COMPOSITION ON THE BASIS OF HYDRATED CALCIUM SILICATE
FIELD: chemistry.SUBSTANCE: invention relates to a composition comprising 5-50% by weight of calcium silicate hydrate, 10-60% by weight of at least one water-soluble, including acidic polymer groups, containing polyester groups and 5-40% by weight of at least one polyalkylene glycol ether. Also a process for the preparation of this composition and cementitious mixtures comprising the composition is disclosed. It is a further object of the present invention to use the compositions of the invention in cementitious mixtures to accelerate the development of a long period of time for the dispersing action of the acid group-containing polymer after adding water for mixing and, accordingly, accelerated molding of the mixture. Invention is developed in dependent claims of the invention.EFFECT: technical result is the rapid curing of the cementitious composition.15 cl, 3 tbl
Изобретение относится к композиции, включающей 5-50 мас. % гидрата силиката кальция, 10-60 мас. % по меньшей мере одного водорастворимого, включающего кислотные группы полимера, содержащего полиэфирные группы, и 5-40 мас. % по меньшей мере одного полиалкиленгликолевого простого эфира. Также раскрыт способ получения этой композиции и цементирующих смесей, включающих композицию. Дополнительным объектом данного изобретения является применение композиций изобретения в цементирующих смесях для ускорения развития длительного периода времени диспергирующего действия включающего кислотные группы полимера после добавления воды для затворения и, соответственно, ускоренной формовки смеси. Изобретение развито в зависимых пунктах формулы изобретения. Технический результат - быстрое отверждение цементирующей композиции. 4 н. и 11 з.п. ф-лы, 3 табл.
COMPOSITION ON THE BASIS OF HYDRATED CALCIUM SILICATE
FIELD: chemistry.SUBSTANCE: invention relates to a composition comprising 5-50% by weight of calcium silicate hydrate, 10-60% by weight of at least one water-soluble, including acidic polymer groups, containing polyester groups and 5-40% by weight of at least one polyalkylene glycol ether. Also a process for the preparation of this composition and cementitious mixtures comprising the composition is disclosed. It is a further object of the present invention to use the compositions of the invention in cementitious mixtures to accelerate the development of a long period of time for the dispersing action of the acid group-containing polymer after adding water for mixing and, accordingly, accelerated molding of the mixture. Invention is developed in dependent claims of the invention.EFFECT: technical result is the rapid curing of the cementitious composition.15 cl, 3 tbl
Изобретение относится к композиции, включающей 5-50 мас. % гидрата силиката кальция, 10-60 мас. % по меньшей мере одного водорастворимого, включающего кислотные группы полимера, содержащего полиэфирные группы, и 5-40 мас. % по меньшей мере одного полиалкиленгликолевого простого эфира. Также раскрыт способ получения этой композиции и цементирующих смесей, включающих композицию. Дополнительным объектом данного изобретения является применение композиций изобретения в цементирующих смесях для ускорения развития длительного периода времени диспергирующего действия включающего кислотные группы полимера после добавления воды для затворения и, соответственно, ускоренной формовки смеси. Изобретение развито в зависимых пунктах формулы изобретения. Технический результат - быстрое отверждение цементирующей композиции. 4 н. и 11 з.п. ф-лы, 3 табл.
COMPOSITION ON THE BASIS OF HYDRATED CALCIUM SILICATE
КОМПОЗИЦИЯ НА ОСНОВЕ ГИДРАТА СИЛИКАТА КАЛЬЦИЯ
BIKHLER MANFRED (Autor:in) / GEDT TORBEN (Autor:in) / LOGES NIKLAS (Autor:in) / MAZANETS OLIVER (Autor:in) / KHESSE KRISTOF (Autor:in)
25.05.2018
Patent
Elektronische Ressource
Russisch
Composition for preparing hydrated calcium silicate material, and hydrated calcium silicate material
| Europäisches Patentamt | 2022
Caesium Immobilisation in Hydrated Calcium-Silicate-Aluminate Systems
| British Library Online Contents | 1998
Hydrated calcium silicate products other than hydraulic cements
| Engineering Index Backfile | 1964