POROUS SILICA-BASED MATERIAL AND PORTLANDITE FOR FILLING INSULATING BRICK WITH CONTROLLED STRUCTURE AND CORRESPONDING PRODUCTION METHOD
FIELD: construction.SUBSTANCE: present invention relates to a method for preparing a porous material containing silica and calcium hydroxide. Method for preparing a porous material containing 25 wt% to 75 wt% of silica and from 75 wt% to 25 wt% of calcium hydroxide comprises the following successive steps: a step synthesising quicklime, a step of mixing the quicklime obtained in the previous step, water and silica according to a molar ratio of CaO/SiOof between 0.8 to 1.2, and a weight ratio of water/(CaO+SiO) of between 2 to 60; a step of hydrothermal synthesis at a saturation water-vapour pressure of higher than or equal to 10Pa (1 bar) and lower or equal to 3×10Pa (3 bar) and at a temperature higher than or equal to 80 °C and lower than 150 °C, a step of drying the ceramic body obtained at a temperature of 100-450 °C.EFFECT: production of highly insulating building bricks.15 cl, 2 tbl, 7 dwg
Изобретение относится к способу получения пористой кремниево-известковой структуры, а также ее использование в производстве строительного кирпича с высокой изоляционной способностью. Способ получения пористого материала, содержащего от 25% мас. до 75% мас. кремнезема и от 75% мас. до 25% мас. гидроксида кальция, включает в себя следующие последовательные стадии: синтез негашеной извести, далее смешивание указанной негашеной извести, полученной на стадии синтеза извести, воды и кремнезема в молярном отношении СаО/SiOот 0,8 до 1,2, и массовое отношение вода/(СаО+SiO) составляет от 2 до 60; гидротермальный синтез под давлением насыщенного водяного пара, выше или равном 10Па (1 бар) и ниже и равном 3×10Па (3 бар), и при температуре, выше или равной 80°С и ниже 150°С, затем сушка указанной керамической массы при температуре от 100 до 450°С. 6 н. и 9 з.п. ф-лы, 2 табл., 7 ил.
POROUS SILICA-BASED MATERIAL AND PORTLANDITE FOR FILLING INSULATING BRICK WITH CONTROLLED STRUCTURE AND CORRESPONDING PRODUCTION METHOD
FIELD: construction.SUBSTANCE: present invention relates to a method for preparing a porous material containing silica and calcium hydroxide. Method for preparing a porous material containing 25 wt% to 75 wt% of silica and from 75 wt% to 25 wt% of calcium hydroxide comprises the following successive steps: a step synthesising quicklime, a step of mixing the quicklime obtained in the previous step, water and silica according to a molar ratio of CaO/SiOof between 0.8 to 1.2, and a weight ratio of water/(CaO+SiO) of between 2 to 60; a step of hydrothermal synthesis at a saturation water-vapour pressure of higher than or equal to 10Pa (1 bar) and lower or equal to 3×10Pa (3 bar) and at a temperature higher than or equal to 80 °C and lower than 150 °C, a step of drying the ceramic body obtained at a temperature of 100-450 °C.EFFECT: production of highly insulating building bricks.15 cl, 2 tbl, 7 dwg
Изобретение относится к способу получения пористой кремниево-известковой структуры, а также ее использование в производстве строительного кирпича с высокой изоляционной способностью. Способ получения пористого материала, содержащего от 25% мас. до 75% мас. кремнезема и от 75% мас. до 25% мас. гидроксида кальция, включает в себя следующие последовательные стадии: синтез негашеной извести, далее смешивание указанной негашеной извести, полученной на стадии синтеза извести, воды и кремнезема в молярном отношении СаО/SiOот 0,8 до 1,2, и массовое отношение вода/(СаО+SiO) составляет от 2 до 60; гидротермальный синтез под давлением насыщенного водяного пара, выше или равном 10Па (1 бар) и ниже и равном 3×10Па (3 бар), и при температуре, выше или равной 80°С и ниже 150°С, затем сушка указанной керамической массы при температуре от 100 до 450°С. 6 н. и 9 з.п. ф-лы, 2 табл., 7 ил.
POROUS SILICA-BASED MATERIAL AND PORTLANDITE FOR FILLING INSULATING BRICK WITH CONTROLLED STRUCTURE AND CORRESPONDING PRODUCTION METHOD
ПОРИСТЫЙ МАТЕРИАЛ НА ОСНОВЕ КРЕМНЕЗЕМА И ПОРТЛАНДИТА ДЛЯ ЗАПОЛНЕНИЯ ИЗОЛИРУЮЩЕГО КИРПИЧА С КОНТРОЛИРУЕМОЙ СТРУКТУРОЙ И СООТВЕТСТВУЮЩИЙ СПОСОБ ПОЛУЧЕНИЯ
DEL-GALLO PASKAL (Autor:in) / KANTONNE ZHEROM (Autor:in)
27.07.2016
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME