REFRACTORY CERAMIC MIXTURE AND BRICK MADE THEREFROM
FIELD: metallurgy.SUBSTANCE: invention relates to refractory ceramic mixture, as well as to refractory ceramic brick made therefrom, and can be used for lining of cement rotary furnaces. Refractory ceramic mixture has following composition: a) 75-98 wt%, at least main initial material from group: sintered magnesium oxide, magnesium oxide, b) oxide 2-25 wt% at least granular aggregate from group: silicon carbide, silicon nitride, silicon oxycarbide, silicon oxycarbonitride, c) maximum 5 wt% of other components, each time in terms of total mixture, main initial material is in range of 10-40 wt% in grinding fraction < 125 mcm, in terms of total mixture and granular aggregate is in granulometric fraction > 125 mcm and < 2 mm. Refractory ceramic brick made from said mixture by pressing and roasting is characterised by that in it granular aggregate maximum is half-sintered with main raw material.EFFECT: technical result of invention is obtaining articles with fire resistance higher than 1,400 °C, high resistance to corrosion and effective structural elasticity.12 cl, 3 ex, 2 tbl
Изобретение относится к огнеупорной керамической шихте, а также к образованному из нее огнеупорному керамическому кирпичу, и может быть использовано для облицовки цементных вращающихся печей. Огнеупорная керамическая шихта имеет состав: a) 75-98 мас.%, по меньшей мере, основного исходного материала из группы: спеченная окись магния, плавленая окись магния, b) 2-25 мас.%, по меньшей мере, зернистого заполнителя из группы: карбид кремния, нитрид кремния, оксикарбид кремния, оксикарбонитрид кремния, c) максимально 5 мас. % других составных частей, каждый раз в пересчете на общую шихту, причем основный исходный материал находится на 10-40 мас.% во фракции помола <125 мкм, в пересчете на общую шихту, а зернистый заполнитель находится в гранулометрической фракции >125 мкм и <2 мм. Огнеупорный керамический кирпич, полученный из этой шихты путём прессования и обжига, характеризуется тем, что в нём зернистый заполнитель максимум наполовину спекается с основным исходным материалом. Технический результат изобретения - получение изделий с огнеупорностью выше 1400°С, высокой стойкостью к коррозии и выгодной структурной эластичностью. 2 н. и 10 з.п. ф-лы, 3 пр., 2 табл.
REFRACTORY CERAMIC MIXTURE AND BRICK MADE THEREFROM
FIELD: metallurgy.SUBSTANCE: invention relates to refractory ceramic mixture, as well as to refractory ceramic brick made therefrom, and can be used for lining of cement rotary furnaces. Refractory ceramic mixture has following composition: a) 75-98 wt%, at least main initial material from group: sintered magnesium oxide, magnesium oxide, b) oxide 2-25 wt% at least granular aggregate from group: silicon carbide, silicon nitride, silicon oxycarbide, silicon oxycarbonitride, c) maximum 5 wt% of other components, each time in terms of total mixture, main initial material is in range of 10-40 wt% in grinding fraction < 125 mcm, in terms of total mixture and granular aggregate is in granulometric fraction > 125 mcm and < 2 mm. Refractory ceramic brick made from said mixture by pressing and roasting is characterised by that in it granular aggregate maximum is half-sintered with main raw material.EFFECT: technical result of invention is obtaining articles with fire resistance higher than 1,400 °C, high resistance to corrosion and effective structural elasticity.12 cl, 3 ex, 2 tbl
Изобретение относится к огнеупорной керамической шихте, а также к образованному из нее огнеупорному керамическому кирпичу, и может быть использовано для облицовки цементных вращающихся печей. Огнеупорная керамическая шихта имеет состав: a) 75-98 мас.%, по меньшей мере, основного исходного материала из группы: спеченная окись магния, плавленая окись магния, b) 2-25 мас.%, по меньшей мере, зернистого заполнителя из группы: карбид кремния, нитрид кремния, оксикарбид кремния, оксикарбонитрид кремния, c) максимально 5 мас. % других составных частей, каждый раз в пересчете на общую шихту, причем основный исходный материал находится на 10-40 мас.% во фракции помола <125 мкм, в пересчете на общую шихту, а зернистый заполнитель находится в гранулометрической фракции >125 мкм и <2 мм. Огнеупорный керамический кирпич, полученный из этой шихты путём прессования и обжига, характеризуется тем, что в нём зернистый заполнитель максимум наполовину спекается с основным исходным материалом. Технический результат изобретения - получение изделий с огнеупорностью выше 1400°С, высокой стойкостью к коррозии и выгодной структурной эластичностью. 2 н. и 10 з.п. ф-лы, 3 пр., 2 табл.
REFRACTORY CERAMIC MIXTURE AND BRICK MADE THEREFROM
ОГНЕУПОРНАЯ КЕРАМИЧЕСКАЯ ШИХТА И ОБРАЗОВАННЫЙ ИЗ НЕЕ КИРПИЧ