BITUMINOUS SHINGLES AND METHOD OF PRODUCING SHINGLES
FIELD: construction.SUBSTANCE: group of inventions is asphalt shingles and method of its production. Bitumen tiles include glass fiber, bitumen mixture impregnating it, basalt granulate applied on the outside and an adhesive. Bitumen mixture has the following composition: distilled bitumen from 30 to 50 %, APAO (amorphous poly-alpha-olefin) from 5 to 15 %, calcium carbonate from 40 to 60 %. When implementing the method of producing shingles, first, in a first mixer, a mixture is made by mixing distilled bitumen and APAO polymer, then the mixture is moved into the second mixer, calcium carbonate is added, mixed until homogenization, then the mixture is moved into an impregnation bath in which the obtained glass fibers are impregnated with the obtained mixture, then, roller is used to apply basalt granulate and sand, perform cooling phase, then perform mechanical pressing, cool down, apply adhesive, then cut and package.EFFECT: group of inventions provides optimum parameters of cold flexibility, heat resistance, durability.4 cl, 1 dwg, 10 tbl
Группа изобретений представляет собой битумную черепицу и способ ее производства. Битумная черепица включает стекловолокно, пропитывающую его битумную смесь, нанесённые снаружи базальтовый гранулят, адгезив. Битумная смесь имеет следующий состав: дистиллированный битум от 30 до 50%, АПАО (аморфный поли-альфа-олефин) от 5 до 15%, карбонат кальция от 40 до 60%. При осуществлении способа производства битумной черепицы вначале в первом миксере изготавливают смесь путём перемешивания дистиллированного битума и полимера АПАО, затем перемещают смесь во второй миксер, добавляют карбонат кальция, перемешивают до гомогенизации, далее перемещают смесь в ванну пропитки, в которой производится пропитывание стекловолокна полученной смесью, далее с помощью ролика наносят базальтовый гранулят и песок, проводят фазу охлаждения, далее проводят механическое прессование, охлаждают, наносят адгезив, после чего производят резку и упаковку. Группа изобретений обеспечивает оптимальные показатели холодной гибкости, термостойкости, долговечности. 2 н. и 2 з.п. ф-лы, 1 ил., 10 табл.
BITUMINOUS SHINGLES AND METHOD OF PRODUCING SHINGLES
FIELD: construction.SUBSTANCE: group of inventions is asphalt shingles and method of its production. Bitumen tiles include glass fiber, bitumen mixture impregnating it, basalt granulate applied on the outside and an adhesive. Bitumen mixture has the following composition: distilled bitumen from 30 to 50 %, APAO (amorphous poly-alpha-olefin) from 5 to 15 %, calcium carbonate from 40 to 60 %. When implementing the method of producing shingles, first, in a first mixer, a mixture is made by mixing distilled bitumen and APAO polymer, then the mixture is moved into the second mixer, calcium carbonate is added, mixed until homogenization, then the mixture is moved into an impregnation bath in which the obtained glass fibers are impregnated with the obtained mixture, then, roller is used to apply basalt granulate and sand, perform cooling phase, then perform mechanical pressing, cool down, apply adhesive, then cut and package.EFFECT: group of inventions provides optimum parameters of cold flexibility, heat resistance, durability.4 cl, 1 dwg, 10 tbl
Группа изобретений представляет собой битумную черепицу и способ ее производства. Битумная черепица включает стекловолокно, пропитывающую его битумную смесь, нанесённые снаружи базальтовый гранулят, адгезив. Битумная смесь имеет следующий состав: дистиллированный битум от 30 до 50%, АПАО (аморфный поли-альфа-олефин) от 5 до 15%, карбонат кальция от 40 до 60%. При осуществлении способа производства битумной черепицы вначале в первом миксере изготавливают смесь путём перемешивания дистиллированного битума и полимера АПАО, затем перемещают смесь во второй миксер, добавляют карбонат кальция, перемешивают до гомогенизации, далее перемещают смесь в ванну пропитки, в которой производится пропитывание стекловолокна полученной смесью, далее с помощью ролика наносят базальтовый гранулят и песок, проводят фазу охлаждения, далее проводят механическое прессование, охлаждают, наносят адгезив, после чего производят резку и упаковку. Группа изобретений обеспечивает оптимальные показатели холодной гибкости, термостойкости, долговечности. 2 н. и 2 з.п. ф-лы, 1 ил., 10 табл.
BITUMINOUS SHINGLES AND METHOD OF PRODUCING SHINGLES
Битумная черепица и способ производства битумной черепицы
MICHELE DRIGO (Autor:in)
19.11.2020
Patent
Elektronische Ressource
Russisch
IPC:
E04D
ROOF COVERINGS
,
Dacheindeckungen
| Europäisches Patentamt | 2017