METHOD OF MAKING CERAMICS BASED ON ZIRCONIUM DIOXIDE
FIELD: chemistry.SUBSTANCE: invention relates to a method of producing ceramics based on zirconium dioxide with a transformable tetragonal crystalline phase and can be used for making wear-resistant parts of a spherical shape, for example, as a milling bead. According to the invention, the base used is a baddeleyite concentrate which is preliminarily milled and mechanically activated by means of a wet high-energy grinding combined with a stabilizer (calcium oxide), a molding suspension is prepared, for which the prepared milling is placed into a mixing container, into which a dispersant, distilled water and aqueous solution of sodium alginate are added, followed by homogenisation of the molding suspension and its degassing. Weight fraction of the baddeleyt powder in the molding suspension ranges from 40 to 60 wt. %, sodium alginate 0.6–1.6 wt. %. Suspension by metering piston device through calibrated nozzle in form of drops is introduced into solution of hardener 1–10 wt. % aqueous solution of calcium chloride, which is held for at least 5 minutes. Balls are extracted from calcium chloride solution, washed in distilled water, dried on filter paper at room temperature throughout the day. Then, the beads are placed in a high-temperature muffle furnace and sintered in an air atmosphere for 4 hours at temperature of 1250–1400 °C with heating rate of 180–300 °C/h, followed by cooling at rate of 180–300 °C/h to temperature 140 °C.EFFECT: by its mechanical properties obtained baddeleyite ceramics is not inferior to engineering ceramics from chemically precipitated ZrO, synthesized from zircon.5 cl, 4 tbl, 8 dwg
Изобретение относится к способу получения керамики на основе диоксида циркония с трансформируемой тетрагональной кристаллической фазой и может быть использовано для изготовления износостойких деталей сферической формы, например, в качестве мелющего бисера. Согласно изобретению в качестве основы используют бадделеитовый концентрат, который предварительно измельчают и механоактивируют путем совместного со стабилизатором (оксидом кальция) мокрого высокоэнергетического помола готовят формовочную суспензию, для чего приготовленный помол помещают в смесительную емкость, в которую добавляют диспергатор, дистиллированную воду и водный раствор альгината натрия, затем проводят гомогенизацию формовочной суспензии и ее дегазацию. Массовая доля бадделеитового порошка в формовочной суспензии составляет от 40 до 60 мас.%, альгината натрия 0,6-1,6 мас.%. Суспензию дозирующим поршневым устройством через калиброванную дюзу в виде капель вводят в раствор отвердителя 1-10 мас.% водного раствора хлорида кальция, в котором выдерживают в течение не менее 5 мин. Шарики извлекают из раствора хлорида кальция, промывают в дистиллированной воде, сушат на фильтровальной бумаге при комнатной температуре на протяжении суток. Далее бисер помещают в высокотемпературную муфельную печь и спекают в воздушной атмосфере в течение 4 ч при температуре 1250-1400°C со скоростью нагрева 180-300°C/ч, после чего производят охлаждение со скоростью 180-300°C/ч до температуры 140°C. По своим механическим свойствам полученная бадделеитовая керамика не уступает инженерной керамике из химически преципитированного ZrO, синтезированного из циркона. 4 з.п. ф-лы, 4 табл., 8 ил.
METHOD OF MAKING CERAMICS BASED ON ZIRCONIUM DIOXIDE
FIELD: chemistry.SUBSTANCE: invention relates to a method of producing ceramics based on zirconium dioxide with a transformable tetragonal crystalline phase and can be used for making wear-resistant parts of a spherical shape, for example, as a milling bead. According to the invention, the base used is a baddeleyite concentrate which is preliminarily milled and mechanically activated by means of a wet high-energy grinding combined with a stabilizer (calcium oxide), a molding suspension is prepared, for which the prepared milling is placed into a mixing container, into which a dispersant, distilled water and aqueous solution of sodium alginate are added, followed by homogenisation of the molding suspension and its degassing. Weight fraction of the baddeleyt powder in the molding suspension ranges from 40 to 60 wt. %, sodium alginate 0.6–1.6 wt. %. Suspension by metering piston device through calibrated nozzle in form of drops is introduced into solution of hardener 1–10 wt. % aqueous solution of calcium chloride, which is held for at least 5 minutes. Balls are extracted from calcium chloride solution, washed in distilled water, dried on filter paper at room temperature throughout the day. Then, the beads are placed in a high-temperature muffle furnace and sintered in an air atmosphere for 4 hours at temperature of 1250–1400 °C with heating rate of 180–300 °C/h, followed by cooling at rate of 180–300 °C/h to temperature 140 °C.EFFECT: by its mechanical properties obtained baddeleyite ceramics is not inferior to engineering ceramics from chemically precipitated ZrO, synthesized from zircon.5 cl, 4 tbl, 8 dwg
Изобретение относится к способу получения керамики на основе диоксида циркония с трансформируемой тетрагональной кристаллической фазой и может быть использовано для изготовления износостойких деталей сферической формы, например, в качестве мелющего бисера. Согласно изобретению в качестве основы используют бадделеитовый концентрат, который предварительно измельчают и механоактивируют путем совместного со стабилизатором (оксидом кальция) мокрого высокоэнергетического помола готовят формовочную суспензию, для чего приготовленный помол помещают в смесительную емкость, в которую добавляют диспергатор, дистиллированную воду и водный раствор альгината натрия, затем проводят гомогенизацию формовочной суспензии и ее дегазацию. Массовая доля бадделеитового порошка в формовочной суспензии составляет от 40 до 60 мас.%, альгината натрия 0,6-1,6 мас.%. Суспензию дозирующим поршневым устройством через калиброванную дюзу в виде капель вводят в раствор отвердителя 1-10 мас.% водного раствора хлорида кальция, в котором выдерживают в течение не менее 5 мин. Шарики извлекают из раствора хлорида кальция, промывают в дистиллированной воде, сушат на фильтровальной бумаге при комнатной температуре на протяжении суток. Далее бисер помещают в высокотемпературную муфельную печь и спекают в воздушной атмосфере в течение 4 ч при температуре 1250-1400°C со скоростью нагрева 180-300°C/ч, после чего производят охлаждение со скоростью 180-300°C/ч до температуры 140°C. По своим механическим свойствам полученная бадделеитовая керамика не уступает инженерной керамике из химически преципитированного ZrO, синтезированного из циркона. 4 з.п. ф-лы, 4 табл., 8 ил.
METHOD OF MAKING CERAMICS BASED ON ZIRCONIUM DIOXIDE
СПОСОБ ИЗГОТОВЛЕНИЯ КЕРАМИКИ НА ОСНОВЕ ДИОКСИДА ЦИРКОНИЯ
RODAEV VYACHESLAV VALEREVICH (Autor:in) / ZHIGACHEV ANDREJ OLEGOVICH (Autor:in) / PIROZHKOVA TATYANA SERGEEVNA (Autor:in) / GOLOVIN YURIJ IVANOVICH (Autor:in)
30.08.2019
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
METHOD FOR PRODUCING BIOACTIVE CERAMICS BASED ON ZIRCONIUM DIOXIDE
| Europäisches Patentamt | 2022
Zirconium dioxide and its complex phase silicon nitride ceramics
| British Library Online Contents | 2002
METHOD OF PRODUCING BIOCOMPATIBLE POROUS ZIRCONIUM DIOXIDE CERAMICS FOR ENDOPROSTHESIS REPLACEMENT
| Europäisches Patentamt | 2021
METHOD FOR LASER PROCESSING OF DUCTILE TOOL FROM ZIRCONIUM DIOXIDE CERAMICS
| Europäisches Patentamt | 2017
METHOD OF MAKING POROUS ARTICLES OF SPHERICAL SHAPE BASED ON ZIRCONIUM DIOXIDE
| Europäisches Patentamt | 2020