for creation of new materials used in devices for recording, storing and processing information. One prepares a suspension of initial oxides for producing solid solutions of BiAFeO, where A is a rare-earth element, x=0-0.20, and performs mechanical activation in planetary ball mill for 10-20 minutes. Then single-step synthesis at temperature of 800°C for two hours with cooling in furnace to room temperature, additional mechanical activation of generated product in ball planet mill for 10-20 minutes, tempering at 800-900°C with intermediate holding of generated product at temperature of 100-150°C lower than hardening temperature for 40-80 minutes.EFFECT: lower relative permittivity to values less than 120 at room temperature and higher stability of relative permittivity by reducing the amount of impurities and reducing the number of non-equilibrium defects in ceramics.2 cl, 2 tbl, 6 dwg
Изобретение относится к технологии производства сегнетоэлектрических керамических материалов на основе феррита висмута и может быть использовано для создания новых материалов, применяемых в устройствах записи, хранения и обработки информации. Технический результат - снижение относительной диэлектрической проницаемости до значений менее 120 при комнатной температуре и повышение стабильности относительной диэлектрической проницаемости за счет снижения количества примесей и уменьшения количества неравновесных дефектов в керамике. Для этого приготавливают навески исходных оксидов для получения твердых растворов BiAFeO, где A - редкоземельный элемент, x=0-0,20, и проводят механоактивацию в шаровой планетарной мельнице в течение 10-20 минут. Затем - одностадийный синтез при температуре 800°C в течение двух часов с охлаждением в печи до комнатной температуры, дополнительную механоактивацию синтезированного продукта в шаровой планетарной мельнице в течение 10-20 минут, закалку при 800-900°С с промежуточной выдержкой синтезированного продукта при температуре на 100-150°C ниже температуры закалки в течение 40-80 минут. 1 з.п. ф-лы, 2 табл. 6 ил.
METHOD OF PRODUCING FERROELECTRIC CERAMIC MATERIAL BASED ON BISMUTH FERRITE
FIELD: manufacturing technology.SUBSTANCE: invention relates to production of ferroelectric ceramic materials based on bismuth ferrite and can be used for creation of new materials used in devices for recording, storing and processing information. One prepares a suspension of initial oxides for producing solid solutions of BiAFeO, where A is a rare-earth element, x=0-0.20, and performs mechanical activation in planetary ball mill for 10-20 minutes. Then single-step synthesis at temperature of 800°C for two hours with cooling in furnace to room temperature, additional mechanical activation of generated product in ball planet mill for 10-20 minutes, tempering at 800-900°C with intermediate holding of generated product at temperature of 100-150°C lower than hardening temperature for 40-80 minutes.EFFECT: lower relative permittivity to values less than 120 at room temperature and higher stability of relative permittivity by reducing the amount of impurities and reducing the number of non-equilibrium defects in ceramics.2 cl, 2 tbl, 6 dwg
Изобретение относится к технологии производства сегнетоэлектрических керамических материалов на основе феррита висмута и может быть использовано для создания новых материалов, применяемых в устройствах записи, хранения и обработки информации. Технический результат - снижение относительной диэлектрической проницаемости до значений менее 120 при комнатной температуре и повышение стабильности относительной диэлектрической проницаемости за счет снижения количества примесей и уменьшения количества неравновесных дефектов в керамике. Для этого приготавливают навески исходных оксидов для получения твердых растворов BiAFeO, где A - редкоземельный элемент, x=0-0,20, и проводят механоактивацию в шаровой планетарной мельнице в течение 10-20 минут. Затем - одностадийный синтез при температуре 800°C в течение двух часов с охлаждением в печи до комнатной температуры, дополнительную механоактивацию синтезированного продукта в шаровой планетарной мельнице в течение 10-20 минут, закалку при 800-900°С с промежуточной выдержкой синтезированного продукта при температуре на 100-150°C ниже температуры закалки в течение 40-80 минут. 1 з.п. ф-лы, 2 табл. 6 ил.
METHOD OF PRODUCING FERROELECTRIC CERAMIC MATERIAL BASED ON BISMUTH FERRITE
СПОСОБ ИЗГОТОВЛЕНИЯ СЕГНЕТОЭЛЕКТРИЧЕСКОГО КЕРАМИЧЕСКОГО МАТЕРИАЛА НА ОСНОВЕ ФЕРРИТА ВИСМУТА
REZNICHENKO LARISA ANDREEVNA (Autor:in) / VERBENKO ILJA ALEKSANDROVICH (Autor:in) / MILLER ALEKSANDR IVANOVICH (Autor:in) / TITOV SERGEJ VALEREVICH (Autor:in) / ABUBAKAROV ABU GELANIEVICH (Autor:in)
10.04.2016
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2023
Lead-free bismuth ferrite-based ceramic material and preparation method thereof
| Europäisches Patentamt | 2020
Bismuth ferrite-based leadless piezoelectric ceramic material and preparation method thereof
| Europäisches Patentamt | 2023