METHODS OF INCREASING CONCRETE STRENGTH AT COMPRESSION USING NANOSILICA OBTAINED FROM HYDROTHERMAL SOLUTION
FIELD: construction.SUBSTANCE: invention relates to a composition of high-strength concrete and can be used for making articles in civil and industrial construction, as well as for building facilities of special purpose. Method is based on silica nanoparticles influence on the rate of calcium silicate hydration reactions, on calcium silicate hydrates gel structure, and, finally, on mechanical properties of concretes. To form silica nanoparticles in a hydrothermal solution polycondensation of molecules of orthosilicic acid (OSA) is performed supplied when dissolving aluminosilicate minerals of rocks under conditions of high pressure and temperature in the entrails of deposits. Nanoparticles produced after completion of the polycondensation of OSA are concentrated with the use of ultrafiltration membrane filters. Stable aqueous sol is mixed with a super plasticizer and introduced in the tempering water at the nanosilica doses by cement of 0.01-2.0 wt% and the super plasticizer doses by cement of 0.0-1.0 wt%, the tempering water is mixed with liquid additives of the sol and the super plasticizer and cement-sand is added into the system with the W/C ratio from 0.71 to 0.25, the cement-sand mix is mixed with the tempering water.EFFECT: technical result is acceleration of hardening and higher compression strength at the design age.1 cl, 2 dwg, 6 tbl
Изобретение относится к составу высокопрочного бетона и может быть использовано для изготовления изделий в гражданском и промышленном строительстве, а также при возведении сооружений специального назначения. Технический результат заключается в ускорении твердения и повышении прочности при сжатии в проектном возрасте. Способ основан на влиянии наночастиц кремнезема на скорость реакций гидратации силикатов кальция, на структуру геля гидратов силикатов кальция, и, в конечном итоге, на механические характеристики бетонов. Для формирования наночастиц кремнезема в гидротермальном растворе проводят поликонденсацию молекул ортокремниевой кислоты (ОКК), поступающей при растворении алюмосиликатных минералов пород в условиях повышенных давлений и температур в недрах месторождений. Наночастицы, образующиеся после завершения поликонденсации ОКК, концентрируют с применением ультрафильтрационных мембранных фильтров. Стабильный водный золь перемешивают с суперпластификатором и вводят в воду затворения при дозах нанокремнезема по цементу 0,01-2,0 масс.% и дозах суперпластификатора по цементу 0,0-1,0 масс.%, перемешивают воду затворения с жидкими добавками золя и суперпластификатора и добавляют в систему цемент-песок при В/Ц от 0,71 до 0,25, перемешивают цементно-песчаную смесь с водой затворения. 2 ил., 6 табл.
METHODS OF INCREASING CONCRETE STRENGTH AT COMPRESSION USING NANOSILICA OBTAINED FROM HYDROTHERMAL SOLUTION
FIELD: construction.SUBSTANCE: invention relates to a composition of high-strength concrete and can be used for making articles in civil and industrial construction, as well as for building facilities of special purpose. Method is based on silica nanoparticles influence on the rate of calcium silicate hydration reactions, on calcium silicate hydrates gel structure, and, finally, on mechanical properties of concretes. To form silica nanoparticles in a hydrothermal solution polycondensation of molecules of orthosilicic acid (OSA) is performed supplied when dissolving aluminosilicate minerals of rocks under conditions of high pressure and temperature in the entrails of deposits. Nanoparticles produced after completion of the polycondensation of OSA are concentrated with the use of ultrafiltration membrane filters. Stable aqueous sol is mixed with a super plasticizer and introduced in the tempering water at the nanosilica doses by cement of 0.01-2.0 wt% and the super plasticizer doses by cement of 0.0-1.0 wt%, the tempering water is mixed with liquid additives of the sol and the super plasticizer and cement-sand is added into the system with the W/C ratio from 0.71 to 0.25, the cement-sand mix is mixed with the tempering water.EFFECT: technical result is acceleration of hardening and higher compression strength at the design age.1 cl, 2 dwg, 6 tbl
Изобретение относится к составу высокопрочного бетона и может быть использовано для изготовления изделий в гражданском и промышленном строительстве, а также при возведении сооружений специального назначения. Технический результат заключается в ускорении твердения и повышении прочности при сжатии в проектном возрасте. Способ основан на влиянии наночастиц кремнезема на скорость реакций гидратации силикатов кальция, на структуру геля гидратов силикатов кальция, и, в конечном итоге, на механические характеристики бетонов. Для формирования наночастиц кремнезема в гидротермальном растворе проводят поликонденсацию молекул ортокремниевой кислоты (ОКК), поступающей при растворении алюмосиликатных минералов пород в условиях повышенных давлений и температур в недрах месторождений. Наночастицы, образующиеся после завершения поликонденсации ОКК, концентрируют с применением ультрафильтрационных мембранных фильтров. Стабильный водный золь перемешивают с суперпластификатором и вводят в воду затворения при дозах нанокремнезема по цементу 0,01-2,0 масс.% и дозах суперпластификатора по цементу 0,0-1,0 масс.%, перемешивают воду затворения с жидкими добавками золя и суперпластификатора и добавляют в систему цемент-песок при В/Ц от 0,71 до 0,25, перемешивают цементно-песчаную смесь с водой затворения. 2 ил., 6 табл.
METHODS OF INCREASING CONCRETE STRENGTH AT COMPRESSION USING NANOSILICA OBTAINED FROM HYDROTHERMAL SOLUTION
СПОСОБЫ ПОВЫШЕНИЯ ПРОЧНОСТИ БЕТОНА ПРИ СЖАТИИ С ИСПОЛЬЗОВАНИЕМ НАНОКРЕМНЕЗЁМА, ПОЛУЧЕННОГО ИЗ ГИДРОТЕРМАЛЬНОГО РАСТВОРА
POTAPOV VADIM VLADIMIROVICH (Autor:in) / KASHUTIN ALEKSANDR NIKOLAEVICH (Autor:in)
10.10.2016
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
/
B82B
Nanostrukturen, gestaltet durch die Manipulation von einzelnen Atomen, Molekülen, oder einer begrenzten Ansammlung von Atomen oder Molekülen als einzelne Einheiten
,
NANOSTRUCTURES FORMED BY MANIPULATION OF INDIVIDUAL ATOMS, MOLECULES, OR LIMITED COLLECTIONS OF ATOMS OR MOLECULES AS DISCRETE UNITS
SP-326—15 Hardening of Concrete with Hydrothermal Nanosilica
| TIBKAT | 2019
The Formation of Microstructure in High Strength Concrete Containing Micro and Nanosilica
| Trans Tech Publications | 2014