METHOD OF PRODUCING HIGH-STRENGTH GYPSUM
FIELD: technological processes.SUBSTANCE: present invention relates to method of producing high-strength gypsum by boiling in liquid mediums at atmospheric pressure. Method includes preliminary mechanical activation of gypsum dihydrate and subsequent treatment of activated gypsum dihydrate with water at temperature of 97–100 °C during 4 hours, wherein calcium sulphate dihydrate is subjected to subsequent processing, in which amount of stored energy corresponding to change of interplanar distances of crystal lattice is at least 312 kJ/mol and total amount of energy corresponding to change of surface area of coherent scattering and microdeformations is in range of 5.6–5.8 kJ/mol.EFFECT: technical result consists in highest degree of conversion of gypsum dihydrate, effective pretreatment of gypsum dihydrate before boiling.5 cl, 1 tbl
Настоящее изобретение относится к способу получения высокопрочного гипса варкой в жидких средах при атмосферном давлении. Технический результат заключается в наибольшей степени конверсии двуводного гипса, эффективной предварительной обработке двуводного гипса перед варкой. Способ включает предварительную механическую активацию двуводного гипса и последующую обработку активированного двуводного гипса водой при температурах 97-100°C в течение 4 часов, причем последующей обработке подвергают двуводный гипс, в котором количество запасенной энергии, соответствующее изменению межплоскостных расстояний кристаллической решетки, не менее 312 кДж/моль и суммарное количество энергии, соответствующее изменению поверхности областей когерентного рассеяния и микродеформаций, в диапазоне от 5,6 до 5,8 кДж/моль. 4 з.п. ф-лы, 1 табл.
METHOD OF PRODUCING HIGH-STRENGTH GYPSUM
FIELD: technological processes.SUBSTANCE: present invention relates to method of producing high-strength gypsum by boiling in liquid mediums at atmospheric pressure. Method includes preliminary mechanical activation of gypsum dihydrate and subsequent treatment of activated gypsum dihydrate with water at temperature of 97–100 °C during 4 hours, wherein calcium sulphate dihydrate is subjected to subsequent processing, in which amount of stored energy corresponding to change of interplanar distances of crystal lattice is at least 312 kJ/mol and total amount of energy corresponding to change of surface area of coherent scattering and microdeformations is in range of 5.6–5.8 kJ/mol.EFFECT: technical result consists in highest degree of conversion of gypsum dihydrate, effective pretreatment of gypsum dihydrate before boiling.5 cl, 1 tbl
Настоящее изобретение относится к способу получения высокопрочного гипса варкой в жидких средах при атмосферном давлении. Технический результат заключается в наибольшей степени конверсии двуводного гипса, эффективной предварительной обработке двуводного гипса перед варкой. Способ включает предварительную механическую активацию двуводного гипса и последующую обработку активированного двуводного гипса водой при температурах 97-100°C в течение 4 часов, причем последующей обработке подвергают двуводный гипс, в котором количество запасенной энергии, соответствующее изменению межплоскостных расстояний кристаллической решетки, не менее 312 кДж/моль и суммарное количество энергии, соответствующее изменению поверхности областей когерентного рассеяния и микродеформаций, в диапазоне от 5,6 до 5,8 кДж/моль. 4 з.п. ф-лы, 1 табл.
METHOD OF PRODUCING HIGH-STRENGTH GYPSUM
СПОСОБ ПОЛУЧЕНИЯ ВЫСОКОПРОЧНОГО ГИПСА
BOGATYREVA ELENA VLADIMIROVNA (Autor:in) / ERMILOV ALEKSANDR GERMANOVICH (Autor:in) / KUCHINA IRINA YUREVNA (Autor:in) / EVTUSHENKO ALEKSEJ VLADIMIROVICH (Autor:in)
16.03.2017
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
METHOD OF PRODUCING HIGH-STRENGTH GYPSUM WITH UNIFORM HEATING
| Europäisches Patentamt | 2020
Process for producing alpha high-strength gypsum powder by using industrial byproduct gypsum
| Europäisches Patentamt | 2021