METHOD OF PRODUCING HIGHLY PURE FINE-CRYSTAL BARIUM TITANATE
FIELD: technological processes.SUBSTANCE: invention relates to synthesis of fine-grained barium titanate used for making ceramic capacitors. Method comprises treatment of a mixture of titanium dioxide and barium-containing reagent in a medium based on water vapor at high temperature and pressure, wherein the barium-containing reagent used is barium nitrate monohydrate Ba(NO)⋅HO and treatment of reagents is carried out in medium of mixture of water vapor and ammonia; mixture of powders of monohydrate of barium nitride and titanium oxide is taken in molar ratio [Ba(NO)⋅HO]/TiOfrom 1.0 to 1.3; in reaction space, mole ratio of NHOH/HO=1/5; thermal treatment of mixture of reagents with steam containing ammonia is carried out for 1 to 16 hours under isothermal conditions at temperature selected in range from 250 to 400 °C with heating rate in range of 50–100 °C/h and water vapor pressure from 3.98 to 26.1 MPa. Reaction of reagents by steam reacts at molar ratio NHOH/[Ba(NO)⋅HO]=2.0–3.2. Obtained product is washed with aqueous solution of acetic acid with concentration of 5 wt%, with distilled water till pH=7 of washing water and dried in air at temperature of 70 °C to consistency of mass.EFFECT: invention enables to obtain fine-grained titanate with average crystal size of 0,2–2 mcm with content of basic substance higher than 99,98 %.3 cl, 6 dwg, 2 tbl, 4 ex
Изобретение относится к области синтеза мелкокристаллического титаната бария, используемого для изготовления керамических конденсаторов. Способ включает обработку смеси диоксида титана и барийсодержащего реагента в среде на основе пара воды при повышенных температуре и давлении, при этом в качестве барийсодержащего реагента используется моногидрат нитрита бария Ba(NO)⋅HO и обработку реагентов ведут в среде смеси пара воды и аммиака; смесь порошков моногидрата нитрита бария и оксида титана берут в мольном отношении [Ва(NO)⋅НO]/ТiOот 1,0 до 1,3; в реакционном пространстве мольное отношение NHOH/НО=1/5; термообработку смеси реагентов паром, содержащим аммиак, ведут в течение времени от 1 до 16 часов в изотермических условиях при температуре, выбранной в интервале от 250 до 400°С со скоростью нагрева в интервале 50-100°С/ч и давлении пара воды от 3,98 до 26,1 МПа. Обработку паром реакционной смеси реагентов ведут при мольном отношении NHOH/ [Ba(NO)⋅HO]=2,0-3,2. Полученный продукт промывают водным раствором уксусной кислоты концентрацией 5 масс. %, дистиллированной водой до достижения рН=7 промывных вод и высушивают на воздухе при температуре 70°С до постоянства массы. Изобретение позволяет получать мелкокристаллический титанат со средним размером кристаллов от 0,2 до 2 мкм с содержанием основного вещества выше 99,98%. 2 з.п. ф-лы, 6 ил., 2 табл., 4 пр.
METHOD OF PRODUCING HIGHLY PURE FINE-CRYSTAL BARIUM TITANATE
FIELD: technological processes.SUBSTANCE: invention relates to synthesis of fine-grained barium titanate used for making ceramic capacitors. Method comprises treatment of a mixture of titanium dioxide and barium-containing reagent in a medium based on water vapor at high temperature and pressure, wherein the barium-containing reagent used is barium nitrate monohydrate Ba(NO)⋅HO and treatment of reagents is carried out in medium of mixture of water vapor and ammonia; mixture of powders of monohydrate of barium nitride and titanium oxide is taken in molar ratio [Ba(NO)⋅HO]/TiOfrom 1.0 to 1.3; in reaction space, mole ratio of NHOH/HO=1/5; thermal treatment of mixture of reagents with steam containing ammonia is carried out for 1 to 16 hours under isothermal conditions at temperature selected in range from 250 to 400 °C with heating rate in range of 50–100 °C/h and water vapor pressure from 3.98 to 26.1 MPa. Reaction of reagents by steam reacts at molar ratio NHOH/[Ba(NO)⋅HO]=2.0–3.2. Obtained product is washed with aqueous solution of acetic acid with concentration of 5 wt%, with distilled water till pH=7 of washing water and dried in air at temperature of 70 °C to consistency of mass.EFFECT: invention enables to obtain fine-grained titanate with average crystal size of 0,2–2 mcm with content of basic substance higher than 99,98 %.3 cl, 6 dwg, 2 tbl, 4 ex
Изобретение относится к области синтеза мелкокристаллического титаната бария, используемого для изготовления керамических конденсаторов. Способ включает обработку смеси диоксида титана и барийсодержащего реагента в среде на основе пара воды при повышенных температуре и давлении, при этом в качестве барийсодержащего реагента используется моногидрат нитрита бария Ba(NO)⋅HO и обработку реагентов ведут в среде смеси пара воды и аммиака; смесь порошков моногидрата нитрита бария и оксида титана берут в мольном отношении [Ва(NO)⋅НO]/ТiOот 1,0 до 1,3; в реакционном пространстве мольное отношение NHOH/НО=1/5; термообработку смеси реагентов паром, содержащим аммиак, ведут в течение времени от 1 до 16 часов в изотермических условиях при температуре, выбранной в интервале от 250 до 400°С со скоростью нагрева в интервале 50-100°С/ч и давлении пара воды от 3,98 до 26,1 МПа. Обработку паром реакционной смеси реагентов ведут при мольном отношении NHOH/ [Ba(NO)⋅HO]=2,0-3,2. Полученный продукт промывают водным раствором уксусной кислоты концентрацией 5 масс. %, дистиллированной водой до достижения рН=7 промывных вод и высушивают на воздухе при температуре 70°С до постоянства массы. Изобретение позволяет получать мелкокристаллический титанат со средним размером кристаллов от 0,2 до 2 мкм с содержанием основного вещества выше 99,98%. 2 з.п. ф-лы, 6 ил., 2 табл., 4 пр.
METHOD OF PRODUCING HIGHLY PURE FINE-CRYSTAL BARIUM TITANATE
Способ получения особочистого мелкокристаллического титаната бария
DANCHEVSKAYA MARINA NIKOLAEVNA (Autor:in) / IVAKIN YURIJ DMITRIEVICH (Autor:in) / KHOLODKOVA ANASTASIYA ANDREEVNA (Autor:in) / MURAVEVA GALINA PETROVNA (Autor:in) / RYBALCHENKO VIKTOR VIKTOROVICH (Autor:in) / VASIN ALEKSANDR ALEKSANDROVICH (Autor:in)
03.02.2020
Patent
Elektronische Ressource
Russisch
IPC:
B01J
Chemische oder physikalische Verfahren, z.B. Katalyse oder Kolloidchemie
,
CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY
/
C01F
COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
,
Verbindungen der Metalle Beryllium, Magnesium, Aluminium, Calcium, Strontium, Barium, Radium, Thorium oder der Seltenen Erden
/
C01G
Verbindungen der von den Unterklassen C01D oder C01F nicht umfassten Metalle
,
COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
/
C04B
Kalk
,
LIME
/
C30B
SINGLE-CRYSTAL GROWTH
,
Züchten von Einkristallen