METHOD OF OBTAINING COMPLEX LITHIUM TANTALATE OF STRONTIUM AND LANTHANUM
FIELD: chemical industry.SUBSTANCE: invention relates to the field of chemical industry, namely to a method for producing complex lithium tantalate of lanthanum and strontium, used as a solid electrolyte - one of the main components of a lithium-ion battery. The method of obtaining complex lithium tantalum lanthanum and strontium is characterized by the fact that the gel-like hydrated tantalum pentoxide, previously obtained by treating anhydrous tantalum pentoxide with hydrofluoric acid and ammonium hydroxide, is dissolved in 11% nitric acid, taken in an amount of 5 mol / 1 mol Ta+ 5with the addition of tartaric acid powder, taken in an amount of 5 mol / 1 mol of Ta+ 5. Add solutions of lanthanum nitrate, lithium nitrate and strontium nitrate, obtained by dissolving a stoichiometric amount of lanthanum oxide, lithium carbonate and strontium carbonate in 11% nitric acid taken in excess (0.05-0.15 mol). Maintain at a temperature of 140-150°C and vigorous stirring for 4 hours, and then subjected to annealing in three stages: Stage I - at a temperature of 380-400°C for 4 hours; Stage II - at a temperature of 650-680°C for 10 hours; Stage III - at a temperature of 780-800°C for 24 hours with re-mixing and pressing after the second stage.EFFECT: obtaining a single-phase final product without any impurity inclusions and obtaining high-density ceramics by reducing the particle size of the resulting material.1 cl
Изобретение относится к области химической промышленности, а именно к способу получения сложного литиевого танталата лантана и стронция, используемого в качестве твердотельного электролита - одного из основных компонентов литий-ионной батареи. Способ получения сложного литиевого танталата лантана и стронция характеризуется тем, что гелеобразный гидратированный пентаоксид тантала, предварительно полученный путем обработки безводного пентаоксида тантала плавиковой кислотой и гидроксидом аммония, растворяют в 11%-ной азотной кислоте, взятой в количестве 5 моль/1 моль Та+5с добавлением порошка винной кислоты, взятой в количестве 5 моль/1 моль Та+5. Добавляют растворы нитрата лантана, нитрата лития и нитрата стронция, полученные растворением стехиометрического количества оксида лантана, карбоната лития и карбоната стронция в 11%-ной азотной кислоте, взятой с избытком (0,05-0,15 моль). Выдерживают при температуре 140-150°С и интенсивном перемешивании в течение 4 ч, а затем подвергают отжигу в три стадии: I стадия - при температуре 380-400°C в течение 4 ч; II стадия - при температуре 650-680°C в течение 10 ч; III стадия - при температуре 780-800°C в течение 24 ч с перешихтовкой и прессованием после второй стадии. Технический результат заключается в получении однофазного конечного продукта без каких-либо примесных включений и получение высокоплотной керамики за счет уменьшения размерности частиц получаемого материала.
METHOD OF OBTAINING COMPLEX LITHIUM TANTALATE OF STRONTIUM AND LANTHANUM
FIELD: chemical industry.SUBSTANCE: invention relates to the field of chemical industry, namely to a method for producing complex lithium tantalate of lanthanum and strontium, used as a solid electrolyte - one of the main components of a lithium-ion battery. The method of obtaining complex lithium tantalum lanthanum and strontium is characterized by the fact that the gel-like hydrated tantalum pentoxide, previously obtained by treating anhydrous tantalum pentoxide with hydrofluoric acid and ammonium hydroxide, is dissolved in 11% nitric acid, taken in an amount of 5 mol / 1 mol Ta+ 5with the addition of tartaric acid powder, taken in an amount of 5 mol / 1 mol of Ta+ 5. Add solutions of lanthanum nitrate, lithium nitrate and strontium nitrate, obtained by dissolving a stoichiometric amount of lanthanum oxide, lithium carbonate and strontium carbonate in 11% nitric acid taken in excess (0.05-0.15 mol). Maintain at a temperature of 140-150°C and vigorous stirring for 4 hours, and then subjected to annealing in three stages: Stage I - at a temperature of 380-400°C for 4 hours; Stage II - at a temperature of 650-680°C for 10 hours; Stage III - at a temperature of 780-800°C for 24 hours with re-mixing and pressing after the second stage.EFFECT: obtaining a single-phase final product without any impurity inclusions and obtaining high-density ceramics by reducing the particle size of the resulting material.1 cl
Изобретение относится к области химической промышленности, а именно к способу получения сложного литиевого танталата лантана и стронция, используемого в качестве твердотельного электролита - одного из основных компонентов литий-ионной батареи. Способ получения сложного литиевого танталата лантана и стронция характеризуется тем, что гелеобразный гидратированный пентаоксид тантала, предварительно полученный путем обработки безводного пентаоксида тантала плавиковой кислотой и гидроксидом аммония, растворяют в 11%-ной азотной кислоте, взятой в количестве 5 моль/1 моль Та+5с добавлением порошка винной кислоты, взятой в количестве 5 моль/1 моль Та+5. Добавляют растворы нитрата лантана, нитрата лития и нитрата стронция, полученные растворением стехиометрического количества оксида лантана, карбоната лития и карбоната стронция в 11%-ной азотной кислоте, взятой с избытком (0,05-0,15 моль). Выдерживают при температуре 140-150°С и интенсивном перемешивании в течение 4 ч, а затем подвергают отжигу в три стадии: I стадия - при температуре 380-400°C в течение 4 ч; II стадия - при температуре 650-680°C в течение 10 ч; III стадия - при температуре 780-800°C в течение 24 ч с перешихтовкой и прессованием после второй стадии. Технический результат заключается в получении однофазного конечного продукта без каких-либо примесных включений и получение высокоплотной керамики за счет уменьшения размерности частиц получаемого материала.
METHOD OF OBTAINING COMPLEX LITHIUM TANTALATE OF STRONTIUM AND LANTHANUM
Способ получения сложного литиевого танталата стронция и лантана
MAKSIMOVA LIDIYA GRIGOREVNA (Autor:in) / DENISOVA TATYANA ALEKSANDROVNA (Autor:in) / BAKLANOVA YANA VIKTOROVNA (Autor:in)
16.03.2021
Patent
Elektronische Ressource
Russisch
Method for producing dense lithium lanthanum tantalate lithium-ion conducting ceramics
| Europäisches Patentamt | 2016
Method for producing dense lithium lanthanum tantalate lithium-ion conducting ceramics
| Europäisches Patentamt | 2018
Photocatalytic Performance of Barium-Doped Strontium Tantalate
| British Library Online Contents | 2007
Hydrothermal synthesis of strontium bismuth tantalate powder
| British Library Online Contents | 2003
Photocatalytic Performance of Barium-Doped Strontium Tantalate
| British Library Online Contents | 2007