COMPOSITION FOR MANUFACTURE OF EXPANDED AGGREGATE
FIELD: chemistry.SUBSTANCE: invention relates to production of construction materials, specifically to production of water glass-based expanded aggregates, intended for manufacture of lightweight concrete, and fill insulation materials. Composition for manufacture of the expanded aggregate comprises as follows, wt %: sodium water glass with a density of 1.41 g/cm50-75, sodium chloride, ground to a particle size below 0.3 mm 1-3, burnt rock, ground to a particle size below 0.14 mm 12-34, drill cuttings, ground to a particle size below 0.14 mm, and oxides, wt %: SiO- 26.2; AlO- 4.5; FeO- 5.6; CaO - 28.3; MgO - 1.2; RO - 0.8; ignition loss - 33.4, 10-15.EFFECT: composition for manufacture of expanded aggregates, with improved compression strength and softening temperature, industrial waste recycling.3 tbl
Изобретение относится к области производства строительных материалов, в частности к производству пористых заполнителей на основе жидкого стекла, предназначенных для изготовления легких бетонов, а также теплоизоляционных засыпок. Композиция для производства пористого заполнителя включает, мас.%: натриевое жидкое стекло плотностью 1,41 г/см50-75, хлорид натрия, размолотый до размера менее 0,3 мм 1-3, горелые породы, размолотые до прохода через сито 0,14 мм 12-34, буровой шлам, размолотый до прохода через сито 0,14 мм и с содержанием оксидов, мас.%: SiO- 26,2; AlO- 4,5; FeO- 5,6; СаО - 28,3; MgO - 1,2; RO - 0,8; п.п.п. - 33,4, 10-15. Технический результат – повышение прочности при сжатии и коэффициента размягчения пористого заполнителя, утилизация промышленных отходов. 3 табл.
COMPOSITION FOR MANUFACTURE OF EXPANDED AGGREGATE
FIELD: chemistry.SUBSTANCE: invention relates to production of construction materials, specifically to production of water glass-based expanded aggregates, intended for manufacture of lightweight concrete, and fill insulation materials. Composition for manufacture of the expanded aggregate comprises as follows, wt %: sodium water glass with a density of 1.41 g/cm50-75, sodium chloride, ground to a particle size below 0.3 mm 1-3, burnt rock, ground to a particle size below 0.14 mm 12-34, drill cuttings, ground to a particle size below 0.14 mm, and oxides, wt %: SiO- 26.2; AlO- 4.5; FeO- 5.6; CaO - 28.3; MgO - 1.2; RO - 0.8; ignition loss - 33.4, 10-15.EFFECT: composition for manufacture of expanded aggregates, with improved compression strength and softening temperature, industrial waste recycling.3 tbl
Изобретение относится к области производства строительных материалов, в частности к производству пористых заполнителей на основе жидкого стекла, предназначенных для изготовления легких бетонов, а также теплоизоляционных засыпок. Композиция для производства пористого заполнителя включает, мас.%: натриевое жидкое стекло плотностью 1,41 г/см50-75, хлорид натрия, размолотый до размера менее 0,3 мм 1-3, горелые породы, размолотые до прохода через сито 0,14 мм 12-34, буровой шлам, размолотый до прохода через сито 0,14 мм и с содержанием оксидов, мас.%: SiO- 26,2; AlO- 4,5; FeO- 5,6; СаО - 28,3; MgO - 1,2; RO - 0,8; п.п.п. - 33,4, 10-15. Технический результат – повышение прочности при сжатии и коэффициента размягчения пористого заполнителя, утилизация промышленных отходов. 3 табл.
COMPOSITION FOR MANUFACTURE OF EXPANDED AGGREGATE
Композиция для производства пористого заполнителя
ABDRAKHIMOVA ELENA SERGEEVNA (Autor:in)
24.03.2017
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
Expanded shale aggregate in prestressed concrete
Engineering Index Backfile | 1956
Expanded shale aggregate in structural concrete
| Engineering Index Backfile | 1951
Mechanical Durability of Expanded Shale Lightweight Aggregate
| British Library Online Contents | 1999